Method for preparing hydrocracking catalyst

A hydrocracking and catalyst technology, applied in the direction of physical/chemical process catalysts, molecular sieve catalysts, chemical instruments and methods, etc., can solve the problems of poor dispersion of performance metals and low utilization efficiency, and achieve low cost, little pollution, The effect of simple solution preparation

Active Publication Date: 2013-07-10
CHINA PETROLEUM & CHEM CORP +1
View PDF15 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the limitation of existing conventional metal-content hydrocracking catalyst performance deficiency and the limitation of the preparation method of hydrocracking catalyst with poor metal dispersion and low utilization efficiency, the present invention provides a large pore volume, large specific surface area, hydrogenation activity The preparation method of high hydrocracking catalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Take 1000g of alumina dry rubber powder and amorphous silica-alumina powder respectively for steam treatment, at a gauge pressure of 0.05MPa, a hydrothermal treatment temperature of 45°C, and a treatment time of 1.5 hours, the obtained alumina dry rubber powder after hydrothermal treatment The moisture content of the amorphous silica and aluminum is 35wt% and 36wt%, respectively, and the codes are LA-1 and LSA-1.

Embodiment 2

[0040] Take 1000g of alumina dry rubber powder and amorphous silica-alumina dry rubber powder respectively for water vapor treatment, at a gauge pressure of 0.08MPa, a hydrothermal treatment temperature of 75°C, and a treatment time of 2 hours, the resulting hydrothermally treated alumina dry powder The water content of rubber powder and amorphous silica-alumina is 43wt% and 42wt% respectively, coded as LA-2 and LSA-2.

Embodiment 3

[0042] Take 1000g of alumina dry rubber powder and amorphous silica-alumina dry rubber powder respectively for water vapor treatment, at a gauge pressure of 0.1MPa, a hydrothermal treatment temperature of 90°C, and a treatment time of 3 hours, the obtained alumina dry rubber after hydrothermal treatment The water content of the powder and amorphous silica-alumina is 50wt% and 49wt% respectively, coded as LA-3 and LSA-3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a hydrocracking catalyst. The method comprises the following steps of carrying out hydrothermal treatment on alumina dry gel powder, uniformly mixing the treated alumina dry gel powder and at least one acidic cracking material powder, dipping the mixture into a hydrogenation active ingredient-containing metal salt solution, carrying out filtration, drying and crushing, adding a peptizing agent or a binder into the crushed product, and carrying out molding, drying and calcination to obtain the hydrocracking catalyst. The hydrocracking catalyst has high hydrogenation active ingredient content, a large pore volume, a large aperture size and a large specific surface area, and is suitable for hydrocracking of a heavy vacuum distillate having a higher boiling point.

Description

technical field [0001] The invention relates to a method for preparing a hydrocracking catalyst, in particular to a method for preparing a hydrocracking catalyst capable of processing heavy distillate oil with high activity. Background technique [0002] Hydrocracking technology has the characteristics of strong adaptability to raw materials, great flexibility in production operations and product plans, and good product quality. It can directly convert various heavy and low-quality feedstocks into high-quality jet fuel, diesel, and lubricating oil base materials that are urgently needed by the market. As well as chemical naphtha and tail oil steam cracking raw materials for ethylene production, it has become one of the most important heavy oil deep processing processes in modern oil refining and petrochemical industries, and has been increasingly widely used at home and abroad. [0003] However, due to the deterioration of crude oil quality year by year, a substantial increa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J29/16C10G47/20
Inventor 刘昶王凤来杜艳泽赵红关明华
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap