A composite color film process on the surface of a stainless steel coil or flat plate

A surface compounding, stainless steel technology, applied in lamination devices, lamination auxiliary operations, lamination and other directions, can solve the problems of long drying time of adhesives, low production efficiency, uneven lamination, etc., and achieve lamination The transmission type is uniform and firm, with high production efficiency and rich colors.

Active Publication Date: 2015-12-23
陈登
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing process of composite color film on the surface of stainless steel plate is to directly coat the adhesive on the stainless steel plate, then put the color film on the stainless steel plate coated with adhesive to make the color film and the stainless steel plate bond together, and then press it manually The color film is used to bond the color film to the stainless steel plate. It takes a long time for the adhesive to dry at room temperature during the above process, which has the disadvantage of low production efficiency; manually press the color film to make the color film and the stainless steel plate closely adhere The fit will appear uneven and not firm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] A stainless steel coil or plate surface composite color film process, comprising the following steps:

[0028] 1) Surface frosting or wire drawing treatment of stainless steel coils or flat plates, surface grinding or wire drawing treatment can enhance the appearance of the product and make the product more beautiful;

[0029] 2) Install bundles of stainless steel coils on the uncoiler at one end of the composite production line and fix them or place a flat plate on the unwinding platform;

[0030] 3) Unpack the fixed coiled plate or flat plate, transport it to the cleaning machine through the conveying platform, and clean the surface of the coiled plate or flat plate with impurities;

[0031] 4) After the cleaned coil or flat plate is pressed by rubber rollers, it is transported to the oven for electric lamp baking, and the surface moisture of the coil or flat plate is dried;

[0032] 5) Transport the dried coil or plate to the cooling place, and use a fan to cool dow...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
heightaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a surface color film compounding process for a stainless steel coil plate or flat plate. The process comprises: carrying out a surface sand milling or wire drawing treatment on the surface of a stainless steel coil plate or flat plate; arranging the stainless steel coil plate or placing the flat plate on a composite production line; unwinding the coil plate or unpacking the flat plate, and cleaning surface impurities; conveying to an oven to dry; conveying to a cooling position to cool; conveying to a roller coat position, and carrying out rolling glue coating on the surface of the coil plate or flat plate by using a glue roller coated with a coating glue on the surface; conveying to the oven to dry the glue until 90% of the glue is dried; conveying to a film adhering position, and carrying out pressing adhering on the color film and the stainless steel coil plate or flat plate by using a steel roller and a glue roller; conveying to a water cooling position to carry out spraying type water cooling; conveying to an air cooling position to cool the coil plate or flat plate to achieve a room temperature; conveying to a packaging position to carry out surface film adhering package; and finally winding the coil plate by using a winding device or carrying out flat plate packing in a wood box. Compared with the process in the prior art, the process of the present invention has advantages of high production efficiency, uniform and firm adhering transmission of the color film and the coil plate or flat plate, and prevention of losing of the decoration effect due to oxidation rusting on the metal surface with the color film.

Description

technical field [0001] The invention relates to a stainless steel lamination process, in particular to a stainless steel coil or plate surface composite color film process. Background technique [0002] The existing process of composite color film on the surface of stainless steel plate is to directly coat the adhesive on the stainless steel plate, then put the color film on the stainless steel plate coated with adhesive to make the color film and the stainless steel plate stick together, and then press it manually The color film is used to bond the color film to the stainless steel plate. It takes a long time for the adhesive to dry at room temperature during the above process, which has the disadvantage of low production efficiency; the color film is pressed manually to make the color film and the stainless steel plate tightly adhered. The joint will appear uneven and not firm. Contents of the invention [0003] The present invention aims to solve the above-mentioned de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B37/12B32B37/06B32B38/16
Inventor 陈登
Owner 陈登
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com