Method of using common rock ballast as slag-modifier agent for silicomanganese alloy smelting
A technology of silicomanganese alloy and slagging agent, which is applied in the field of metallurgy, can solve the problems of increased energy consumption, prolonged time, and high price of slag adjusting agent, and achieves the effects of high moisture resistance, high construction cost, and cost reduction
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] Silicon-manganese alloy smelting After the molten iron is released, ordinary rock slag with a particle size of 10-50mm and a calcium carbonate content of 50wt% is added to the submerged arc furnace. The ordinary rock slag is calcined for 60 minutes under the waste heat of the submerged arc furnace to decompose the calcium carbonate in it to form calcium oxide. , add manganese ore, coke, and silica that meet the requirements of silicomanganese alloy smelting, mix evenly, and smelt with conventional smelting techniques to obtain silicomanganese alloy; 2 ) is 0.6~0.8.
[0020] Note: Each time before adding ordinary gravel, the composition of the gravel will be tested to obtain the content of calcium carbonate and silicon dioxide.
[0021] Before adding manganese ore, coke, and silica, the content of each component will also be detected to meet the requirements of the compound smelting ratio of the added manganese ore, coke, and silica. At the same time, the content of calc...
Embodiment 2
[0023] After the silicon-manganese alloy is smelted and released from the furnace in Example 1, ordinary stone slag with a particle size of 10 to 50 mm and a calcium carbonate content of 90wt% is added to the submerged arc furnace. Calcium is decomposed to generate calcium oxide, and manganese ore, coke, and silica that meet the requirements of silicomanganese alloy smelting are added, mixed evenly, and smelted by conventional smelting processes to obtain silicon-manganese alloy; the amount added is to make the slag alkalinity n(CaO+MgO) / n (SiO 2 ) is 0.6~0.8.
[0024] Note: Each time before adding ordinary gravel, the composition of the gravel will be tested to obtain the content of calcium carbonate and silicon dioxide. , silica compound smelting ratio requirements, and also detect the content of calcium oxide, silicon dioxide and magnesium oxide in manganese ore, coke and silica, and then calculate how much ordinary rock slag should be added to make the alkalinity n(CaO+Mg...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap