Method for preparing special water glass for petrochemical catalysts by wet method

A petrochemical catalyst and water glass technology, applied in the direction of alkali metal silicate, silicate, etc., can solve the problems of high production energy consumption, inability to filter, and heavy pollution, and achieve the goals of reducing emissions, reducing sites, and saving equipment investment Effect

Inactive Publication Date: 2015-08-19
张振慧 +2
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention provides a method for preparing water glass special for petrochemical catalysts by wet method, which is used to solve the above-mentioned defects such as high energy consumption, heavy pollution and inability to filter by dry method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1, produce the special water glass 3.3M of petrochemical catalyst, Be ' 32 °.

[0013] 1. Use refined quartz sand and sodium hydroxide, Fe<0.02% as raw materials, produce 2.8M, Be'45° sodium silicate solution by wet method according to known technology, and filter it through a plate and frame filter press at 80-100°C for standby .

[0014] 2. Use 2.8M sodium silicate solution to prepare hydrated silicic acid A and prepare silica sol. Take 1.5 tons of hydrochloric acid in the silica sol reaction kettle and dilute to Be'8°. Under stirring, slowly add Be'10° silicic acid Sodium solution, control the pH below 3.5 to prevent the generation of jelly. B. Add an appropriate amount of water into the hydrated silicic acid precipitation kettle and heat it to 80-100°C. Add the silica sol solution and sodium silicate solution under stirring. Control PH < 7 and white hydrated silicic acid will be precipitated at this time. After the slurry is acidified and aged, polyethy...

Embodiment 2

[0017] Production of 3.3M, Be'38° sodium silicate solution

[0018] 1. Use refined quartz sand and sodium hydroxide, Fe<0.02% as raw materials, produce 2.6M by wet method according to known technology, Be'45° sodium silicate solution is filtered through filter press at 80-100°C to become clear and transparent Sodium silicate solution for use.

[0019] 2. Use 2.6M, Be'45° sodium silicate solution to prepare hydrated silicic acid A and silica sol, take 1.5 tons of hydrochloric acid in the silica sol reaction kettle and dilute to Be'18°, and slowly add Be'10 under stirring ° sodium silicate solution, control the pH below 3.5 to prevent the generation of jelly. B. Add an appropriate amount of water into the hydrated silicic acid precipitation kettle and heat it to 80-100°C. Add the silica sol solution and sodium silicate solution under stirring, and control the pH<7. At this time, white hydrated silicic acid will precipitate and the slurry will After acidification and aging, pol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a wet production method of high-modulus sodium silicate, particularly a production method of special water glass for a petrochemical catalyst, and solves the problems that high-modulus sodium silicate cannot be produced by a wet method and a high-modulus sodium silicate solution is difficult to filter. Compared with dry production methods, the wet production method saves 70 kg of standard coal and reduces 0.7-0.8 ton of emitted carbon dioxide during the production of each ton of high-modulus sodium silicate, and has obvious economic and social benefits.

Description

1. Technical field [0001] The invention relates to a method for wet manufacturing special water glass for petrochemical catalysts, which can also be applied to the preparation of ordinary high modulus sodium silicate, and belongs to the improvement of the production method of inorganic silicon compound sodium silicate. 2. Background technology [0002] Sodium silicate is also known as sodium silicate, and its production methods include dry method and wet method. The dry method is to use soda ash and quartz sand, or sodium sulfate, coal powder and quartz sand to react at a high temperature of 1350 ° C to 1450 ° C to produce sodium silicate The vitreous body is then hydrolyzed into solution under saturated vapor pressure. The high modulus sodium silicate solution has a high viscosity and is difficult to filter. It can only let the impurities settle naturally. It takes a long time for clarification to obtain qualified products. The dry process consumes a lot of energy and cause...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B33/32
Inventor 张振慧张兴海张新洋
Owner 张振慧
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com