Wire mesh flexible composite fabric for surface modification and preparation method of wire mesh flexible composite fabric

A metal wire mesh and surface modification technology, which is applied in the field of metal wire mesh flexible composite cloth and its preparation, can solve the problems of low bonding strength and thin metal protective coating, and achieves improved preparation formability, improved welding structure and Welding performance, the effect of excellent performance

Inactive Publication Date: 2013-03-13
NANCHANG INST OF TECH
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0028] The purpose of the present invention is to provide a kind of preparation method of the wire mesh flexible composite cloth that is aimed at the urgently needed protective coating requirements of high temperature, heavy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0059] Example 1

[0060] The specific formula of the wire mesh flexible composite cloth used for metal surface modification in this embodiment is: tungsten carbide (WC), nickel-chromium alloy powder (Ni 30 Cr 6 ) according to the weight of each substance: 62 parts of tungsten carbide (WC), nickel-chromium alloy powder (Ni 30 Cr 6 ) 29 servings. The total amount of molding agent and binder is 9 parts by weight. The molding agent is composed of the following parts by weight: 3 parts of rubber and 3 parts of stearic acid. The binder is 3 parts by weight of resin.

[0061] Mix the above materials thoroughly, and granulate by electromagnetic stirring, lay one layer of wire mesh on the hopper of the rolling equipment, and then lay the granulated powder on the wire mesh, and roll it in the rolling equipment. , to obtain a wire mesh flexible composite cloth. Roll forming in rolling equipment to obtain metal wire mesh flexible composite cloth.

Example Embodiment

[0062] Example 2

[0063] The specific formula of the wire mesh flexible composite cloth used for metal surface modification in this embodiment is: 62 parts of tungsten carbide (WC), nickel-chromium alloy powder (Ni 30 Cr 6 ) 32 servings. The total amount of molding agent and binder is 6 parts by weight. The molding agent is composed of the following parts by weight: 2 parts of rubber and 2 parts of stearic acid. The binder is 2 parts by weight of resin.

[0064] Mix the above materials thoroughly, and granulate by electromagnetic stirring, lay 2 layers of metal wire mesh on the hopper of the rolling equipment, and then lay the granulated powder on the wire mesh, and roll it in the rolling equipment. , to obtain a wire mesh flexible composite cloth. Roll forming in rolling equipment to obtain metal wire mesh flexible composite cloth.

Example Embodiment

[0065] Example 3

[0066] The specific formula of the wire mesh flexible composite cloth used for metal surface modification in this embodiment is: 62 parts of tungsten carbide (WC), nickel-chromium alloy powder (Ni 30 Cr 6 ) 35 servings. The total amount of the molding agent and the binder is 3 parts by weight. The molding agent is composed of the following parts by weight: 2 parts of rubber and 0.5 part of stearic acid. The binder is 0.5 parts by weight of resin.

[0067] Mix the above materials thoroughly, and granulate by electromagnetic stirring, lay 1 to 2 layers of wire mesh on the hopper of the rolling equipment, and then lay the granulated powder on the wire mesh, and roll it in the rolling equipment. Press molding to obtain a metal wire mesh flexible composite cloth. Roll forming in rolling equipment to obtain metal wire mesh flexible composite cloth.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a wire mesh flexible composite fabric for surface modification and a preparation method of the wire mesh flexible composite fabric. The wire mesh flexible composite fabric comprises wolfram carbide (WC) or WC-cobalt (Co), mechanically alloyed nickel-chromium alloy powder, a forming agent and a binding agent. The wire mesh flexible composite fabric for surface modification is made through roll forming. By adopting a mechanical alloying technology, a nanocrystalline technology and a wire mesh technology, the preparation forming property of the flexible fabric is greatly improved, the thickness of the flexible fabric is extremely controlled, and the design idea of gradient coatings of more than two layers can be realized, so that the stress is reduced and the welding texture and the welding property are improved. The WC coating with excellent performance is prepared.

Description

technical field [0001] The invention relates to a wire mesh flexible composite cloth specially used for preparing high-temperature and corrosion-resistant coatings and a preparation method thereof. It can be used for the protection of mechanical parts in power stations, petroleum, aviation, food, plastics and other fields. Background technique [0002] Friction, wear and corrosion are the main forms of failure of metal workpieces in various mechanical equipment, and the resulting economic losses caused by increased energy and material consumption are huge. Therefore, research on metal wear and wear-resistant and corrosion-resistant materials has always been Wide attention at home and abroad. [0003] Traditional surface coatings such as pre-clad coatings, wear-resistant coatings, spray welding, surfacing, thermal spray coatings, etc. still have serious deficiencies and disadvantages in terms of wear resistance, heat transfer and operation requirements, and can only provide ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C47/14C22C47/06C22C49/02C22C49/14C22C111/00C22C121/00
Inventor 晏建武张晨曙
Owner NANCHANG INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap