A kind of superficial root fruit tree soil conditioner and production method thereof
The technology of a soil conditioner and a production method is applied in the field of soil conditioners for superficial root fruit trees, can solve the problems not mentioned, and achieve the effects of improving the survival rate, reducing the cost of afforestation, and having high economic value.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0041] 1) The main component of acrylic acid with a molar ratio of 1:0.25 and the auxiliary components of potassium polyacrylamide and polyacrylamide are polymerized for 40 minutes at a temperature of 300°C in a reactor, and the product is cooled and crushed by impact Machine crushing, the crushed products pass through the grading vibrating sieve, and the finished products between 40 and 80 mesh are taken, sieved, and the undersize and oversize are removed. Check that the pH is less than or equal to 7, then it can be used for later use.
[0042] 2) The bentonite attapulgite clay used as the ATB carrier material is subjected to rough selection, selection, and impurity removal processes to make the crystal attapulgite content > 70%, and after crushing, add 3% by weight of MgO and mix it to control the viscosity ≥ 2000mpa.s , through a 120-mesh sieve, and the ATB carrier material moisture ≤ 12% can be used for later use.
[0043] 3) Get 38 parts of the 120 mesh ATB carrier mater...
Embodiment 2
[0045] 1) The main component acrylic acid and the auxiliary component polyacrylamide with a molar ratio of 1:0.25 are polymerized and synthesized in a reactor at a temperature of 350°C for 40 minutes, and the product is cooled out of the reactor and crushed by an impact crusher. The broken products pass through the grading vibrating sieve, and the finished products between 40 and 80 meshes are taken, sieved, and the undersize and oversize are removed. Check that the pH is less than or equal to 7, then it can be used for later use.
[0046] 2) The montmorillonite attapulgite clay used as the ATB carrier material is subjected to rough selection, selection, and impurity removal processes to make the crystal attapulgite content > 70%, and after crushing, add 3% by weight of MgO and mix it to control the viscosity ≥ 2000mpa .s, through a 120-mesh sieve, ATB carrier material moisture ≤ 12% can be used for later use.
[0047] 3) Add 35 parts of 35 parts containing a large amount of ...
Embodiment 3
[0049] 1) The main component of acrylic acid with a molar ratio of 1:0.25 and the auxiliary component of polyacrylamide potassium are polymerized and synthesized in a reactor at a temperature of 400°C for 40 minutes, and the product is cooled and crushed by an impact crusher. The product is passed through a grading vibrating sieve, and the finished product between 40 and 80 meshes is taken, sieved, and the undersize and oversize are removed. Check that the pH is less than or equal to 7, then it can be used for later use.
[0050] 2) After the silicate attapulgite clay used as the ATB carrier material is roughed, selected, and impurity-removed, the crystal attapulgite content is > 70%, and after crushing, 3% by weight of MgO is added to mix it to control the viscosity ≥ 2000mpa .s, through a 120-mesh sieve, ATB carrier material moisture ≤ 12% can be used for later use.
[0051] 3) Add 30 parts of 40 parts of ATB carrier material components containing a large amount of elements...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| particle size | aaaaa | aaaaa |
| water absorption | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More