A kind of chitosan hydrogel for antibacterial dressing and preparation method thereof

A technology of chitosan and sugar water, which is applied in medical science, absorbent pads, bandages, etc., can solve the problems of doubtful antibacterial safety and poor antibacterial durability, and achieve the effect of enhanced antibacterial effect, strong antibacterial ability and high strength

Inactive Publication Date: 2016-01-20
SHANGHAI INST OF TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention provides a kind of antibacterial dressing with good drug resistance, good antibacterial property, antibacterial lasting, water absorption rate etc. Chitosan hydrogel with high and good mechanical properties for antibacterial dressings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of chitosan hydrogel for antibacterial dressing and preparation method thereof
  • A kind of chitosan hydrogel for antibacterial dressing and preparation method thereof
  • A kind of chitosan hydrogel for antibacterial dressing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A chitosan hydrogel for antibacterial dressing, calculated in parts by weight, its composition and content are as follows:

[0047] 2 parts of chitosan

[0048] 5 parts of water-soluble monomer

[0049] Antibacterial agent polyhexamethyleneguanidine hydrochloride 1 part

[0050] 0.015 parts of crosslinking agent

[0051] Condensing agent 1 part

[0052] 1 part of activator

[0053] 0.1 part of initiator

[0054] 109 parts of dimethyl sulfoxide;

[0055] The chitosan has a degree of deacetylation of 80.0 and a viscosity of 50-800 mPa.s;

[0056] The water-soluble monomer is methacrylic acid;

[0057] The crosslinking agent is N,N-methylenebisacrylamide;

[0058] The condensation agent is diisopropylcarbodiimide (DIC);

[0059] The activator is 1-hydroxybenzotriazole (HOBt);

[0060] The initiator is potassium persulfate.

[0061] The above-mentioned preparation method of chitosan hydrogel for antibacterial dressing specifically includes the following steps:

[0062] (1) Dissolve 2g of chitos...

Embodiment 2

[0071] A chitosan hydrogel for antibacterial dressing, calculated in parts by weight, its composition and content are as follows:

[0072] Chitosan 3 parts

[0073] 6 parts of water-soluble monomer

[0074] Antibacterial agent polyhexamethyleneguanidine hydrochloride 1.5 parts

[0075] 0.02 parts of crosslinking agent

[0076] Condensing agent 1 part

[0077] 1 part of activator

[0078] 0.15 parts of initiator

[0079] 113.5 parts of dimethyl sulfoxide;

[0080] The chitosan has a degree of deacetylation of 85.0 and a viscosity of 50-800 mPa.s;

[0081] The water-soluble monomer is acrylic acid;

[0082] The crosslinking agent is glutaraldehyde;

[0083] The condensing agent is 1-(3-dimethylaminopropyl)-3-ethylcarbodiimide (EDCI);

[0084] The activator is 1-hydroxybenzotriazole (HOBt);

[0085] The initiator is ammonium persulfate.

[0086] The above-mentioned preparation method of chitosan hydrogel for antibacterial dressing specifically includes the following steps:

[0087] (1) Dissolve 3 g o...

Embodiment 3

[0093] A chitosan hydrogel for antibacterial dressing, calculated in parts by weight, its composition and content are as follows:

[0094] 4 parts of chitosan

[0095] 10 parts of water-soluble monomer

[0096] Antibacterial agent polyhexamethyleneguanidine hydrochloride 3 parts

[0097] 0.045 parts of crosslinking agent

[0098] Condensing agent 1.5 parts

[0099] 1.5 parts of activator

[0100] 0.25 parts of initiator

[0101] 127 parts of dimethyl sulfoxide;

[0102] The chitosan has a degree of deacetylation of 90.0 and a viscosity of 50-800 mPa.s;

[0103] The water-soluble monomer is methacrylic acid;

[0104] The crosslinking agent is N,N-methylenebisacrylamide;

[0105] The condensation agent is diisopropylcarbodiimide (DIC);

[0106] The activator is 4-N,N-lutidine (DMAP);

[0107] The initiator is potassium persulfate.

[0108] The above-mentioned preparation method of chitosan hydrogel for antibacterial dressing specifically includes the following steps:

[0109] (1) Dissolve 4g of chit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a chitosan hydrogel for an antibacterial dressing and a preparation method thereof. The chitosan hydrogel for the antibacterial dressing comprises, by weight, 2 to 6 parts of chitosan, 5 to 20 parts of a water-soluble monomer, 1 to 5 parts of an antibacterial agent polyhexamethyleneguanidine hydrochloride, 0.015 to 0.1 part of a cross-linking agent, 1 to 5 parts of a condensing agent, 1 to 5 parts of an activator, 0.1 to 0.5 part of an initiator and 109 to 145 parts of dimethyl sulfoxide. The preparation method comprises the following steps: introducing a carboxyl group on chitosan in the manner of free radical polymerization; subjecting the carboxyl group introduced on chitosan and the antibacterial agent polyhexamethyleneguanidine hydrochloride to an amidation reaction by using the condensing agent and the activator; and uniformly mixing chitosan for the antibacterial dressing with the cross-linking agent and pouring an obtained mixture into a die for a reaction so as to obtain the hydrogel with good drug resistance, good antibacterial property, a lasting antibacterial effect, high water absorption and good mechanical properties.

Description

Technical field [0001] The invention relates to an antibacterial dressing, in particular to a chitosan hydrogel for an antibacterial dressing suitable for the treatment of burns, scalds and open mechanical wounds and a preparation method thereof. Background technique [0002] Medical dressing is a key material for clinical treatment of wounds. The main function of traditional dressing is to cover the wound and prevent wound infection. In the 21st century, modern medical dressings have gradually replaced traditional dressings. Compared with traditional dressings, modern dressings, especially hydrogel dressings, have good mechanical strength and can resist mechanical factors (such as injury, collision, etc.) damage, pollution and chemical stimulation of the wound (due to the application of the dressing to the wound at the joint Later, when the patient exercises, it is mainly affected by tension. If the mechanical properties (such as tensile strength) are low, the hydrogel dry fil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L15/28A61L15/42A61L15/44C08G81/02C08F251/00C08F220/06C08J3/24
Inventor 吴蓁宋羽顾顺超王玮媛盛奥奇张英强
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap