Medical stone ceramic product and preparation method thereof

A technology for ceramic products and medical stone, which is applied to the preparation of medical stone ceramic products and the field of medical stone ceramic products, can solve the problems of no medical stone ceramic products, unscientific ingredients, and immature preparation technology, etc. Small plasticity, improved performance, and poor water-encapsulation effects

Inactive Publication Date: 2014-02-05
马仁水
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there has not been a medical stone ceramic product with relatively mature technology on the market so far.
The main reason is tha

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example 1

[0017] Medical stone ceramic teapot, which is composed of the following raw materials in weight percentage: medical stone powder 45%, its silicon dioxide content is greater than 60.00%, alumina content is greater than 14.00%, sodium oxide content is greater than 4.00%; potassium feldspar powder 18%, Its potassium oxide content is greater than 10.00%, and its iron oxide content is less than 0.30%; albite powder is 13%, its sodium oxide content is greater than 8.00%, and its iron oxide content is less than 0.30%; quartz powder is 9%, its silicon dioxide content is greater than 98.00%, Iron oxide content is less than 0.10%; Laiyang soil 15%, its silica content is less than 75.00%, alumina content is greater than 13.00%, and iron oxide content is less than 1.00%.

[0018] The preparation method comprises the following steps:

[0019] (1), take raw material by weight percentage, pulverize through 100 mesh sieves, mix uniformly and set aside;

[0020] (2), accor...

Example Embodiment

[0023] Example 2

[0024] Medical stone ceramic mouth cup, which is composed of the following raw materials in weight percentage: medical stone powder 41%, its silicon dioxide content is greater than 60.00%, alumina content is greater than 14.00%, sodium oxide content is greater than 4.00%; potassium feldspar powder 20% , its potassium oxide content is greater than 10.00%, and its iron oxide content is less than 0.30%; albite powder is 12%, its sodium oxide content is greater than 8.00%, and its iron oxide content is less than 0.30%; quartz powder is 10%, its silicon dioxide content is greater than 98.00% , iron oxide content is less than 0.10%; Laiyang soil 17%, its silica content is less than 75.00%, alumina content is greater than 13.00%, and iron oxide content is less than 1.00%.

[0025] The preparation method comprises the following steps:

[0026] (1), take raw material by weight percentage, pulverize through 130 mesh sieves, mix uniformly and set aside;

[0027] (2),...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a medical stone ceramic product prepared from the following raw materials in percentage by weight: 41-45% of medical stone powder, 16-20% of potassium feldspar powder, 10-14% of soda feldspar powder, 8-10% of quartz powder and 12-17% of Laiyang soil. The preparation method comprises the following steps: weighing raw materials in percentage by weight, grinding and filtering the raw materials by a sieve with the granularity of 100-150 meshes, and uniformly mixing for later use; grinding the powder in a ball miller for 1-2 hours according to the condition that the ratio of the material to balls to water is 1:2:0.5, filtering mud through a sieve with the granularity of 32-35 meshes, and pugging to obtain a finished mud product; performing slip-casting, demoulding, correcting and grinding, and drying for 12-24 hours; sintering a dried mud blank in a furnace in steps and cooling to obtain the required product. The medical stone ceramic product is reasonable in material proportion and scientific in sintering method, so that the medical stone has improved performance, good air permeability and high plasticity, and the yield is up to 97%; the medical stone is free from toxicity and radiation, and has no change in original property and precipitated trace elements; the medical stone can be prepared into various beautiful new material tea sets, cups and other finished products.

Description

Technical field [0001] The invention relates to the technical field of ceramic manufacturing, in particular to a medical stone ceramic product. [0002] The invention also relates to a preparation method of the medical stone ceramic product. Background technique [0003] A large number of facts show that medical stone contains a variety of indispensable trace elements for human body, animals and plants, and has good adsorption, fast dissolution, and is easily absorbed by plants and animals. At the same time, medical stone is also a precious Chinese medicinal material, which can eliminate harmful lead, mercury, tin, arsenic and other toxic substances and harmful bacteria in the human body. Therefore, medical stone plays a special role in health care, disease prevention, cancer prevention, anti-aging, and water purification. In order to make better use of the above characteristics of medical stone, in recent years people have processed medical stone into various cups and ric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/13
Inventor 马仁水
Owner 马仁水
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap