Plastic-wood composite floor and preparation method thereof

A wood-plastic composite material and flooring technology, which is applied in the field of materials, can solve the problems of plastic-wood composite materials such as restrictions on the use of wood-plastic composite materials and the inability to seal the installation site, and achieve excellent sealing effects, reduce installation costs, and ensure environmental protection.

Active Publication Date: 2014-02-05
南京聚锋新材料有限公司 +1
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the rigidity of the material itself, the wood-plastic composite material is often installed with links at the installation interface. This kind of installation cannot achieve the sealing of the installation place, which limits the use of wood-plastic composite materials in many aspects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plastic-wood composite floor and preparation method thereof
  • Plastic-wood composite floor and preparation method thereof
  • Plastic-wood composite floor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The wood-plastic composite material floor of this embodiment is composed of the following materials by weight percentage:

[0023]

[0024] In this example, the following methods are used to prepare wood-plastic composite flooring:

[0025] Step 1, mixing materials, PVC plastic powder, wood fiber, mineral filling, foaming agent, foaming regulator, lubricant, titanium dioxide and pigment according to the stated ratio, first add PVC powder, stabilizer and stir until the friction heat When the temperature of the material rises to 40-60°C, add foaming regulator, mineral filler, and plant fiber. When the friction heat makes the material rise to 60-70°C, add lubricant and pigment (selected according to needs), and wait until the friction heat rises to 60-70°C. When the material rises to 100°C, add foaming agent, mix to 120-130°C, discharge the material into the cold mixer, and release the material when stirring and cooling to 20-70°C, to obtain plastic-wood mixture;

[00...

Embodiment 2

[0032] The difference between this embodiment and Embodiment 1 is that it consists of the following materials by weight percentage:

[0033]

Embodiment 3

[0035] The difference between this embodiment and Embodiment 1 is that it consists of the following materials by weight percentage:

[0036]

[0037]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a composite floor and a preparation method thereof and belongs to the technical field of materials. Plant fibers are distributed in a polyolefin plastic-wood section in a continuous extension manner, so that the plant fibers which are continuously extended can quickly transfer the local stress to the whole section when the plastic-wood section is stressed during an application process. Thus, the strength and the impact resistance of the plastic-wood section are substantially improved. In addition, coconut shell powder or palm fibers are adopted in the plant fibers, so that the environmental friendliness is good. The anti-oxidation degree of the surface of the plastic-wood composite is improved through co-extrusion of a surface material; and the scratch resistance and the abrasion resistance of the plastic-wood composite are improved at the same time. A PVC (Poly Vinyl Chloride) soft adhesive tape is coextruded at a buckling part of the plastic-wood composite, so that the excellent sealing effect is achieved.

Description

technical field [0001] The invention relates to a composite material floor and a preparation method, belonging to the technical field of materials. Background technique [0002] Wood-plastic composite material is an emerging environmentally friendly, low-carbon composite material. It mainly uses recycled plastics and agricultural and forestry wastes as raw materials, which are processed into planks, guardrails, or indoor and outdoor decorations. However, due to the low mechanical properties of wood-plastic composite materials, they cannot be widely used in the construction field, especially for force-bearing parts or structural parts. At the same time, due to the limitations of the structural design and installation method of the current plastic wood flooring, the sealing of the installation interface cannot be guaranteed. The application of plastic-wood composite materials at home and abroad is currently in the development stage. How to enhance the performance of plastic-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08K13/02C08K3/26C08K3/34C08J9/04E04F15/10B29C47/92B29C47/06B29C48/92B29C48/875
CPCB29C48/875B29C48/92B29C2948/92704B29C2948/92895
Inventor 刘曙阳艾顺杨英昌丁建生朱方政
Owner 南京聚锋新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap