Casting-rolling method for aluminum alloy plate

An aluminum alloy plate, casting and rolling technology, applied in the field of metal plate processing, can solve problems such as affecting product quality, horseshoe-shaped cracks, failure of vertical plates, etc., and achieve the effects of improving labor productivity, large throughput and reasonable configuration

Active Publication Date: 2015-04-08
SHANDONG XINTONG ALUMINUM IND
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, if the traditional casting and rolling method is used for production, due to the high content of impurities in the melt, it will cause technical problems such as vertical plate failure, sticking rolls and horseshoe-shaped cracks, which will affect product quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Casting-rolling method for aluminum alloy plate
  • Casting-rolling method for aluminum alloy plate
  • Casting-rolling method for aluminum alloy plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] It can be seen from the records in the background technology that the deformation of the 3004 aluminum alloy plate processed by the direct water cooling method (DC method) is large, and the processing cost is relatively high in terms of economy and energy consumption. For this reason, the inventor considers adopting the casting-rolling method to process 3004 aluminum alloys. The continuous casting-rolling method has: less investment, quick results, and short payback period, which is feasible for small and medium-sized aluminum strip rolling plants; the metal throughput is large and can be used Recycling scrap as raw material, the production cost is low, and the price is quite competitive; the time from melt to ingot to hot-rolled strip or re-rolling is considerably reduced, and processes such as ingot, milling, and billeting are omitted , Improve labor productivity; reduce energy consumption due to a series of processes required for hot rolling.

[0035] The casting and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a casting-rolling method for an aluminum alloy plate. The method includes the following steps: furnace charge is placed in a smelting furnace and smelted into melt under the temperature of 700DEG C to 800DEG C, and the melt is refined for one time with argon blown into the smelting furnace and slag-off is carried out for one time every 1.5h to 2.5h; the melt is led into a still standing furnace, the temperature in the furnace is kept to be 725DEG C to 740 DEG C, 2kg / t to 3 kg / t of refining agents are added after still standing lasts for 15min to 1h, and the slag-off is carried out for one time after refining; the melt in the still standing furnace is led into a degasification tank, argon is blown into the degasification tank for degassing and refining every 1.5 to 2.5h, and the slag-off is carried out every 1h; the melt in the degasification tank is led into a filter tank to filter out impurities in the melt; and the melt is led into a middle upright plate of a front tank through a launder of the front tank, the liquid level of the melt in the front tank is controlled, and the melt is led into a double-roller continuous casting-rolling mill through a feeding mouth to form strip plates by continuous casting-rolling. The casting-rolling method for the aluminum alloy plate is little in investment and fast in effect achievement.

Description

technical field [0001] The invention belongs to the technical field of metal plate processing, and more specifically relates to a casting and rolling method of an aluminum alloy plate. Background technique [0002] 3004 aluminum alloy is used for punching cans, ship decks, food packaging and other industries. 3004 aluminum alloy punched cans have high yield, good decorative performance, strong plasticity and excellent anti-corrosion performance. Main technical indicators: the tensile strength of H28 is not less than 260MPa, and the elongation is greater than 3%; the tensile strength of H12 is 190-240MPa, and the elongation is greater than 5%. [0003] At present, the manufacturing process of 3004 aluminum alloy adopts direct water cooling method (DC method), including casting, ingot homogenization heat treatment, hot rolling, recrystallization annealing, cold rolling, annealing, and finally obtains foil 3004 aluminum alloy strip for packaging materials. Blank. Due to the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/06B22D21/04
Inventor 吴正晖张大庆张雷袁之国
Owner SHANDONG XINTONG ALUMINUM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com