Preparation method of rodlike N-doped niobium pentoxide photocatalyst

A technology of niobium pentoxide and photocatalyst, which is applied in physical/chemical process catalysts, chemical instruments and methods, chemical/physical processes, etc., can solve the problem of low utilization rate of sunlight, and achieve low catalytic activity and excellent long-term performance. The effect of diameter ratio and large specific surface area

Inactive Publication Date: 2014-03-19
NANTONG AGRI COLLEGE
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is mainly to solve the problem of low utilization rate of sunlight and the serious recombination of photogenerated electron-hole pairs in the body of niobium pentoxide photocatalyst, improve the catalytic activity of photocatalyst, and expand the application range of photocatalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0012] A preparation method of nitrogen-doped rod-shaped niobium pentoxide photocatalyst, comprising the following steps:

[0013] 1) Preparation of rod-shaped niobium pentoxide, using Nb 2 o 5 NR means

[0014] Dissolve 0.2g of metal niobium powder in 80mL of deionized water, stir at 1000rpm for 30min, transfer the above solution to a 100mL autoclave, age at 200°C for 7 days, filter to obtain the product, and then use deionized The mixture of water and ethanol was washed 2-3 times, filtered, and dried at 60°C for 1 hour to obtain the product Nb 2 o 5 NR;

[0015] 2) Preparation of nitrogen-doped rod-shaped niobium pentoxide, using N-Nb 2 o 5 NR means

[0016] The above steps are prepared to obtain Nb 2 o 5 Mix NR and urea at a mass ratio of 1:1, grind them evenly with a mortar, and calcinate the obtained sample at 400°C for 2 hours, wash the obtained sample with dilute nitric acid and deionized water, filter it with suction, and then dry it in an oven at 70°C Dry fo...

specific Embodiment 2

[0017] A preparation method of nitrogen-doped rod-shaped niobium pentoxide photocatalyst, comprising the following steps:

[0018] 1) Preparation of rod-shaped niobium pentoxide, using Nb 2 o 5 NR means

[0019] Dissolve 0.4g of metal niobium powder in 80mL of deionized water, stir at 1000rpm for 30min, transfer the above solution to a 100mL autoclave, age at 200°C for 7 days, filter to obtain the product, and then use deionized The mixture of water and ethanol was washed 2-3 times, filtered, and dried at 60°C for 1 hour to obtain the product Nb 2 o 5 NR, ready for use;

[0020] 2) Preparation of nitrogen-doped rod-shaped niobium pentoxide, using N-Nb 2 o 5 NR means

[0021] The above steps are prepared to obtain Nb 2 o 5 Mix NR and urea at a mass ratio of 2:1, grind them evenly with a mortar, calcinate the obtained sample at 400°C for 2 hours, wash the obtained sample with dilute nitric acid and deionized water, filter it with suction, and then dry it in an oven at 7...

specific Embodiment 3

[0022] A preparation method of nitrogen-doped rod-shaped niobium pentoxide photocatalyst, comprising the following steps:

[0023] 1) Preparation of rod-shaped niobium pentoxide, using Nb 2 o 5 NR means

[0024] Dissolve 0.6g of metal niobium powder in 80mL of deionized water, stir at 1000rpm for 30min, transfer the above solution to a 100mL autoclave, age at 200°C for 7 days, filter to obtain the product, and then use deionized The mixture of water and ethanol was washed 2-3 times, filtered, and dried at 60°C for 1 hour to obtain the product Nb 2 o 5 NR, ready for use;

[0025] 2) Preparation of nitrogen-doped rod-shaped niobium pentoxide, using N-Nb 2 o 5 NR means

[0026] The above steps are prepared to obtain Nb 2 o 5 Mix NR and urea at a mass ratio of 3:1, grind them evenly with a mortar, calcinate the obtained sample at 400°C for 2 hours, wash the obtained sample with dilute nitric acid and deionized water, filter it with suction, and then dry it in an oven at 7...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a rodlike N-doped niobium pentoxide photocatalyst. The preparation method comprises the steps of preparing rodlike niobium pentoxide; and preparing the rodlike N-doped niobium pentoxide photocatalyst. According to the preparation method, metal niobium powder and urea are used as raw materials to prepare the rodlike N-doped niobium pentoxide photocatalyst. The preparation method can remarkably improve the photocatalytic activity of the niobium pentoxide, effectively enhance the sunlight utilization rate of the niobium pentoxide and further widen the application range of theniobium pentoxide photocatalyst. The rodlike N-doped niobium pentoxide photocatalyst can rapidly and effectively mineralize organic pollutants in water into CO2 and H2O, has high repeating utilization rate, has good application prospect and economic benefit and achieves an environment-friendly effect.

Description

technical field [0001] The invention relates to the field of semiconductor photocatalyst preparation, in particular to a method for preparing a nitrogen-doped rod-shaped niobium pentoxide photocatalyst. Background technique [0002] With the development of the economy, the energy crisis is becoming more and more serious: the consumption of petrochemical energy, the pollution of air and water resources, etc. have become the bottleneck of sustainable development. Imminent task. Photocatalysis has attracted much attention due to its clean, efficient, and safe properties. [0003] Since Fujishima discovered semiconductor TiO in 1972 2 Since water can be split by photoelectric catalysis, the study of semiconductor photocatalytic materials has become a hot spot for scientists. Recently, niobium pentoxide (Nb 2 o 5 ) as a typical n-type semiconductor photocatalyst has received great attention. However, due to the small specific surface area of ​​niobium pentoxide nanoparticle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/24B01J35/10C02F1/30
Inventor 丁敏娟李亚蒋云霞李蓉金洁蓉闫生荣
Owner NANTONG AGRI COLLEGE
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com