Oily high-temperature resistant coating material, application thereof and titanium ingot production method

A high-temperature, oil-resistant technology, applied in coating and other directions, can solve the problem of unsatisfactory protection of titanium ingots, and achieve the effects of increasing production cost and production time, simple preparation process and reducing production cost.

Active Publication Date: 2014-11-19
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the defects that the existing high-temperature protective coatings are not ideal for the protection of titanium ingots, and provide a new oil-based high-temperature resistant coating and its application and production method for titanium ingots

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oily high-temperature resistant coating material, application thereof and titanium ingot production method
  • Oily high-temperature resistant coating material, application thereof and titanium ingot production method
  • Oily high-temperature resistant coating material, application thereof and titanium ingot production method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] There is no special requirement for the preparation method of the oil-based high-temperature resistant coating of the present invention, and various methods commonly used in this field can be used, as long as the components are mixed uniformly. However, the inventors of the present invention have found in their research that the following method is used to prepare the oil-based high-temperature resistant coating, which can make the components mix more uniformly. The specific method is: first mix the oily film-forming agent with the diluent to dilute, then slowly add the oxidation protection agent under stirring, then add the curing agent, stir evenly, then add the dispersant, and stir until a uniform and stable phase is obtained.

[0030] In the second aspect, the present invention provides the application of the above-mentioned oily high temperature resistant coating in the production of titanium ingots.

[0031] In a third aspect, the present invention provides a meth...

Embodiment 1

[0046] This embodiment is used to illustrate the production method of the oily high temperature resistant coating and titanium ingot of the present invention.

[0047] (1) At normal temperature and pressure (25°C, 0.1MPa), weigh 100g of oily epoxy resin (solid content 50% by weight) and place it in a container;

[0048] (2) Add 5g of polypropylene glycol diglycidyl ether (purchased from Changzhou Mingtai Chemical Technology Co., Ltd., model: 207), and stir evenly;

[0049] (3) Weigh 800g Al powder, 50g Fe powder and 50g Sn powder, and slowly add them into the container under stirring;

[0050] (4) Weigh 1g SiO 2 , add to the container, and stir evenly;

[0051] (5) Weigh 0.5g of polyvinyl alcohol (purchased from Qingdao Anmao International Trade Co., Ltd., Z-200) into a container, stir until the liquid is in a uniform and stable phase, and obtain oily high temperature resistant coating A1.

[0052] The solid content of the oily high temperature resistant coating A1 was dete...

Embodiment 2

[0055] This embodiment is used to illustrate the production method of the oily high temperature resistant coating and titanium ingot of the present invention.

[0056] (1) At normal temperature and pressure (25°C, 0.1MPa), weigh 54g of oily epoxy resin (solid content 40% by weight) and place it in a container;

[0057] (2) Add 2.6g propylene oxide butyl ether (purchased from Changzhou Mingtai Chemical Technology Co., Ltd., model: 501), and stir evenly;

[0058] (3) Weigh 770g Al powder, 40g Fe powder and 40g Sn powder, slowly add in the container under stirring;

[0059] (4) Weigh 1.7g SiO2 2 , add to the container, and stir evenly;

[0060] (5) Weigh 0.68g of polyvinylpyrrolidone (purchased from Guangzhou Batai Chemical Co., Ltd., PVPK90) into a container, and stir until the liquid becomes a uniform and stable phase to obtain oily high temperature resistant coating A2.

[0061] The measured solid content of the oily high temperature resistant coating A2 is 90%, and the pH ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an oily high-temperature resistant coating material. The oily high-temperature resistant coating material is obtained after a raw material mixture is uniformly mixed, wherein the raw material mixture contains an oxidation protecting agent and an oily film forming agent; the oxidation protecting agent contains Al powder, Fe powder and Sn powder which are in the weight ratio of 1: (0.01-0.1): (0.01-0.1). The invention further discloses an application of the oily high-temperature resistant coating material in titanium ingot production and a titanium ingot production method. The oily high-temperature resistant coating material disclosed by the invention has the advantages that the condition that the surface of a titanium ingot is not subjected to oxidation cracking under the condition that the titanium ingot undergoes constant temperature for 8 hours at the high temperature of 1,000 DEG C can be guaranteed, and the forming possibility of an oxygen dissolved layer can be greatly reduced; the oily high-temperature resistant coating material has an environment-friendly effect; the preparation process is simple; a variety of coating manners can be adopted. The titanium ingot production method disclosed by the invention has good economic and social benefits and has relatively broad popularization and application prospects in titanium plate and titanium tube production industries.

Description

technical field [0001] The invention relates to the field of metal high-temperature-resistant coatings, in particular to an oil-based high-temperature-resistant coating, the application of the oily high-temperature-resistant coating in the production of titanium ingots, and a production method for titanium ingots. Background technique [0002] Titanium ingots generally undergo annealing treatment during the production process. Annealing is generally carried out at a high temperature of about 900°C. At high temperatures, oxygen will enter the surface of the titanium ingot to form a hard dissolved oxygen layer. The titanium ingot is heated at 900°C for 4 hours. Deep cracks with a depth of about 20mm will appear on the above surface. In order to ensure the subsequent rolling of titanium tubes and the surface quality of hot-rolled titanium plates, it is necessary to cut and grind the titanium ingots during the rolling process to remove cracks and dissolved oxygen layers, which r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/12C21D1/68
Inventor 许哲峰王莹彭琳肖聪李军
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com