Metal-based composite material for vapor plating of masking plates, vapor-plated masking plate and preparation method thereof
A composite material and mask technology, which is applied in the field of metal matrix composite materials, evaporation mask and its preparation, can solve problems such as cost reduction and mask drape, and achieve cost reduction, density reduction, and overall performance improvement Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
specific Embodiment 1
[0046] This specific embodiment provides a metal matrix composite material for a mask plate and a preparation method thereof.
[0047] The metal-matrix composite material used in the mask plate provided in this example uses iron-nickel alloy as the matrix, and the non-metallic particles dispersed in the matrix as the reinforcing phase. The schematic diagram of the obtained metal-matrix composite material is shown in Figure 1 . figure 1 Among them, 1 is the iron-nickel alloy, and 2 is the non-metallic particles dispersed in the iron-nickel alloy. Preferably, in the iron-nickel alloy, the nickel content is 30%-36wt%; more preferably, the nickel content is 35.4wt%. The nickel content is 30%-36wt%, more preferably the iron-nickel alloy matrix with a nickel content of 35.4wt% has good plasticity and impact toughness, and can improve the strength, elastic modulus, hardness, etc. of the material under the action of the reinforcing phase performance.
[0048] The metal matrix composi...
specific Embodiment 2
[0056] This specific embodiment provides another metal matrix composite material used for an evaporation mask and a method for preparing the evaporation mask.
[0057] The content of each component in the metal matrix composite material prepared by this method is the same as that of the metal matrix composite material in the first specific embodiment, but the performance of the material prepared by the method provided by this specific embodiment is improved, and the cost is reduced .
[0058] image 3 The process flow chart of the preparation method provided for this specific embodiment. In step S201, iron powder, nickel powder, and non-metallic particles (selected from any one of SiC particles, Al2O3 particles, AlN particles, image 3 Take SiC as an example) according to the required ratio, so that in the final metal matrix composite material, the content of nickel in the iron-nickel alloy is 30%-36wt%, more preferably the nickel content is 35.4wt% , the volume ratio of no...
specific Embodiment 3
[0065] This specific embodiment provides yet another metal matrix composite material used for an evaporation mask and a method for preparing the evaporation mask.
[0066] The content of each component in the metal matrix composite material prepared by this method is the same as that of the metal matrix composite material in the first specific embodiment, but the performance of the material prepared by the method provided by this specific embodiment is improved, and the cost is reduced .
[0067] Figure 4 The process flow chart of the preparation method provided for this specific embodiment. In step S301, first iron-nickel pre-alloy powder, non-metallic particles (selected from SiC particles, Al 2 o 3 Any of particles, AlN particles, Figure 4 Take SiC as an example) according to the required ratio, so that in the final metal matrix composite material, the content of nickel in the iron-nickel alloy is 30%-36wt%, more preferably the nickel content is 35.4wt% , the volume ...