Soyabean protein adhesive for plywood and method for preparing same

A soybean protein and adhesive technology, which is applied in the preparation of protein adhesives, animal glue or gelatin, adhesives, etc., can solve the problems of unsatisfactory stability and viscosity, unobvious synergistic effect, complex components, etc. Value, source-rich, and easy-to-use effects

Active Publication Date: 2015-05-06
SCHOLAR HOME SHANGHAI NEW MATERIAL CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the actual use process, it was found that due to the complexity of its components and the lack of obvious synergistic effect between them, its stability and viscosity were not ideal, and its practicability was poor. Therefore, it is still necessary to propose an environmentally friendly soybean protein with excellent performance. adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soyabean protein adhesive for plywood and method for preparing same
  • Soyabean protein adhesive for plywood and method for preparing same
  • Soyabean protein adhesive for plywood and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] 1) Prepare materials according to the following weight ratio:

[0037]

[0038] Among them, the complexing agent is a powder prepared by the School of Materials Science and Technology of Beijing Forestry University, including zinc chloride: 0.8 parts, copper sulfate: 0.5 parts, zirconium carbonate: 0.5 parts, which are ground and mixed evenly; the reinforcing agent is Glutaraldehyde solution with a mass concentration of 30%.

[0039] 2) Add all the demineralized water, sodium carbonate and soy protein powder into the reaction kettle equipped with agitator, thermometer and condensing device, and stir evenly.

[0040] 3) Heating to 45-47°C, keeping it warm for 3 hours to obtain a mixture.

[0041] 4) Cool the mixture down to 30°C to make a uniform soy protein mucus.

[0042]5) Add a complexing agent to the soy protein mucus and stir evenly to make it undergo complexation reaction.

[0043] 6) Continue to add the enhancer to it and stir evenly to obtain the soybean p...

Embodiment 2

[0046] 1) Prepare materials according to the following weight ratio:

[0047]

[0048] Among them, the complexing agent is a powder prepared by the School of Materials Science and Technology of Beijing Forestry University, including 1.2 parts of zinc chloride, 1.5 parts of copper sulfate, and 1.5 parts of zirconium carbonate. 30% glutaraldehyde solution.

[0049] 2) Add all the demineralized water, sodium carbonate and soy protein powder into the reaction kettle equipped with agitator, thermometer and condensing device, and stir evenly;

[0050] 3) Heating to 40-42°C and reacting for 6 hours to obtain the mixture;

[0051] 4) Cool the mixture down to 30°C to make a uniform soy protein mucus.

[0052] 5) Add a complexing agent to the soy protein mucus and stir evenly to make it undergo complexation reaction.

[0053] 6) Continue to add the enhancer to it and stir evenly to obtain the soybean protein adhesive.

[0054] The performance and quality indicators of the adhesiv...

Embodiment 3

[0056] 1) Prepare materials according to the following weight ratio:

[0057]

[0058]

[0059] Among them, the complexing agent is a powder prepared by the School of Materials Science and Technology, Beijing Forestry University, including the following components in weight proportions: 0.8 parts of zinc chloride, 1.5 parts of copper sulfate, and 1 part of zirconium carbonate, which are ground evenly and mixed Uniform; the enhancer is a glutaraldehyde solution with a mass concentration of 40%.

[0060] 2) Add all the demineralized water, sodium carbonate and soy protein powder into the reaction kettle equipped with agitator, thermometer and condensing device, and stir evenly.

[0061] 3) Heating to 68-70°C and reacting for 5 hours to obtain a mixture.

[0062] 4) Cool the mixture down to 30°C to make a uniform soy protein mucus.

[0063] 5) Add a complexing agent to the soy protein mucus and stir evenly to make it undergo complexation reaction.

[0064] 6) Continue to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a soyabean protein adhesive for a plywood, prepared from the following raw materials according to parts by weight: 70-80 parts of dispersion medium, 20-35 parts of degreased soyabean protein powder, 0.5-3 parts of sodium carbonate, 1-2 parts of complexing agent and 1-5 parts of enhancer. The adhesive provided by the invention has the characteristics that all the components have excellent mutual synergistic effect, a material such as a metal salt is compounded with the soybean protein, and simultaneously, glutaraldehyde is taken as the enhancer so that the problem of poor water resistence of the common soybean protein adhesive is solved; therefore, the adhesive is capable of meeting the waterproof requirement of the adhesive for the plywood and guaranteeing the practical performance of the soybean protein adhesive; and the plywood prepared by using the adhesive provided by the invention is capable of meeting the international requirements of the class II plywood. Besides, the invention also provides a method for preparing the soyabean protein adhesive for the plywood; and the method is simple in process, convenient for operation and suitable for popularization and application.

Description

technical field [0001] The invention relates to an adhesive and a preparation method thereof, in particular to a soybean protein adhesive used for preparing plywood and a preparation method thereof. Background technique [0002] In 2010, the total output of my country's wood-based panels was 153.6 million cubic meters, accounting for about 50% of the world's weight, including 71.3966 million cubic meters of plywood and 16.5228 million cubic meters of blockboard. The total output of wood-based panels, plywood, furniture, and wood flooring has ranked first in the world for many years in a row. [0003] The adhesives commonly used in the production of wood-based panels are formaldehyde-based synthetic resins, mainly urea-formaldehyde resins and their modified products. Although after years of hard work, the production level of wood-based panel adhesives in my country has been greatly improved, and the environmental protection characteristics of wood-based panels and their prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J189/00C09J11/04C09J11/06
Inventor 李建章秦志永周文瑞张纪芝张世锋高强
Owner SCHOLAR HOME SHANGHAI NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer