Ultra-high molecular weight anion biological polysaccharide grafted copolymer and preparation method thereof

A technology of ultra-high molecular weight graft copolymer, which is applied in the field of ultra-high molecular weight anionic biopolysaccharide graft copolymer and its preparation, can solve the problems that the molecular weight and structural properties are difficult to meet the actual needs, and the application is difficult to promote. Socioeconomic benefits, broad market prospects, and the effect of a wide range of pH values

Inactive Publication Date: 2015-02-04
威海汉邦生物环保科技股份有限公司
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] From the above, it can be seen that most of the sugar materials used in many studies are derived from the artificial extraction of natural materials. Although they are biodegr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-high molecular weight anion biological polysaccharide grafted copolymer and preparation method thereof
  • Ultra-high molecular weight anion biological polysaccharide grafted copolymer and preparation method thereof
  • Ultra-high molecular weight anion biological polysaccharide grafted copolymer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Preparation of graft copolymers of biological polysaccharides, acrylamide and sodium 2-acrylamido-2-methylpropanesulfonate

[0031] Preparation of 2-acrylamido-2-methylpropanesulfonic acid sodium aqueous solution: put the 2-acrylamido-2-methylpropanesulfonic acid aqueous solution with a mass fraction of 50% in an ice-water bath, and slowly add the concentration 30% sodium hydroxide aqueous solution, the pH of the final solution is 7-8.

[0032] In a 500ml three-neck flask, add 200g of a non-ionic biological polysaccharide solution with a mass concentration of 15%, start stirring, and then add 10g of acrylamide and a 42.3% mass concentration of 2-acrylamido-2-methylpropanesulfonate sodium solution 141.8g, after passing nitrogen to remove oxygen, heat up to 40°C, then add 1ml of 0.1mol / L cerium ammonium nitrate solution and 1.8g sodium sulfate, continue stirring for 20min, stop nitrogen flow, stop stirring, seal, keep warm for 3h, and finally Cool, take it out, add exces...

Embodiment 2

[0038] Preparation of graft copolymers of biopolysaccharides, acrylamide and acrylic acid

[0039] Prepare an acrylic acid monomer solution with a neutralization degree of 80%: Weigh 100g of acrylic acid and 44.4g of sodium hydroxide, place the acrylic acid in an ice-water bath, dissolve the sodium hydroxide in about 150ml of water, and slowly drop into In acrylic acid, a monomer solution with a neutralization degree of 80% and a monomer content of 34.2% can be obtained by stirring while dropping.

[0040]Add 100g of biological polysaccharide solution with a mass concentration of 15% into a 500ml three-neck flask, start stirring, add 15g of acrylamide and 131.58g of the above-mentioned acrylic acid solution in sequence, after purging nitrogen to remove oxygen, heat up to 30°C, and then add 0.1mol / L of 1ml of ammonium cerium nitrate solution and 2.8g of urea, continue to stir for 20min, stop nitrogen, stop stirring, seal, keep warm for 4h, finally cool, take out, add excess eth...

Embodiment 3

[0046] Preparation of graft copolymers of biological polysaccharides, acrylamide and 2-acrylamido-2-methylpropanesulfonic acid

[0047] Add 200g of biological polysaccharide solution with a mass concentration of 15% in a 500ml three-neck flask, start stirring, add 15g of acrylamide and 60g of 2-acrylamido-2-methylpropanesulfonic acid, and after purging nitrogen to remove oxygen, heat up to 40°C , and then add 2ml of 0.1mol / L cerium ammonium nitrate solution and 2g of sodium sulfate, continue to stir for 20min, stop nitrogen, stop stirring, seal, keep warm for 2h, finally cool, take out, add excess ethanol and stir, then suction filter, The filter residue was taken, washed three times with acetone, then dried in a vacuum oven to constant weight, and ground to obtain the final product.

[0048] The product can be used as paper-making auxiliary agent and water treatment agent in the range of sewage pH=2-12.

[0049] The structural formula of the product is:

[0050] Intrinsic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to an ultra-high molecular weight anion biological polysaccharide grafted copolymer and a preparation method thereof. The anion biological polysaccharide grafted copolymer of which the molecular weight is 3-50 million is ultimately prepared by taking non-ionic biological polysaccharide which is already produced in large scale and has the ultra-high molecular weight of 2-30 million as a raw material, alkenyl amide, alkenyl carboxylic acid (carboxylate) and alkenyl sulfonic acid (sulfonate) as reaction monomers and one of ammonium persulfate/sodium hydrogen sulfite, azo diisobutyl amidine or ceric ammonium nitrate as an initiator in a solution free radial polymerization manner. The ultra-high molecular weight anion biological polysaccharide grafted copolymer is simple in production process, easy to control, high in molecular weight, biodegradable, excellent in property and wide in application range, and has very high application values and wide market prospect.

Description

technical field [0001] The invention belongs to the technical field of ultra-high molecular weight biological polysaccharide modification technology, in particular to an ultra-high molecular weight anionic biological polysaccharide graft copolymer and a preparation method thereof. Background technique [0002] Biological polysaccharides are a class of polymer compounds formed by the polymerization of more than 10 monosaccharide molecules, and are widely produced in animals, plants, microorganisms and algae lichens. Anionic biological polysaccharides can be prepared by anionic modification of biological polysaccharides. Due to its electrostatic attraction to positively charged substances and its excellent properties such as high molecular weight, thickening, lubricity, and film-forming properties, its The research and application have been widely concerned by many scholars. At present, the anionically modified biological polysaccharide materials can be widely used in sewage t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F251/00C08F220/56C08F220/58C08F220/06
Inventor 庄茅胡阳
Owner 威海汉邦生物环保科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap