Method and product of artificially cultivating "salt flower"
An artificial cultivation, salt flower technology, applied in the field of handicrafts, can solve the problems of not forming "salt flower, not many good-looking, difficult to dig, etc., and achieve the effect of simple method, easy-to-obtain raw materials, and better viewing.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] Example 1 Production of "Salt Flower" Dapeng Wing Spreading Handicraft
[0023] Coat the surface of the "Dapeng Spreading Wings" gypsum model with a surface agent (a mixture of Arowana brand varnish and salt); weigh 28Kg of edible salt, dissolve it with 70Kg of fresh water, stir for 30 minutes and then clarify, remove the supernatant liquid and place it in an evaporation basin; Put the model in salt water so that the model is completely submerged in salt water.
[0024] Use a stirring device to stir slowly to allow the brine to evaporate naturally, and salt crystals begin to grow on the surface of the model; the thickness of the salt crystals grows to about 1 cm (for 17 days), stop stirring, and take out the wet "salt flowers"; the remaining saturated brine can be used continuously.
[0025] The wet "salt flower" is dried naturally, and a handicraft of "dapeng spreading wings" and "salt flower" is completed.
Embodiment 2
[0026] Example 2 Production of "Salt Flower" Ding Crafts
[0027] Use ordinary PVC ceiling as the material, cut it according to the size of the tripod, use quick glue to smoothly bond the tripod model, and coat the surface with a surface agent (a mixture of Arowana brand varnish and salt); use the method in Example 1 to prepare saturated brine ( This example was not prepared separately, and directly used the remaining saturated brine in Example 1); put the model in the brine, so that the model was completely submerged in the brine.
[0028] Use a stirring device to stir slowly to allow the brine to evaporate naturally, and salt crystals begin to grow on the surface of the model; the thickness of the salt crystals grows to about 1cm (lasting 14 days), stop stirring, take out the wet "salt flowers"; the remaining saturated brine can be used continuously.
[0029] Dry the wet "salt flower" naturally, and complete the production of a "salt flower" tripod craft;
Embodiment 3
[0030] Example 3 Production of "Salt Flower" Bodhisattva Handicraft
[0031] Coat the surface of the "Bodhisattva" plaster model with a surface agent (ordinary paint such as a mixture of Arowana brand varnish and salt); take 100Kg of intercrystalline brine (saturated salt water) from Chaerhan Salt Lake in Qinghai; put the model in the brine to make The model was completely submerged in salt water.
[0032] Use a stirring device to stir slowly to allow the brine to evaporate naturally, and salt crystals begin to grow on the surface of the model; the thickness of the salt crystals grows to about 1cm (lasting 11 days), stop stirring, and take out the wet "salt flowers"; the remaining brine is before the carnallite salt is saturated Can continue to be used.
[0033] Dry the wet "salt flower" naturally, and make a "salt flower" Bodhisattva handicraft;