Method for determining melting behavior and melting point of slag-like material

A technology of melting point measurement and behavior, which is applied in the field of metallurgical slag material detection, can solve the problems of low accuracy, difficult control of the stability of the measurement conditions of the molten steel slag method, and high measurement costs, so as to achieve accurate test results and dynamic testing process intuitive effect

Active Publication Date: 2013-06-26
SHOUGANG CORPORATION
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] The invention uses a high-temperature laser confocal microscope to observe the melting behavior of slag in situ, continuously, and dynamically during the entire heating process, and overcomes the shortcomings of the traditional melting point test method, which only uses the slag column deformation method, that is, the hemispherical point temperature test method is not high in accuracy. And the limitations of the stability of the measurement conditions of the molten steel slag method are difficult to control and the measurement cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for determining melting behavior and melting point of slag-like material
  • Method for determining melting behavior and melting point of slag-like material
  • Method for determining melting behavior and melting point of slag-like material

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0050] Example 1 Observation of melting behavior of blast furnace slag and accurate determination of melting point

[0051] The present invention is applied in the observation of melting behavior of blast furnace slag and the determination of melting point. The specific steps are as follows:

[0052] 1. Slag sample preparation. After burning the blast furnace slag to glassy molten slag and water quenching, it is ground into 100 mesh slag powder.

[0053] 2. Slag sample forming. With the help of dextrin and anhydrous filter paper, the powder sample is pressed and fixed on the platinum sheet to form the slag sample.

[0054] 3. High temperature laser sample loading. Place the platinum sheet with the molded slag sample on the Al 2 O 3 After the bottom of the crucible, put it into the high temperature metallographic heating furnace of the high temperature laser confocal microscope.

[0055] 4. Experimental program settings. Set up the temperature increase experiment program of blast fur...

example 2

[0062] Example 2 Observation of melting behavior of mold flux and accurate determination of melting point

[0063] The present invention is applied in observation of melting behavior of mold flux and determination of melting point, and the specific steps are as follows:

[0064] 1. Slag sample preparation. After burning the mold powder to glassy molten slag and water quenching, it is ground into 150 mesh slag powder.

[0065] 2. Slag sample forming. With the help of dextrin and anhydrous filter paper, the powder sample is pressed and fixed on the platinum sheet to form the slag sample.

[0066] 3. High temperature laser sample loading. Place the platinum sheet with the shaped slag sample on the Al 2 O 3 After the bottom of the crucible, put it into the high temperature metallographic heating furnace of the high temperature laser confocal microscope.

[0067] 4. Experimental program settings. Set up the temperature increase experiment program of the mold powder (see image 3 ), after...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for determining a melting behavior and a melting point of a slag-like material, belonging to the technical field of detection of metallurgical slag-like material. The process comprises slag sample preparation, slag sample formation, high-temperature laser sample filling, experimental parameter setting, melting process observation and data and image processing. The method provided by the invention has the advantages that the defect of low accuracy of the slag column deformation method, i.e. the hemisphere point temperature testing method, in the traditional melting point testing can be overcome, and the limitations of difficulties in control of the stability of testing conditions and high testing costs in the method of slag melting in liquid steel can be eliminated. The initial melting temperature of the slag sample from the solid phase to the liquid phase and the melting temperature of the slag sample to the full liquid phase can be captured promptly so as to accurately determine the melting point of the slag sample; and the liquid phase nucleation, growth and other melting changes and behaviors of the slag sample in the heating process can also be analyzed, the direct theoretical basis and technical support can be provided for the curing of liquid slag and the control of metallurgical reaction in the steel-making and iron-making process, and different characteristics of different slag samples in the melting process can be used as an important means for evaluation of high-temperature properties of different slag samples.

Description

Technical field [0001] The invention belongs to the technical field of detection of metallurgical slag materials, and in particular provides a method for melting behavior and melting point determination of slag materials; it is suitable for research on blast furnace slag, mold flux and other slag materials. Background technique [0002] The smelting process requires the slag to have good fluidity. High-speed continuous casting requires the mold slag to have a low melting temperature to ensure sufficient supply of liquid slag, and the melting temperature of the slag is important for selecting the power supply parameters of electric furnace smelting to ensure the appropriate slag temperature and comparison. Low power consumption also makes a lot of sense. Therefore, the melting temperature of the slag determines the temperature system in metallurgical engineering. If the melting temperature of the slag is high and the viscosity of the slag is too high, it will be detrimental to the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N25/04
Inventor 班丽丽史学星温娟鞠新华刘卫平
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com