Inorganic art mineral coating and construction method thereof
A kind of art and mineral technology, applied in the field of inorganic art mineral paint and its construction, can solve the problems of easy aging, easy fading, mildew, etc., and achieve the effect of eliminating peculiar smell, wide applicability and strong adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0024] Raw material composition of inorganic art mineral paint: 200g of white silicate 42.5 cement (whiteness greater than 87%), 400g of heavy calcium carbonate (300-400 mesh), 300g of highly active diatomite (200-400 mesh), iron oxide yellow 15g, wood fiber (length less than 400μm) 3g, low viscosity cellulose ether (MKX15000PP20) 4g, AGITAN P803 defoamer 0.5g, CASUCOL301 starch ether (fineness less than 500μm) 1.5g, ethylene, vinyl chloride and vinyl laurate Ternary copolymerization redispersible latex powder 20g, Thixotropic lubricant 2g, calcium formate 4g, high activity alkali elimination powder 20g, negative ion powder 15g, nano titanium dioxide 15g.
[0025] Preparation method: Add the above raw materials into a high-speed mixer and stir for a few minutes to obtain an inorganic art mineral paint.
Embodiment 2
[0027] Raw material composition of inorganic artistic mineral paint: white silicate 42.5 cement (whiteness greater than 87%) 150g, 42.5 white high-alumina cement (whiteness greater than 87%) 70g, heavy calcium carbonate (300-400 mesh) 375g, high activity Diatomaceous earth (200-400 mesh) 310g, iron oxide yellow 12g, wood fiber (length less than 400μm) 4g, low viscosity cellulose ether (MH10005P2) 5g, AGITAN P803 defoamer 0.5g, CASUCOL301 starch ether (fineness less than 500μm) 1.5g, terpolymerized redispersible latex powder of ethylene, vinyl chloride and vinyl laurate 18g, Thixotropic lubricant 2g, sodium citrate 2g, high activity alkali elimination powder 15g, negative ion powder 18g, nano titanium dioxide 17g.
[0028] The preparation method is the same as in Example 1.
Embodiment 3
[0030] Raw material composition of inorganic art mineral paint: 250g of 42.5 white high alumina cement (whiteness greater than 87%), 300g of heavy calcium carbonate (300-400 mesh), 375g of high active diatomite (200-400 mesh), 16g of cobalt blue, Wood fiber (length less than 400μm) 5g, low viscosity cellulose ether (MH10007P4) 6g, AGITAN P803 defoamer 0.5g, CASUCOL301 starch ether (fineness less than 500μm) 1.5g, ethylene, vinyl chloride and vinyl laurate ternary Copolymerized redispersible latex powder 15g, Thixotropic lubricant 2g, sodium citrate 2g, anion powder 13g, nano titanium dioxide 14g.
[0031] The preparation method is the same as in Example 1.
PUM
Property | Measurement | Unit |
---|---|---|
length | aaaaa | aaaaa |
whiteness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com