Novel cement grinding aid and preparation method thereof and application thereof

A cement grinding aid, a new type of technology, applied in the field of new cement grinding aids and its preparation, can solve the problem that the lattice cohesion cannot be effectively reduced, the surface adsorption of solid particles is not strong, and the grinding efficiency of cement grinding aids is low and other problems, to achieve the effect of reducing the stickiness of materials, increasing the compressive strength, and increasing the time

Active Publication Date: 2013-05-01
溧阳市精卫新型材料有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the production process of cement grinding, the grinding efficiency of the cement grinding aid used is low, and the strengthening effect is not obvious. The strength and hardness of the particles, as well as the lattice cohesion at the interface, cannot be effectively reduced. Only when more grinding aid molecules are adsorbed on the surface of the cracks of the rolled object, a protective layer is formed, which is conducive to the expansion of particle cracks and prevents cracks. Heal, play a grinding aid effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel cement grinding aid and preparation method thereof and application thereof
  • Novel cement grinding aid and preparation method thereof and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] First, add 670g of water into the reaction pot, start stirring, add 150g of commercially available polymerized mixed fat, 100g of molasses, 100g of ethylene glycol monoisopropanolamine, and 30g of triethanolamine, and stir for 2 hours to obtain the finished product.

Embodiment 2

[0021] First, add 460g of water into the reaction pot, start stirring, add 280g of commercially available polymerized mixed fat, 50g of molasses, 150g of ethylene glycol monoisopropanolamine, and 90g of triethanolamine, and stir for 2 hours to obtain the finished product.

Embodiment 3

[0023] First, add 250g of water into the reaction pot, start stirring, add 400g of commercially available polymerized mixed fat, 250g of ethylene glycol monoisopropanolamine, and 150g of triethanolamine, and stir for 2 hours to obtain the finished product.

[0024] The cement grinding aid that example 1-3 is synthesized is applied small grinding test result as follows:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel cement grinding aid. The novel cement grinding aid comprises the following components in part by weight: 3-15 parts of triethanolamine, 10-25 parts of ethylene glycol monoisopropanolamine, 15-40 parts of polymerized mixed lipid, 5-15 parts of molasses and 25-67 parts of water. The invention further provides a preparation method of the novel cement grinding aid; and the preparation method comprises the following steps: adding 25-67 parts of water to a reaction pot; rapidly stirring the water; adding 15-40 parts of polymerized mixed lipid, 5-15 parts of molasses, 10-25 parts of ethylene glycol monoisopropanolamine and 3-15 parts of triethanolamine to the reaction pot; and stirring an obtained mixture for 2 hours so as to obtain a finished product. The invention further provides an application of the cement grinding aid; and during manufacture of a cement through pulverizing, the cement grinding aid which accounts for 0.03-0.1% of the total weight of the cement is blended in 45-85 parts of clinkers, 10-25 parts of fly ashes, 5-15 parts of slag and 5-10 parts of gypsums by weight.

Description

technical field [0001] The invention belongs to the field of cement admixtures, and in particular relates to a novel cement grinding aid and its preparation method and application. Background technique [0002] At present, in the production process of cement grinding, the grinding efficiency of the cement grinding aid used is low, and the strengthening effect is not obvious. The strength and hardness of the particles, as well as the lattice cohesion at the interface, cannot be effectively reduced. Only when more grinding aid molecules are adsorbed on the surface of the cracks of the rolled object, a protective layer is formed, which is conducive to the expansion of particle cracks and prevents cracks. Heal and play a grinding aid effect. Contents of the invention [0003] The invention can significantly improve the fluidity and dispersibility of the material in the mill, reduce the stickiness of the material, and at the same time quickly provide foreign ions to satisfy th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/24C04B28/14C04B103/52
Inventor 张天喜
Owner 溧阳市精卫新型材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com