Non-aromatic corrosion prevention technology for metal structure

A technology for anti-corrosion coatings and coatings, which is applied in the direction of anti-corrosion coatings and coatings, and can solve problems such as poor stability of the treatment process

Inactive Publication Date: 2013-02-27
QINGDAO WINTEC SYSTEM CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the presence of strong oxidants, the stability of the treatment process is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Prepare the following components (parts by mass):

[0028] a N-[N'-(2'-aminoethyl)-2-aminoethyl]-3-aminopropyl-triethoxysilane 11;

[0029] b propanol 60;

[0030] c SiO 2 Particle 6;

[0031] d Hydroxide 6 of Cheng;

[0032] e deionized water 26;

[0033] f Triethylamine 3;

[0034] g carbon fiber 8;

[0035] h polyimide 3;

[0036] (2) Mix the above components and perform aging treatment, then spray, brush or dip on the surface of the substrate, and form a coating on the surface of the substrate after deposition to achieve surface anti-corrosion treatment.

Embodiment 2

[0038] (1) Prepare the following components (parts by mass):

[0039] a N-[N'-(2'-aminoethyl)-2-aminoethyl]-3-aminopropyl-triethoxysilane 20;

[0040] b propanol 80;

[0041] c SiO 2 grain 10;

[0042] d Hydroxide 10 of Cheng;

[0043] e deionized water 50;

[0044] f triethylamine 5;

[0045] g carbon fiber 10;

[0046] h polyimide 5;

[0047] (2) Mix the above components and perform aging treatment, then spray, brush or dip on the surface of the substrate, and form a coating on the surface of the substrate after deposition to achieve surface anti-corrosion treatment.

Embodiment 3

[0049] (1) Prepare the following components (parts by mass):

[0050] a N-[N'-(2'-aminoethyl)-2-aminoethyl]-3-aminopropyl-triethoxysilane 15;

[0051] b propanol 70;

[0052] c SiO 2 particle 8;

[0053] d Hydroxide 8 of Cheng;

[0054] e deionized water 38;

[0055] f triethylamine 4;

[0056] g carbon fiber 9;

[0057] h polyimide 4;

[0058] (2) Mix the above components and perform aging treatment, then spray, brush or dip on the surface of the substrate, and form a coating on the surface of the substrate after deposition to achieve surface anti-corrosion treatment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a non-aromatic corrosion prevention technology for a metal structure, and discloses a coating method of anti-corrosive paint, which comprises the steps of: mixing the components such as siloxane, solvent, silica particles, rare earth compound, deionized water, catalyst, carbon fiber and polyimide, and then curing; filtering the cured mixture; and spraying, brushing or impregnating the filtered mixture on the surface of base material,wherein a coating is formed on the surface of the base material after deposition, thus realizing surface anti-corrosion treatment.

Description

technical field [0001] The invention relates to an anti-corrosion paint coating method, in particular to a coating method for an environmentally friendly paint which is suitable for the surface of a metal structure, has excellent gloss and mechanical and physical properties, and does not contain aromatic hydrocarbon solvents. Background technique [0002] In modern industry and daily life, metal corrosion can be seen everywhere, especially in the form of crevice corrosion, stress corrosion and corrosion fatigue in the storage containers of fuel oil and hazardous chemicals, which cause great safety hazards to people's lives. [0003] The metal protection methods currently used can be roughly divided into three categories: one is anodic oxidation treatment, that is, an anodic oxidation film with a thickness of tens of microns is formed on the metal surface, but due to the large energy consumption of the anodic oxidation process and the contamination of the electrolyte solution ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/08C09D179/08C09D7/12C09D5/08
Inventor 殷良策
Owner QINGDAO WINTEC SYSTEM CO LTD