Matte surface and semi-matte surface rubber flooring and manufacturing method and special equipment
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of rubber floor and matte surface, which is applied in the manufacture of semi-matte surface, and the surface of rubber floor is treated into a matte surface, which can solve the problem that the floor is difficult to adapt to
Active Publication Date: 2015-06-17
陕西秦力橡胶有限责任公司
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, it is difficult to adapt to the existing rubber floor manufacturing process to directly manufacture matte or semi-matte floor
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0021] 46.4 kg of styrene-butadiene rubber and 11.6 kg of nitrile rubber were masticated on the open mill first, and after mixing evenly, they were put into the internal mixer. The temperature of the internal mixer is 90~100 ℃, add 0.87 kg of accelerator A, 0.58 kg of accelerator B, 2.9 kg of zinc oxide, 3.48 kg of stearic acid, 1.16 kg of anti-aging agent, 29 kg of white carbon black, 34.8 kg of filler, retardant 29 kg of fuel material and 4.64 kg of pigment, after mixing for 11 to 12 minutes, discharge. After the temperature of the mixed rubber is cooled to 40-50 °C, add 2.32 kg of sulfur, mix well, and then remove the sheet, cool, park and set aside. Accelerator A is a sulfenic acid amine accelerator, accelerator B is a dithiocarbamate accelerator, the anti-aging agent is a phenolic anti-aging agent, the filler is clay, and the flame-retardant material is an inorganic flame-retardant material and zinc borate , the pigment is a phthalocyanine blue pigment.
[0022] Roll ou...
Embodiment 2
[0027] 46.4 kg of styrene-butadiene rubber and 11.6 kg of nitrile rubber were masticated on the open mill first, and after mixing evenly, they were put into the internal mixer. The temperature of the internal mixer is 90~100 ℃, add 0.87 kg of accelerator A, 0.58 kg of accelerator B, 2.9 kg of zinc oxide, 3.48 kg of stearic acid, 1.16 kg of anti-aging agent, 29 kg of white carbon black, 34.8 kg of filler, retardant Combustible material 29 kg and color masterbatch 4.64 kg, after mixing for 11-12 minutes, discharge. After the temperature of the mixed rubber is cooled to 40-50 °C, add 2.32 kg of sulfur, mix well, and then remove the sheet, cool, park and set aside. Accelerator A is a sulfenic acid amine accelerator, accelerator B is a dithiocarbamate accelerator, the anti-aging agent is a phenolic anti-aging agent, the filler is clay, and the flame-retardant material is an inorganic flame-retardant material and zinc borate , the color masterbatch is phthalocyanine blue color mast...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to a matte surface and semi-matte surface rubber flooring which is manufactured from the following raw materials in parts by weight: 55-80 parts of butadiene styrene rubber, 20-45 parts of butadiene-acrylonitrile rubber, 3-5 parts of zinc oxide, 2-6 parts of stearic acid, 2-4 parts of accelerant, 1-2 parts of anti-aging agent, 30-50 parts of white carbon black, 40-80 parts of filler, 30-50 parts of flame-retardant mixture material, 3-6 parts of sulfur and 5-10 parts of pigment. Meanwhile, the invention provides a method for manufacturing the bottom plate, as well as special equipment. Devices and materials are increased on the basis of the technical equipment of the original rubber flooring manufacturing process, and the aim of producing the matte surface and semi-matte surface rubber flooring is fulfilled according to the re-determined process technology conditions. Compared with the rubber flooring produced through a matte drum, the matte surface and semi-matte surface rubber flooring has the advantages that the equipment investment is greatly reduced, and the adverse factors that the drum surface is easily dirty and difficult to clean are eliminated.
Description
technical field [0001] The invention relates to a method for manufacturing a rubber floor, in particular to a method for manufacturing a rubber floor whose surface is treated to a matte or semi-matte surface. Background technique [0002] As a new type of flexible flooring material, rubber flooring has the characteristics of beauty, comfort, safety, economy and meeting the requirements of special conditions. With the improvement of people's living standards, people are more and more pursuing a higher quality of life, especially in recent years, they have put forward higher and higher requirements for its appearance quality. People are no longer satisfied with the original bright surface products with high luminous intensity on the surface, and hope that the surface of the product has no reflection or low reflection, so that the light in the space is softer and more suitable for human senses. However, it is difficult to adapt to the existing rubber floor manufacturing proces...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More