Z2CND18-12N control nitrogen stainless steel forging technology

A stainless steel and process technology, which is applied in the forging process of nitrogen-controlled stainless steel, can solve problems such as failure to meet requirements, difficulty in improvement, and unstable actual indicators, and achieve reliable and safe performance and long service life.

Active Publication Date: 2013-12-25
无锡市法兰锻造有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The actual indicators of the existing Z2CND18-12N domestic forgings are very unstable, and most of them fail to meet the requirements, and it is difficult to improve even through re-heat treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] An embodiment of the present invention, Z2CND18-12N nitrogen-controlled stainless steel forging process, includes raw material control, heating forging and heat treatment steps, wherein heating forging includes forging blank heating process and forging deformation process.

[0008] The technique of the present invention mainly takes measures in three aspects, so that the strength of its product reaches more than 460MPa at 350°C:

[0009] 1. Quality control of raw materials. The quality of raw materials is the basic factor that determines the performance of forgings, including reasonable chemical composition, the lowest possible impurity content, and smelting methods.

[0010] Control the chemical composition of the raw material Z2CND18-12N nitrogen-controlling stainless steel material, the standard value of c content of the raw material is ≤0.035%, in order to improve the strength, increase the lower limit content, control it at 0.02%-0.35%; the standard value of Si con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a Z2CND18-12N control nitrogen stainless steel forging technology relates to the processing method of stainless steel material. The invention uses raw materials controlling chemical compositions and selects lower solid solution treatment temperature through three-section temperature rise method and heat treatment. The temperature rise speed in the heat treatment is not greater than 150 degrees centigrade and the heat holding time is calculated according to 1.5min / mm and not less than 2.5h. The Z2CND18-12N control nitrogen stainless steel forging material processed by the method of the invention has strength above 460Mpa stably at high temperature of 350 DEG C to meet the component manufacturing requirements of nuclear power industry. The processing method is applied for manufacturing important components such as nuclear power pipe flange.

Description

technical field [0001] The invention relates to a forging process of stainless steel, in particular to a forging process of a nitrogen-controlled stainless steel marked Z2CND18-12N. Background technique [0002] Z2CND18-12N is a nitrogen-controlled austenitic stainless steel material. It is graded according to the NF standard steel grade and is widely used in the nuclear power industry. For example, in nuclear power pipelines, most flanges are made of this material. In general end use, a certain forging process is required, and the technical requirement after forging is that the tensile strength at a high temperature of 350°C should reach more than 445MPa. Due to the backwardness of my country's basic material science, it is difficult for domestically produced materials to meet the requirements. For example, for the same grade of steel, imported materials can meet the performance requirements, but materials produced by domestic steel mills cannot meet the requirements. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21J5/00C22C38/58
Inventor 邹上元
Owner 无锡市法兰锻造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com