Composite pulverized coal modifier, modified coal prepared by using composite pulverized coal modifier, and preparation method of modified coal

A modifier and pulverized coal technology, which is applied in fuel, solid fuel, petroleum industry, etc., can solve the problem of limited non-coking coal consumption, and achieve the effect of saving coking coal resources and reducing coking costs

Active Publication Date: 2013-06-12
CHONGQING UNIV
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in traditional coal blending and coking, the amount of directly blending non-coking coal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Preparation of composite pulverized coal modifier (composite pulverized coal modifier is 100kg), its components and mass percentages are:

[0019] 3% phenylacetic acid, 5% borax, 10% boron oxide, 35% boric acid, 9.8% calcium dodecylbenzenesulfonate, 8% N-acyl glutamate, 9% powdered polyethylene, 10 atactic polypropylene %, sodium bentonite and calcium bentonite 0.2%, iron concentrate powder 10%.

[0020] According to the above proportions, compound coal powder modifier is prepared, and it is ball milled and mixed.

[0021] Preparation of modified coal (quantitative amount of modified coal is 1000Kg), its components and mass percentages are: 0.05% of composite pulverized coal modifier in this embodiment, 49.95% of long-flame coal, and 50% of anthracite.

[0022] The preparation method of the modified coal is as follows: grind the composite pulverized coal modifier of this embodiment into powder, and pulverize the non-coking coal so that the particle size of the two powd...

Embodiment 2

[0026] Preparation of composite pulverized coal modifier (composite pulverized coal modifier is 100kg), its components and mass percentages are:

[0027] 10% phenylacetic acid, 25% borax, 0.3% boron oxide, 30% boric acid, 0.2% calcium dodecylbenzenesulfonate, 15% N-acyl glutamate, 0.2% powdered polyethylene, 18 atactic polypropylene %, sodium bentonite 1%, iron concentrate powder 0.3%.

[0028] According to the above proportions, compound coal powder modifier is prepared, and it is ball milled and mixed.

[0029] Preparation of modified coal (quantitative amount of modified coal is 1000Kg), its components and mass percentage content are: 0.1% of the composite pulverized coal modifier of this embodiment, 30% of long-flame coal, 30% of non-caking coal, and 39.9% of anthracite %.

[0030] The preparation method of the modified coal is as follows: grind the composite pulverized coal modifier of this embodiment into powder, and pulverize the non-coking coal so that the particle s...

Embodiment 3

[0034] Preparation of composite pulverized coal modifier (composite pulverized coal modifier is 100kg), its components and mass percentages are:

[0035] 0.3% phenylacetic acid, 0.3% borax, 30% boron oxide, 50% boric acid, 8.5% calcium dodecylbenzenesulfonate, 0.2% N-acyl glutamate, 0.5% powdered polyethylene, 0.2 atactic polypropylene %, calcium-based bentonite 5%, iron concentrate powder 5%.

[0036] According to the above proportions, compound coal powder modifier is prepared, and it is ball milled and mixed.

[0037] Preparation of modified coal (quantitative amount of modified coal is 1000Kg), its components and mass percentage content are: 0.5% of the composite pulverized coal modifier of this embodiment, 14.5% of non-caking coal, 20% of weakly caking coal, long flame Coal 30%, anthracite 35%.

[0038] The preparation method of the modified coal is as follows: grind the composite pulverized coal modifier of this embodiment into powder, and pulverize the non-coking coal s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite pulverized coal modifier, a modified coal prepared by using the composite pulverized coal modifier, and a preparation method of the modified coal. The pulverized coal modifier comprises the following components in percentage by mass: 0.1-10% of phenylacetic acid, 0.1-25% of borax, 0.1-30% of boron oxide, 30-50% of boric acid, 0.1-10% of calcium dodecyl benzene sulfonate, 0.1-15% of N-acyl glutamate, 0.1-10% of polyethylene powder, 0.1-20% of atactic polypropylene, 0.1-5% of sodium bentonite or/and calcium bentonite, and 0.1-15% of iron ore concentrates. The modified coal comprises the following components in percentage by mass: 0.01-3% of the composite pulverized coal modifier and 97-99.99% of non-coking coal. The preparation method of the modified coal comprises the following steps of: milling the composite pulverized coal modifier into a powder; crushing non-coking coal; placing the non-coking coal and the composite pulverized coal modifier in a reactor, and adequately mixing and reacting; controlling a temperature in the reactor to be 25-300 DEG C; and controlling the reaction time for more than 30 minutes. The composite pulverized coal modifier, the modified coal prepared by using the composite pulverized coal modifier, and the preparation method for the modified coal disclosed by the invention have the advantage that the mass ratio of the modified non-coking coal occupying coking blended coal is up to more than 70%, so that the resources of coking coal can be saved, and the coking cost can be greatly decreased.

Description

technical field [0001] The invention relates to the technical field of coal blending and coking, in particular to a composite pulverized coal modifier, modified coal prepared by using the composite pulverized coal modifier, and a preparation method of the modified coal. Background technique [0002] Although the world's coal resources are abundant, the coal resources for coking are very limited. Therefore, economical use and expansion of the scope of coking coal have been widely valued both at home and abroad. With the rapid development of my country's iron and steel industry and the large-scale blast furnace, the demand for coke and the quality requirements are also increasing. In 2012, the output of iron and steel in my country was 680 million tons and 720 million tons respectively, and the output of coke was 443 million tons, equivalent to about 600 million tons of raw coal for coking. Although my country has abundant coal resources and a complete range of coal types, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10B57/06C10L9/10
Inventor 朱子宗
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap