Hydrocracking catalyst carrier and preparation method thereof

A catalyst carrier, hydrocracking technology, applied in the direction of catalyst carrier, physical/chemical process catalyst, molecular sieve catalyst, etc. The effect of moderate grain size, ensuring skeleton continuity and high crystal retention

Active Publication Date: 2011-05-11
CHINA PETROLEUM & CHEM CORP +1
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The small-grain Y-type molecular sieve prepared by the raw material has a low degree of crystallization retention, and the modification method adopted has high preparation costs and is difficult to realize industrially.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrocracking catalyst carrier and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The preparation method of the small grain NaY type molecular sieve in the carrier of the present invention specifically comprises the following steps:

[0033] A. Preparation of directing agent at low temperature.

[0034] According to Na 2 O:Al 2 o 3 : SiO 2 :H 2 O=10~20: 1: 10~20: 300~400 feed molar ratio, at a temperature above 0°C and less than 15°C, preferably at a temperature of 0°C to 10°C, the water glass is slowly stirred under the condition of stirring Add it into the high-alkaline sodium metaaluminate solution and mix evenly, then stir at the above temperature at a constant temperature and speed for 0.5-2 hours; then seal the mixed solution in a synthesis kettle, and age it at a static temperature for 10-14 hours to obtain a directing agent The directing agent is preferably added with 20% to 40% of the weight of the directing agent before use.

[0035] B. Preparation of gel at low temperature.

[0036] Mix water glass, aluminum sulfate solution, low-al...

Embodiment 1

[0052] This example is to prepare NaY type molecular sieve with small crystal grain as raw material.

[0053] The raw materials used are as follows:

[0054] High alkali sodium metaaluminate: Na 2 O content 291g / L, Al 2 o 3 Content 42g / L; low alkali sodium metaaluminate: Na 2 O content 117g / L, Al 2 o 3 Content 77g / L; water glass: SiO 2 Content 250g / L, modulus 3.2; aluminum sulfate: Al 2 o 3 Content 90g / L.

[0055] Preparation of LY-1:

[0056] A. Preparation of directing agent: Slowly add 1200ml of water glass into 800ml of high alkali sodium metaaluminate under stirring condition at 10°C. After adding water glass, stir at constant temperature for 40 minutes. Stirring was stopped, and the mixed solution was sealed in a container, and aged at a temperature of 5°C for 12 hours at a constant temperature. After the constant temperature is finished, add 667ml of clean water to the mixed solution as a guiding agent.

[0057]B. Preparation of the gel: Add 59.4ml of alumin...

Embodiment 2

[0064] Firstly, ammonium exchange is carried out on the raw material small grain NaY molecular sieve LY-1. The preparation concentration is 10 liters of 0.5mol / l ammonium nitrate aqueous solution. Weigh 2000 grams of small-grain NaY-type molecular sieves, dissolve them in 10 liters of prepared ammonium nitrate aqueous solution, stir at a constant temperature of 90 ° C for 1 hour at a stirring speed of 300 ℃, then filter the molecular sieves, and leave a small sample for analysis of Na 2 O content; repeat the above operation until Na in the molecular sieve 2 The O content reaches 2.5-5wt%, and the sample number obtained after drying is LNY-1.

[0065] Measure 1 liter of clean water and dissolve 1000 g of LNY-1 in the clean water, heat up and stir rapidly, the temperature is 95°C, and the stirring speed is 300 rpm. In 2 hours, add ammonium hexafluorosilicate aqueous solution to the molecular sieve slurry at a uniform speed, add 50 grams of ammonium hexafluorosilicate in total,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a hydrocracking catalyst carrier and a preparation method thereof. The carrier consists of a small crystal particle Y-shaped molecular sieve and alumina, wherein the small crystal particle Y-shaped molecular sieve has high crystallinity, high ratio of silicate to aluminium, continuous and stable framework structure and smooth pores. A hydrocracking catalyst prepared from the carrier has the characteristics of high catalytic activity, high heavy naphtha selectivity, high potential aromatic hydrocarbon content, low bureau of mines correlation index (BMCI) value of hydrocracking tail oil and the like.

Description

technical field [0001] The invention relates to a hydrocracking catalyst carrier and a preparation method thereof, in particular to a hydrocracking catalyst carrier capable of producing high-quality heavy naphtha and tail oil with a low BMCI value and a preparation method thereof. Background technique [0002] The carrier is an important part of the catalyst. It not only provides a place for the metal active components to disperse, but also participates in the reaction itself, and completes the entire catalytic reaction together with other active components. Existing hydrogenation catalyst supports generally contain molecular sieves, alumina, and other refractory oxides, and are generally used in processes such as hydrocracking of heavy oil, hydrogenation of distillate oil to remove impurities, and hydrogenation of inferior diesel oil. [0003] With the rapid development of my country's economy, the market demand for chemical products has increased sharply. Among them, the d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J32/00B01J29/08C01B39/24C10G47/20
Inventor 刘昶王凤来杜艳泽关明华
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com