Preparation method of seamless steel pipe for nuclear power containing rare earth

A seamless steel pipe and rare earth technology, which is applied in the preparation of rare earth-containing seamless steel pipes for nuclear power, and in the field of rare earth-containing seamless steel pipes for nuclear power, can solve the problems of increased power generation costs and aggravated environmental pollution, and achieve high production efficiency and high production efficiency. Process energy saving and environmental protection, good compressive strength and high temperature resistance

Active Publication Date: 2015-11-18
INNER MONGOLIA BAOTOU STEEL UNION
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the long-distance transportation of coal to coastal areas for power generation, 48% of the railway transportation capacity and 25% of the road transportation capacity are occupied, which not only increases the cost of power generation, but also aggravates the environmental pollution of conventional power plants in this area

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of seamless steel pipe for nuclear power containing rare earth
  • Preparation method of seamless steel pipe for nuclear power containing rare earth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The invention adopts Baotou Steel's own ore as raw material, and the ore contains rare earth elements. The rare earth elements include La and Ce.

[0013] The steelmaking production process of steel is:

[0014] The steel smelting and continuous casting process is molten iron pretreatment→converter smelting→LF refining→VD degassing→round billet continuous casting. The smelting uses a 100-ton top-bottom combined blowing converter, using desulfurized molten iron, ferrosilicon, ferromanganese and other alloys using deoxidation alloying, single slag process, and the final slag alkalinity is controlled at 3.0. The final composition of the converter is controlled to be no less than 0.03% carbon, no more than 0.01% phosphorus, the temperature of the molten steel in the converter is controlled above 1600°C, and 100-300kg of limestone is added during the tapping process. LF refining adopts single refining production, and the whole process is blown argon according to the normal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rare earth-containing nuclear seamless steel tube material. The seamless steel tube material comprises components in percentage by weight: 0.12-0.18 of C, 0.17-0.37 of Si, 0.6-1.0 of Mn, 0.016-0.018 of Cr, 0.02-0.04 of V, no more than 0.015 of P, no more than 0.010 of S, 0.002-0.005 of Re, and the balance of Re, wherein the sum of mass percentage is 100%. The invention further discloses a preparation method of the earth-containing nuclear seamless steel tube material. The preparation method is unique in production technique, high in production efficiency, low in cost and energy-saving and environment-friendly in production technique, the produced seamless steel tube is good in compressive strength and high-temperature resistance property, high in economic benefits, and suitable for large-scale production, and has good popularization values.

Description

technical field [0001] The invention relates to a metallurgical material technology, in particular to a preparation method of a rare earth-containing seamless steel pipe for nuclear power, which can prepare the rare earth-containing seamless steel pipe for nuclear power with better compressive strength and high temperature resistance. Background technique [0002] Among my country's natural energy resources, about 80% of coal is concentrated in the northwest and north; about 70% of water resources are distributed in the southwest. The eastern and southeastern coastal areas with dense population, rapid economic development and high demand for electricity are extremely scarce in natural energy resources. The contradiction between power supply and demand in the eastern and southeastern coastal areas with rapid economic development is more prominent, and it has led to "transporting electricity from west to east, coal from north to south" and pressure on environmental protection ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/24
Inventor 石晓霞刘金马爱清靳燕张行刚惠志国
Owner INNER MONGOLIA BAOTOU STEEL UNION