Offset ink for improving polyester film binding fastness

A technology of combination fastness and offset printing ink, which is applied in the direction of ink, household utensils, applications, etc., can solve the problem of low combination fastness, achieve the effect of easy ink mixing operation, unique synthesis process, and improve the combination fastness

Active Publication Date: 2014-01-01
CHINA BANKNOTE INK +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a kind of offset printing ink that improves the binding fastness of polyester film, overcome the technical deficiency that existing offset printing ink is not high in binding fastness on polyester film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Offset ink for improving polyester film binding fastness
  • Offset ink for improving polyester film binding fastness
  • Offset ink for improving polyester film binding fastness

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Polyamide-modified alkyd resin, prepared by the following method:

[0024] Alcohol-hydrocarbon co-soluble polyamide versamid940 is prepared by reacting with alkyd resin at 190°C for 60 minutes. Its weight percentage is: alcohol-hydrocarbon co-soluble polyamide 20%, alkyd resin 80%;

[0025] Offset printing ink formula: (weight percent)

[0026]

[0027] The various components are mixed, stirred, rolled and dispersed to obtain the product.

[0028] The ink is proofed on neutral paper with IGT, and after drying, use 3M company scotch600 ink adhesion standard test tape to test the binding fastness. The results are as follows: no falling off.

Embodiment 2

[0030] Polyamide-modified alkyd resin, prepared by the following method:

[0031] Alcohol-hydrocarbon co-soluble polyamide P1074 is prepared by reacting with alkyd resin at 200°C for 50 minutes. Its weight percentage is: alcohol-hydrocarbon co-soluble polyamide 10%, alkyd resin 90%;

[0032] Offset printing ink formula: (weight percent)

[0033]

[0034] The various components are mixed, stirred, rolled and dispersed to obtain the product.

[0035] The ink is proofed on neutral paper with IGT, and after drying, use 3M company scotch600 ink adhesion standard test tape to test the binding fastness. The results are as follows: no falling off.

Embodiment 3

[0037] Polyamide-modified alkyd resin, prepared by the following method:

[0038] Alcohol-hydrocarbon co-soluble polyamide versamid950 is prepared by reacting with alkyd resin at 210°C for 30 minutes. The percentage by weight is: 5% of alcohol-hydrocarbon co-soluble polyamide and 95% of alkyd resin.

[0039] Offset printing ink formula: (weight percent)

[0040]

[0041] The various components are mixed, stirred, rolled and dispersed to obtain the product.

[0042] The ink is proofed on neutral paper with IGT, and after drying, use 3M company scotch600 ink adhesion standard test tape to test the binding fastness. The results are as follows: no falling off.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an offset ink for improving polyester film binding fastness, which comprises the following components by weight: 5-25% of polyamide-modified alkyd resin, 40-70% of rosin modified phenolic resin, 5-25% of organic pigments, and 1-10% of additives. The offset ink of the invention has a simple preparation flow, and has good binding fastness with paper substrates.

Description

technical field [0001] The invention relates to an offset printing ink, in particular to an offset printing ink printed on a polyester film. Background technique [0002] In the printing industry, offset printing inks are widely used. The bonding fastness of offset printing inks is good on ordinary paper substrates, but on some special film substrates, especially polyester films with low surface energy, the bonding fastness of offset printing inks is not good. Ideal, especially when printing on some paper and film composite substrates (such as paper containing polyester anti-counterfeiting threads or anti-counterfeiting films), offset printing inks are required to meet both the bonding fastness on paper and the film on the film. Bond fastness. Therefore, on the basis of general offset printing inks, it is of great significance to develop inks with high binding fastness to polyester films. Contents of the invention [0003] The purpose of the present invention is to provi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/10C09D11/103C09D11/105
Inventor 李青齐永路顾悦任志勇沈斌周建岗孟庆飞
Owner CHINA BANKNOTE INK