Anti-corrosive paint coating method

An anti-corrosion coating and coating technology, applied in anti-corrosion coatings, coatings and other directions, can solve problems such as poor processing stability

Inactive Publication Date: 2013-03-27
青岛博益特生物材料股份有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the presence of strong oxidants, the stability of the treatment process is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Prepare the following components (parts by mass):

[0028] a 3-(triethoxysilyl)propyl acrylate 11;

[0029] b Methanol 60;

[0030] c SiO 2 Particle 6;

[0031] d Cerium oxide 6;

[0032] e deionized water 26;

[0033] f Acetic acid 3;

[0034] g carbon fiber 8;

[0035] h polyimide 3;

[0036] (2) Mix the above components and perform aging treatment, then spray, brush or dip on the surface of the substrate, and form a coating on the surface of the substrate after deposition to achieve surface anti-corrosion treatment.

Embodiment 2

[0038] (1) Prepare the following components (parts by mass):

[0039] a 3-(triethoxysilyl)propyl acrylate 20;

[0040] b Methanol 80;

[0041] c SiO 2 grain 10;

[0042] d cerium oxide 10;

[0043] e deionized water 50;

[0044] f Acetic acid 5;

[0045] g carbon fiber 10;

[0046] h polyimide 5;

[0047] (2) Mix the above components and perform aging treatment, then spray, brush or dip on the surface of the substrate, and form a coating on the surface of the substrate after deposition to achieve surface anti-corrosion treatment.

Embodiment 3

[0049] (1) Prepare the following components (parts by mass):

[0050] a 3-(triethoxysilyl)propyl acrylate 15;

[0051] b Methanol 70;

[0052] c SiO 2 particle 8;

[0053] d Cerium oxide 8;

[0054] e deionized water 38;

[0055] f acetic acid 4;

[0056] g carbon fiber 9;

[0057] h polyimide 4;

[0058] (2) Mix the above components and perform aging treatment, then spray, brush or dip on the surface of the substrate, and form a coating on the surface of the substrate after deposition to achieve surface anti-corrosion treatment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-corrosive paint coating method. The method comprises the following steps of: mixing components including siloxane, a solvent, silicon dioxide grains, a rare earth compound, de-ionized water, a catalyst, carbon fiber, polyimide and the like; subjecting the mixture to aging treatment; filtering the aged mixture; and then spray coating, brush coating or dipping the filtered mixture on a base material surface so as to form a coating on the base material surface after deposition, thus realizing surface anti-corrosive treatment.

Description

technical field [0001] The invention relates to an anti-corrosion paint coating method, in particular to a coating method for an environmentally friendly paint which is suitable for the surface of a metal structure, has excellent gloss and mechanical and physical properties, and does not contain aromatic hydrocarbon solvents. Background technique [0002] In modern industry and daily life, metal corrosion can be seen everywhere, especially in the form of crevice corrosion, stress corrosion and corrosion fatigue in the storage containers of fuel oil and hazardous chemicals, which cause great safety hazards to people's lives. [0003] The metal protection methods currently used can be roughly divided into three categories: one is anodic oxidation treatment, that is, an anodic oxidation film with a thickness of tens of microns is formed on the metal surface, but due to the large energy consumption of the anodic oxidation process and the contamination of the electrolyte solution ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D5/08
Inventor 冯伊琳李叶宋福来
Owner 青岛博益特生物材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com