Finishing agent of polyester silk-like fabric and preparation and post-treatment methods of fabric

A technology of fabric finishing agent and imitation silk, which is applied in fiber treatment, textile and papermaking, fiber type, etc. It can solve the problems of poor durability and high processing cost, and achieve the effects of good hygroscopicity, convenient product processing, and excellent wrinkle resistance

Active Publication Date: 2011-05-04
ZHEJIANG TAIHUA NEW MATERIAL
View PDF5 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a method that can not only improve the hygroscopicity and air permeability of polyester silk-like fabrics but also improve its functional durability in view of the problems of high processing cost and poor durability in the finishing agent for polyester spun silk fabrics in the prior art. sexual finishing agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Finishing agent of polyester silk-like fabric and preparation and post-treatment methods of fabric
  • Finishing agent of polyester silk-like fabric and preparation and post-treatment methods of fabric
  • Finishing agent of polyester silk-like fabric and preparation and post-treatment methods of fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The base fabric is polyester. The warp and weft raw materials of the base fabric are 1 / 75D / 72f polyester filaments, the warp and weft density is 580×380 threads / 10cm; the square meter weight is 83g / m2 .

[0039] Post-processing proceeds as follows:

[0040] (1) Desizing: use an open-width desizing machine. The temperature of the desizing tank is 95°C; the running speed of the fabric is 40m / min.

[0041] The formulation of the treatment liquid, by weight, includes 2.5% caustic soda; 0.45% stabilizer; 0.225% penetrant; 0.225% scouring agent, and the rest is water.

[0042] (2) Base weight reduction treatment: use high temperature and high pressure overflow reduction machine. The bath ratio is 1:18; the treatment temperature is 120°C; the treatment time is 40 minutes, and then washed with water and dried.

[0043] The formulation of the treatment liquid, by weight: 2.5% caustic soda; 0.2% penetrating agent; 0.2% scouring agent.

[0044] The weight reduction rate of th...

Embodiment 2

[0050] (1) desizing: with embodiment 1

[0051] (2) Base weight reduction treatment: use high temperature and high pressure overflow reduction machine. The bath ratio is 1:15; the treatment temperature is 115°C; the treatment time is 43 minutes, and then washed with water and dried.

[0052] The formulation of the treatment liquid, by weight: 2% caustic soda; 0.25% penetrating agent; 0.25% scouring agent.

[0053] The weight reduction rate of the fabric after finishing in step (2) is 10%.

[0054] (3) Padding finishing solution: padding at room temperature. The fabric running speed is 20±1m / min; the drying temperature is 120°C; the baking temperature is 158°C.

[0055] The finishing agent is prepared according to the following formula (parts by weight), including 5 parts of silk peptide; 3 parts of polyethylene glycol; 3 parts of citric acid, 1.5 parts of sodium dihydrogen phosphate, 2 parts of acetic acid, 2 parts of denatured silicone, and 1 part of chitosan share.

[0...

Embodiment 3

[0059] (1) desizing: with embodiment 1

[0060] (2) Base weight reduction treatment: use high temperature and high pressure overflow reduction machine. The bath ratio is 1:20; the treatment temperature is 125°C; the treatment time is 37 minutes, and then washed with water and dried.

[0061] The formulation of the treatment liquid, by weight: 3% caustic soda; 0.15% penetrating agent; 0.15% scouring agent.

[0062] The weight reduction rate of the fabric after finishing in step (2) is 12%.

[0063] The finishing agent is prepared according to the following formula (parts by weight), including 7 parts of silk peptide; 5 parts of polyethylene glycol; 5 parts of maleic anhydride, 2.5 parts of disodium hydrogen phosphate, 1 part of acetic acid, 1 part of softening agent, and 0.5 parts of chitosan share.

[0064] The preparation process of the finishing solution is as follows: by weight, dissolve 1 part of acetic acid in 75 parts of water, then add 0.5 parts of chitosan, dissolve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a finishing agent for preparing comfortable and cool polyester silk-like fabric and a post-treatment method of the comfortable and cool polyester silk-like fabric, aiming at overcoming the defects of the finishing agent of the polyester silk-like fabric, such as high processing cost and poor durability in the prior art. The finishing agent provided by the invention is composed of the following components in parts by weight: 5-7 parts of silk peptide, 3-5 parts of polyethylene glycol, 3-5 parts of a cross-linking agent, 1.5-2.5 parts of a cross-linking catalyst, 1-2 parts of acetic acid, 1-2 parts of a softening agent, 0.5-1 part of chitosan and the balance of water. The post-treatment method of the polyester silk-like fabric comprises the following steps: desizing, alkali weight reduction treatment of the base fabric, and pad finishing. By utilizing the finishing agent and the post-treatment method in the invention, the defect, such as hard feel, of the polyester fabric is overcome so that the polyester fabric has the advantages of excellent wrinkle resistance and soft feel, and is air-permeable, cool and comfortable to wear.

Description

technical field [0001] The invention relates to a finishing agent for a comfortable and cool polyester imitation silk fabric, a preparation method thereof and a post-treatment method for a comfortable and cool polyester imitation silk fabric. Background technique [0002] Polyester fabrics have incomparable excellent properties of natural fibers such as high strength, wear resistance, good wrinkle resistance, no insects, quick drying, and easy care. However, it has low moisture regain, poor moisture absorption and vapor permeability, stuffy clothes, easy to generate static electricity, easy to absorb dirt and breed bacteria. Therefore, the wearing comfort of polyester fabric is poor. [0003] The shortcomings of polyester fabrics can be improved by chemical fiber modification technology, and their wearing comfort can be improved. Such as adding hydrophilic monomers or polymers in the process of synthesis and spinning, but this technical operation is difficult and costly. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/15D06M15/53D06M15/03D06M15/643D06M13/192D06M13/203D06M101/32
Inventor 汪蔚沈卫锋徐丽亚厉恩祥许斌
Owner ZHEJIANG TAIHUA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com