Tissue engineering bracket applicable to human body organ construction and preparation method thereof

A technology for tissue engineering scaffolds and organs, applied in prosthetics, medical science, etc., can solve the problems of material pore size, poor smoothness, poor biological and histocompatibility, and mismatched cell growth conditions, etc., to achieve superior application value , Uniform pore size and low raw material cost

Inactive Publication Date: 2014-07-30
CHONGQING UNIV OF TECH
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Natural materials have poor formability and poor mechanical properties after molding, and their biodegradation rate is too fast, which does not match the growth conditions of cells. Some materials may also have immunogenicity, etc. Synthetic materials have good mechanical properties, but there are also It is difficult to degrade, does not match the growth rate of cells, the material has poor pore size and smoothness, and poor biological and tissue compatibility. Some natural-synthetic materials have overcome some problems, but problems in molding and degradation also plague the organization. engineering researchers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tissue engineering bracket applicable to human body organ construction and preparation method thereof
  • Tissue engineering bracket applicable to human body organ construction and preparation method thereof
  • Tissue engineering bracket applicable to human body organ construction and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A preparation method for a tissue engineering scaffold suitable for human organ construction, specifically comprising the following steps:

[0038] (1) Dissolve sericin powder in deionized water to prepare a sericin solution with a concentration of 5.0% (W / V);

[0039] Chitosan is dissolved in the dilute hydrochloric acid solution that concentration is 0.1mol / L, is made into the chitosan solution that concentration is 2% (W / V);

[0040] Dissolve sodium glycerophosphate in deionized water to prepare a sodium glycerophosphate solution with a concentration of 50% (W / V);

[0041] (2) Below 20°C, weigh 0.68ml of the sericin solution obtained in step (1) and 5ml of the chitosan solution, stir and mix evenly, then add 1ml of the sodium glycerophosphate solution obtained in step (1) dropwise, and stir 30min;

[0042] Put the mixed solution into the mold, control the temperature of the mold at 37°C, and make the mixed solution gel into shape; then place the molded material at -2...

Embodiment 2

[0044] A preparation method for a tissue engineering scaffold suitable for human organ construction, specifically comprising the following steps:

[0045] (1) Dissolve sericin powder in deionized water to prepare a sericin solution with a concentration of 5.0% (W / V);

[0046] Chitosan is dissolved in the dilute hydrochloric acid solution that concentration is 0.1mol / L, is made into the chitosan solution that concentration is 2% (W / V);

[0047] Dissolve sodium glycerophosphate in deionized water to prepare a sodium glycerophosphate solution with a concentration of 50% (W / V);

[0048] (2) Below 20°C, weigh 0.68ml of the sericin solution obtained in step (1) and 6ml of the chitosan solution, stir and mix evenly, then add 1ml of the sodium glycerophosphate solution obtained in step (1) dropwise, and stir 30min;

[0049] Put the mixed solution into the mold, control the temperature of the mold at 37°C, and make the mixed solution gel into shape; then place the molded material at ...

Embodiment 3

[0051] A preparation method for a tissue engineering scaffold suitable for human organ construction, specifically comprising the following steps:

[0052] (1) Dissolve sericin powder in deionized water to prepare a sericin solution with a concentration of 5.0% (W / V);

[0053] Chitosan is dissolved in the dilute hydrochloric acid solution that concentration is 0.1mol / L, is made into the chitosan solution that concentration is 2% (W / V);

[0054] Dissolve sodium glycerophosphate in deionized water to prepare a sodium glycerophosphate solution with a concentration of 50% (W / V);

[0055] (2) Below 20°C, weigh 0.68ml of the sericin solution obtained in step (1) and 7ml of the chitosan solution, stir and mix evenly, then add 1ml of the sodium glycerophosphate solution obtained in step (1) dropwise, and stir 30min;

[0056] Put the mixed solution into the mold, control the temperature of the mold at 37°C, and gel the mixed solution into shape; then place the molded material at -20°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a tissue engineering bracket applicable to human body organ construction, and the tissue engineering bracket has the bore diameter of 5 mu m-200 mu m, good bore connectivity and proper degradability, and can be applicable to growth of cells in the bracket. The invention further discloses a preparation method of the tissue engineering bracket applicable to human body organ construction. The preparation method comprises the following steps: firstly preparing sericin liquor, chitosan liquor and sodium glycerophosphate liquor into mixed liquor; then, converting the mixed liquor into a gel state; finally, obtaining the tissue engineering bracket by virtue of a process comprising freezing and drying, placing and softening, and high-pressure steam treating. By regulating the ratio of the sericin liquor, chitosan liquor and sodium glycerophosphate liquor or changing process conditions, the bore diameter size and degradation performance of the obtained tissue engineering bracket can be obtained in a controlled manner, so that the tissue engineering bracket satisfies the requirements of the tissue engineering bracket applicable to human body organ construction. The preparation method has the advantages of being gentle in reaction condition, simple in process and low in material cost, and is suitable for industrial scale-up production.

Description

technical field [0001] The invention belongs to the technical field of biological materials and tissue engineering, and in particular relates to a tissue engineering scaffold suitable for constructing human organs and a preparation method thereof. Background technique [0002] Tissue engineering is one of the research hotspots in the medical field today, and its birth brings hope for the regeneration of various functional tissues or organs. Surgical treatment methods reported in the literature often repair tissue defects by sacrificing normal tissue at the expense of surgical trauma. Not only the effect is not good, but also there are many complications. With the improvement of living standards, people pay more and more attention to their own health and safety, so more and more attention is paid to the research on tissue engineering scaffolds. All over the world, developing an ideal biological scaffold is an urgent problem in the field of tissue engineering and has become a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/24A61L27/58A61L27/56
Inventor 陈忠敏刘琼庞亚妮王富平李江峰
Owner CHONGQING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap