A universal interface adhesive

A technology of interface binder and mass ratio, which is applied in the direction of adhesive, adhesive type, polymer adhesive additive, etc., can solve the problems of self-adhesive coil bonding performance, etc., to achieve convenient construction and reduce construction pressure , the effect of long operating time

Active Publication Date: 2016-09-28
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in actual engineering, the self-adhesive modified bitumen waterproofing membrane system often encounters many quality problems, and the existence of these quality problems involves all aspects, including the material itself, the primer material, the base layer, etc., and the relationship between them. The effect of different primer coating materials has a significant impact on the bonding performance of self-adhesive coils

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A universal interface adhesive
  • A universal interface adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Accurately weigh 30g of epoxy-based co-solvent, 5g of diethanolamine, 2g of iron oxide red, 3g of precipitated barium sulfate and 2g of ethylene glycol glycidyl ether, add the above materials together into a stirring tank at 60°C, and stir for 1 hour until the system viscosity Almost uniform, then add 20g of component B to it, mix evenly and cool the resulting mixture to room temperature to obtain a universal interface adhesive.

[0022] When in use, apply the universal interface adhesive on the surface of the treated concrete, and the dosage is 0.3kg / m 2 .

[0023] At room temperature, the viscosity of the universal interface adhesive prepared in Example 1 is 200Cp, and the viscosity is still in a good flow state after an average of 180 minutes.

Embodiment 2

[0025] Accurately weigh 60g of epoxy-based co-solvent, 25g of N-methylolethanolamine, 10g of red iron oxide, 15g of mica powder and 20g of polypropylene glycol diglycidyl ether, and add the above materials together into a stirring tank at 60°C, and stir for 1 hour Until the viscosity of the system is almost uniform, then add 100g of component B to it, mix evenly and cool the resulting mixture to room temperature to obtain a universal interface adhesive.

[0026] When in use, apply the universal interface adhesive on the surface of the treated concrete, and the dosage is 0.3kg / m 2 .

[0027] At room temperature, the viscosity of the universal interface adhesive prepared in Example 2 is 220Cp, and the viscosity is still in a good flow state after an average of 180 minutes.

Embodiment 3

[0029] Accurately weigh 50g of epoxy-based co-solvent, 5g of N-propenyl ethanolamine, 5g of precipitated barium sulfate, 10g of hollow microspheres and 20g of ethylene glycol glycidyl ether, and add the above materials together into a stirring tank at 60°C, and stir for 1h Until the viscosity of the system is almost uniform, then add 16g of component B to it, mix evenly and cool the resulting mixture to room temperature to obtain a universal interface adhesive.

[0030] When in use, apply the universal interface adhesive to the concrete surface after surface treatment, and the dosage is 0.3kg / m 2 .

[0031] At room temperature, the viscosity of the universal interface adhesive prepared in Example 3 is 215Cp, and the viscosity is still in a good flow state after an average of 180 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a universal interfacial binding agent which comprises a component A and a component B, wherein the component A comprises the following raw materials in parts by weight: 30-50 parts of a cosolvent, 5-25 parts of en epoxy resin curing agent, 2-20 parts of a special auxiliary and 5-25 parts of filler; the component B is water soluble epoxy resin, and the weight ratio of the components A and B is (0.5-5):1. The universal interfacial binding agent provided by the invention has relatively low viscosity under room temperature, the necessary flowing property of the universal interfacial binding agent being used is guaranteed, the operable time is relatively long, and the construction pressure is greatly alleviated. The universal interfacial binding agent provided by the invention has the characteristics of being hard in coating, free of oil separation, short in drying time, green, environment-friendly and pollution-free and convenient to construct. Experiments verify that the viscosity of the universal interfacial binding agent provided by the invention at 20 DEG C is about 200cp and a good application performance for construction within 180 minutes after being mixed can be maintained.

Description

technical field [0001] The invention relates to a general interface adhesive. Background technique [0002] The universal interface adhesive is a new type of material that not only closes the pores and tiny defects on the surface of the concrete base, but also effectively enhances the bonding force between the concrete base material and the concrete surface coating such as polyurethane and polyurea. At present, it has been widely used in many fields such as high-speed railway bridge deck and civil building waterproof layer. The quality of the closed primer material directly affects the service life of the building. Therefore, this kind of primer material needs to be curable at room temperature, with high penetration, good sealing effect on the pores of the base surface and good compatibility with the cladding material, effectively strengthening the bond between the cladding material and the concrete base material. Performance characteristics such as adhesion, as well as go...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J163/00C09J11/04C09J11/08C09J11/06
Inventor 杨迎生林海侠
Owner BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com