Process of terylene breathable flame-retardant fabric

A process method and fuel-resistant technology, applied in the textile field, can solve the problems of cloth color change, economic loss, etc.

Inactive Publication Date: 2013-04-17
南通卓越纺织涂层有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The common method of polyester breathable flame-retardant fabric is to soak and roll the flame retardant and then dry it after setting. As the fabric dries in the shade, patches of mottling will appear, and the color of the fabric will also change, directly causing economic losses
Flame retardants on the market will produce this phenomenon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] (1) Preparation of retardant working fluid:

[0014] Formula: FR-SH, water and 0.3% waterproofing agent;

[0015] Mix and stir the above three raw materials to obtain a fuel retardant working fluid, which is set aside;

[0016] (2) The base fabric is dipped and rolled in the above-mentioned fuel-resistant working fluid by a setting machine with a temperature of 140°C and a vehicle speed of 60m / min, and dried;

[0017] (3) After the cloth is released, it is soaked and rolled in the working liquid of waterproofing agent with a concentration of 0.2% by a setting machine with a temperature of 140°C and a speed of 60m / min, and then dried;

[0018] (4) After the cloth is released, the finished product is obtained.

[0019] The cloth obtained by the present invention has excellent flame retardancy, and after the weather of rain and fog, there are basically no spots on the cloth, and the color of the cloth does not change in any way.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process of a terylene breathable flame-retardant fabric. The process is characterized in that a protection film enabling the fabric not to be wetted easily can be formed on the breathable flame-retardant fabric by filling waterproof agents into fire retardants, and the flame-retardant performance of the fabric cannot be affected.

Description

technical field [0001] The invention relates to a process method for polyester air-permeable flame-retardant fabric, which belongs to the field of textiles. Background technique [0002] The common method of polyester breathable flame-retardant fabric is to soak and roll the flame retardant and then dry it after setting. As the cloth dries in the shade, patches of piebald spots are produced, and the color of the cloth will also change, directly causing economic losses. All flame retardants on the market will have this phenomenon. Contents of the invention [0003] In order to overcome the shortcomings of the prior art, the present invention provides a process method for polyester breathable flame-retardant fabric, which is characterized in that: the specific steps are as follows: [0004] (1) Preparation of retardant working fluid: [0005] Formula: FR-SH, water and 0.3% waterproofing agent; [0006] Mix and stir the above three raw materials to obtain a fuel retardant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06B3/18
Inventor 刘卫星
Owner 南通卓越纺织涂层有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com