A kind of inorganic ecological wall mud dry powder and production method thereof

An ecological wall and dry powder technology, applied in sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of human injury, inability to apply interior decoration for a long time, pollute the air, etc., to purify the indoor environment, enhance Breathability, the effect of protecting the natural environment

Active Publication Date: 2016-04-13
南通华仑节能建材有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the limited storage conditions of the above materials, anti-corrosion materials are added to the glue and latex paint in the production process to varying degrees, and these anti-corrosion materials release harmful substances such as formaldehyde into the air to varying degrees after construction Gases, while polluting the air, they also bring harm to the human body
[0004] At present, with the improvement of people's awareness of environmental protection requirements, the above-mentioned large white powder, glue, latex paint and wallpaper and other decorative materials are far from meeting people's needs, and cannot be used for interior decoration for a long time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of inorganic ecological wall mud dry powder and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] An inorganic ecological wall mud dry powder, which comprises the following components by weight percentage: shell 40%, diatomite 15%, desulfurized gypsum 8%, sodium silicate 5.3%, calcium carbonate 20%, wood short fiber 1 %, cellulose 0.2%, iron oxide pigment 0.5%, quartz sand 10%. During production, the shells are firstly rinsed with water, dried, and then dried and crushed (the crushing mesh is 200). After crushing, the particles are classified with a grading sieve, and the classified powder is packaged for later use; then Put the crushed shell raw materials into the mixer, and then put diatomaceous earth, sodium silicate, desulfurized gypsum, calcium carbonate, wood short fiber, cellulose, iron oxide pigment and quartz sand into the mixer in the above ratio one by one. After the input is completed, stir for 15 minutes to make it fully stirred evenly, and measure and fill the evenly stirred dry powder of ecological wall mud to obtain the finished product.

Embodiment 2

[0021] An inorganic ecological wall mud dry powder, which comprises the following components by weight percentage: 30% shells, 20% diatomaceous earth, 8% desulfurized gypsum, 10% sodium silicate, 20% calcium carbonate, 1 wood short fiber %, cellulose 0.5%, iron oxide pigment 0.5%, quartz sand 10%. During production, the shells are firstly rinsed with water, dried, and then dried and crushed (the crushing mesh is 400). After crushing, the particles are classified with a grading sieve, and the classified powder is packaged for later use; then Put the crushed shell raw materials into the mixer, and then put diatomaceous earth, sodium silicate, desulfurized gypsum, calcium carbonate, wood short fiber, cellulose, iron oxide pigment and quartz sand into the mixer in the above ratio one by one. After the input is completed, stir for 15 minutes to make it fully stirred evenly, and measure and fill the evenly stirred dry powder of ecological wall mud to obtain the finished product.

Embodiment 3

[0023] An inorganic ecological wall mud dry powder, which includes the following components by weight percentage: 30% shellfish, 15% diatomaceous earth, 10% desulfurized gypsum, 8% sodium silicate, 20% calcium carbonate, 5% short wood fiber %, 1% cellulose, 1% iron oxide pigment, 10% quartz sand. During production, the shells are firstly rinsed with water, dried, and then dried and crushed (the crushing mesh is 300). After crushing, the particles are classified with a grading sieve, and the classified powder is packed for use; then Put the crushed shell raw materials into the mixer, and then put diatomaceous earth, sodium silicate, desulfurized gypsum, calcium carbonate, wood short fiber, cellulose, iron oxide pigment and quartz sand into the mixer in the above ratio one by one. After the input is completed, stir for 20 minutes to make it fully stirred evenly, and measure and fill the evenly stirred ecological wall mud dry powder to obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses inorganic ecological wall mud dry powder, comprising the following components in percentage by mass: 30%-40% of shell, 15%-25% of kieselguhr, 8%-15% of flue gas desulfurization gypsum, 5%-10% of portil, 20%-30% of calcium carbonate, 1%-5% of wood short fiber, 0.2%-1% of cellulose, 0.5%-3% of iron oxide pigment, and 10%-20% of silica sand. The production method comprises the following steps: firstly, rinsing the shell with water, airing, baking and crushing, and carrying out granule grading treatment by using a grading screen; packaging the graded powder for later use; feeding the crushed shell raw material to a stirrer, and then gradually adding the kieselguhr, the portil, the flue gas desulfurization gypsum, the calcium carbonate, the wood short fiber, the cellulose, the iron oxide pigment and the silica sand to the stirrer to which the shell raw material is added according to the ratio; fully stirring evenly for 15-30 minutes after feeding is ended, metering and bulking the evenly stirred ecological wall mud dry powder, so as to obtain the product.

Description

technical field [0001] The invention relates to a novel building decoration material, in particular to an inorganic ecological wall mud dry powder and a production method thereof. Background technique [0002] The interior wall decoration is the most important part in the decoration of every family house, and every family house expects to meet the requirements of aesthetics and environmental protection through environmentally friendly interior wall materials when decorating. [0003] For a long time, interior wall decoration has basically been using large white powder, 801 glue, latex paint, wallpaper and other materials for construction. Due to the limited storage conditions of the above materials, anti-corrosion materials are added to the glue and latex paint in the production process to varying degrees, and these anti-corrosion materials release harmful substances such as formaldehyde into the air to varying degrees after construction Gases, while polluting the air, also...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/26C04B28/14C04B18/04
CPCY02W30/91
Inventor 张玲管图军
Owner 南通华仑节能建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap