Waste oil-based environment-friendly mold separating agent and preparation method thereof

A waste oil, environment-friendly technology, applied in the direction of manufacturing tools, unloading devices, lubricating compositions, etc., can solve the problems of general demoulding effect, environmental health hazards, and high cost, achieve good demoulding effect, reduce production costs, smooth surface effect

Active Publication Date: 2013-11-27
ZHEJIANG NORMAL UNIVERSITY
View PDF1 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the release agents used in the concrete industry are mineral oil-based release agents, but this type of release agent will pollute the steel and concrete surfaces, the cost is high, and the release effect is average.
In addition, this type of release agent is a non-renewable resource and releases volatile organic compounds into the air, which will cause certain harm to the environment and human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Weigh the raw materials according to the following weight proportions: 300Kg of waste oil, 70Kg of Tween 60, 20Kg of alkylphenol polyoxyethylene ether, 10Kg of spherical natural graphite with a particle size of less than 10μm, and 600Kg of water; (2) Weigh Add 300Kg of half the weight of water in the formula system to the stainless steel reactor, stir at 100 rpm, heat up to 60°C, and then add 70Kg of Tween 60 and 20Kg of alkylphenol polyoxyethylene ether in sequence , stirred for 30 minutes to form a mixed solution M-1; (3) In another reactor, add 300Kg of waste oil and under the condition of 100-300 rpm, add 10Kg of sliding components with a particle size of less than 10μm spherical For natural graphite, stir for 30 minutes, then heat up to 90-100°C, react for 1 hour, and form a mixed solution M-2; (4) Pour the mixed solution M-2 into the mixed solution M-1, and keep the stirring speed at 100-300 Turn / min, after mixing and stirring for 10 minutes, heat to 90-10...

Embodiment 2

[0023] (1) Weigh the raw materials according to the following weight ratio: 200Kg of waste oil, 100Kg of Tween 20, 50Kg of alkylphenol polyoxyethylene ether, 20Kg of spherical natural graphite with a particle size of less than 10μm, and 630Kg of water; (2) Weigh Add 315Kg of half the weight of water in the formula system into the stainless steel reactor, stir at 100 rpm, heat up to 60°C, and then add 100Kg of Tween 20 and 50Kg of alkylphenol polyoxyethylene ether in sequence, Stir for 30 minutes to form a mixed solution M-1; (3) In another reaction kettle, add 200Kg of waste oil and under the condition of 100-300 rpm, add 20Kg of spherical natural stone with a sliding component particle size less than 10μm Ink, stir for 30 minutes, then raise the temperature to 90-100°C, react for 1 hour, and form a mixed solution M-2; (4) Pour the mixed solution M-2 into the mixed solution M-1, and keep the stirring speed at 100-300 rpm / min, after mixing and stirring for 10min, heat to 9...

Embodiment 3

[0025] (1) Weigh the raw materials according to the following weight ratio: 400Kg of waste oil, 50Kg of Tween 80, 10Kg of fatty alcohol polyoxyethylene ether, 10Kg of spherical natural graphite with a particle size of less than 10μm, and 539Kg of water; Add 269.5Kg of half the weight of water in the formula system into a stainless steel reactor, stir at 100 rpm, heat up to 60°C, then add 50Kg of Tween 80 and 10Kg of fatty alcohol polyoxyethylene ether in sequence, Stir for 30 minutes to form a mixed solution M-1; (3) In another reaction kettle, add 400Kg of waste oil and under the condition of 100-300 rpm, add 1Kg of spherical natural stone with a sliding component particle size less than 10μm Ink, stir for 30 minutes, then raise the temperature to 90-100°C, react for 1 hour, and form a mixed solution M-2; (4) Pour the mixed solution M-2 into the mixed solution M-1, and keep the stirring speed at 100-300 rpm / min, after mixing and stirring for 10min, heat to 90-100°C, then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waste oil-based environment-friendly mold separating agent and a preparation method thereof. The technical scheme provided by the invention adopts key points that the waste oil-based environment-friendly mold separating agent is mainly prepared from the following raw materials by weight percent: 20 to 40 percent of waste oil, 5 to 10 percent of emulsifier, 1 to 5 percent of wetting agent, 0.1 to 2 percent of sliding component and the balance of water. The invention further discloses the preparation method of the waste oil-based environment-friendly mold separating agent and the using method thereof. The waste oil-based environment-friendly mold separating agent provided by the invention is high in temperature resistance, has a good demolding effect, has strong rust preventing performance and is high in water scouring resisting performance, and the preparation method takes waste oil as raw material, gets rid of the dependence of a traditional mold separating agent on mineral oil, not only achieves waste comprehensive utilization, but also lowers the cost, and reduces environment pollutions and harm to human bodies.

Description

technical field [0001] The invention relates to a concrete release agent and a preparation method thereof, in particular to a waste oil-based environment-friendly release agent and a preparation method thereof. The prepared release agent has good release effect, high quality cement products, low cost and Environmental protection and other advantages. Background technique [0002] In recent years, due to the improvement of living standards and the rapid development of the catering industry, waste oil produced by various fast food restaurants and restaurants has flowed into rivers, lakes and seas through sewage pipes, and even a large part of waste oil has been illegally repurchased as edible oil and continued to flow back to the dining table , causing serious food safety hazards and environmental pollution. [0003] Waste oil generally refers to all kinds of low-quality oils that exist in daily life, such as recycled cooking oil, repeatedly used frying oil, etc. If people c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M173/00B28B13/06
Inventor 王爱军冯九菊吕晶晶李姗姗陈得军
Owner ZHEJIANG NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com