A kind of mildew-proof and antibacterial adhesive tape and preparation method thereof

A technology of anti-mildew and anti-bacterial tape, applied in adhesives, anti-fouling/underwater coatings, paints containing biocides, etc., can solve the problems of unreachable, labor-intensive and disinfection materials, good disinfection effect, etc., and achieve the convenience of use Effect

Active Publication Date: 2016-08-24
广东新时代新材料科技有限公司 +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current general disinfection treatment method is to repeatedly wipe with a disinfectant cleaner, but because the source of infection will repeatedly contact the wiped part, it consumes labor and disinfection materials, and at the same time does not achieve a good disinfection effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of mildew-proof and antibacterial adhesive tape and preparation method thereof
  • A kind of mildew-proof and antibacterial adhesive tape and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] It should be noted that the sources and trade names of the materials used, as well as those whose components must be listed, are all indicated when they appear for the first time, and the same materials used thereafter have the same contents as those indicated for the first time unless otherwise specified.

[0024] The preparation of embodiment 1 mildew-proof antibacterial adhesive tape, its steps are as follows successively:

[0025] 1) Preparation of antibacterial film layer. In Example 1, the imidazole thiophene mixture was used as the antibacterial agent, and PEVA was used as the base material of the film for mixing and preparation. The imidazole-thiophene mixture is formed by physically mixing imidazole and thiophene at a weight ratio of 1:1. Firstly, the imidazole thiophene mixture is uniformly mixed with PEVA, and the resulting product is passed through an extruder to produce a PEVA film with anti-mold and antibacterial effects, that is, an antibacterial film la...

Embodiment 2

[0029] The preparation of embodiment 2 mildew-proof and antibacterial adhesive tapes, its steps are as follows successively:

[0030] a) Preparation of antibacterial coating. In Example 2, imidazole thiophene mixture and fumed silica were used as antibacterial agent, ethyl acetate was used as co-solvent, and PET was used as plastic substrate. Disperse the mixture of imidazolethiophene and gas-phase silica in ethyl acetate, and disperse and mix evenly under a high-speed mixer. Be prepared into antibacterial coating, its proportioning ratio is as shown in the following table 1:

[0031] Material

Weight ratio / part

imidazothiophene mixture

1

fumed silica

1

ethyl acetate

100

[0032] Table 1

[0033] b) corona treatment of PET to obtain a PET film with a surface dyne value ≥ 38 dyne;

[0034] c) Preparation of antibacterial film layer. Using coating technology, the anti-mold and anti-bacterial coating is coated on one side of the...

Embodiment 3

[0037] The preparation of embodiment 3 mildew-proof and antibacterial adhesive tapes, its steps are as follows successively:

[0038] a) Preparation of antibacterial coating. In Example 3, imidazole thiophene mixture and fumed silica were used as antibacterial agent, ethyl acetate was used as co-solvent, and PET was used as plastic substrate. Disperse the mixture of imidazolethiophene and gas-phase silica in ethyl acetate, and disperse and mix evenly under a high-speed mixer. Be prepared into antibacterial coating, its proportioning ratio is as shown in the following table 2:

[0039] Material

Weight ratio / part

imidazothiophene mixture

20

fumed silica

20

ethyl acetate

80

[0040] Table 2

[0041] b) corona treatment of PET to obtain a PET film with a surface dyne value ≥ 38 dyne;

[0042] c) Preparation of antibacterial film layer. Using coating technology, the anti-mold and anti-bacterial coating is coated on one side of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
melting pointaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a mildewproof antibacterial adhesive tape and a preparation method thereof. The mildewproof antibacterial adhesive tape comprises an antibacterial film layer and an adhesive layer, wherein the adhesive layer is attached to one surface of the antibacterial film layer; the antibacterial film layer comprises an antibacterial agent and a plastic base material; the antibacterial agent comprises an imidazole and thiofuran mixture; the antibacterial film layer is prepared by mixing the antibacterial agent and the plastic base material or prepared by coating the antibacterial agent on one surface of a plastic film made from the plastic base material; the adhesive layer is attached to the other surface of the plastic film. The preparation method sequentially comprises the following steps of (1) mixing the antibacterial agent and the plastic base material, and preparing the antibacterial film layer from the mixture through an extruder; (2) coating one surface of the antibacterial film layer with glue, and drying to form the adhesive layer. The mildewproof antibacterial adhesive tape disclosed by the invention can achieve the mildewproof antibacterial effect by tearing a segment of a product and adhering on a touched article.

Description

technical field [0001] The invention relates to an anti-mildew and anti-bacterial adhesive tape and a preparation method thereof. Background technique [0002] With the continuous improvement of human science and technology, people in both developing countries and developed countries have higher and higher requirements for hygiene, especially in some special environments, people are paying more and more attention. The following examples The technical background of this invention will be explained. [0003] The medical industry, the door handrail of the operating room in the hospital and other places where the staff may touch. Before the doctor prepares for the operation, the doctor and the surgical team must wear special surgical gloves and other equipment, and disinfect them before entering the operating room to operate on the patient. The work done by the doctors and the surgical team is to prevent bacteria and other microorganisms from being brought into the operating r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/02C09D5/14
Inventor 穆晓敏李杰马亮廖其云
Owner 广东新时代新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap