Corrosion-resistant physical and chemical board for laboratory

A laboratory-use, corrosion-resistant technology, applied in the field of physical and chemical boards, can solve the problems of physical and chemical boards' corrosion resistance, heat resistance and service life that cannot meet market demand, high curing temperature, and long curing time, etc., to achieve light weight and stickiness High junction strength, excellent heat resistance and chemical corrosion resistance

Active Publication Date: 2017-11-17
ANHUI XIMA OUMEIJIA DECORATIVE MATERIAL IND
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the gradual increase of laboratory equipment at present, the physical and chemical board used in the laboratory is used more and more widely as an indispensable material. Phenolic resin has high bonding strength, water resistance, heat resistance, wear resistance and good chemical stability. It is widely used in the physical and chemical board industry due to its advantages, but it has disadvantages such as high cost, high curing temperature and long curing time. The current physical and chemical boards are increasingly unable to meet market demand in terms of corrosion resistance, heat resistance and service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A corrosion-resistant physical and chemical board for laboratories proposed by the present invention includes 90 parts of physical and chemical substrates, 10 parts of physical and chemical films, and 0.5 parts of adhesive in parts by weight. The physical and chemical substrates and the physical and chemical films are bonded by adhesives. The agent is modified phenolic resin;

[0018] The raw materials of physical and chemical substrates include by weight: 50 parts of kraft paper, 50 parts of modified phenolic resin, 8 parts of curing agent, and 1 part of buffering agent;

[0019] The raw materials of the physical and chemical film include by weight: 30 parts of vinyl ester resin, 14 parts of dimethyldiethoxysilane, 15 parts of phenolic resin, 1 part of silicon carbide fiber, 40 parts of ceramic powder, and 2 parts of titanium dioxide;

[0020] In the preparation process of the modified phenolic resin, 90 parts of wheatgrass lignin, 20 parts of formaldehyde and 4 parts ...

Embodiment 2

[0022] A kind of corrosion-resistant physical and chemical plate for laboratory proposed by the present invention comprises 100 parts of physical and chemical substrate, 5 parts of physical and chemical film and 1 part of adhesive by weight, and the physical and chemical substrate and the physical and chemical film are bonded by adhesive;

[0023] The raw materials of physical and chemical substrates include by weight: 40 parts of kraft paper, 70 parts of modified phenolic resin, 5 parts of curing agent, and 3 parts of buffering agent;

[0024] The raw materials of the physical and chemical film include by weight: 25 parts of vinyl ester resin, 17 parts of dimethyldiethoxysilane, 10 parts of phenolic resin, 4 parts of silicon carbide fiber, 35 parts of ceramic powder, and 5 parts of titanium dioxide;

[0025] In the preparation process of the modified phenolic resin, 70 parts of wheatgrass lignin, 30 parts of formaldehyde and 2 parts of sodium hydroxide were sent into the react...

Embodiment 3

[0027] A kind of corrosion-resistant physical and chemical plate for laboratory proposed by the present invention comprises 97 parts of physical and chemical substrate, 6.5 parts of physical and chemical film and 0.75 part of adhesive by weight, and the physical and chemical substrate and the physical and chemical film are bonded by adhesive;

[0028] The raw materials of physical and chemical substrates include by weight: 47 parts of kraft paper, 64 parts of modified phenolic resin, 6.4 parts of curing agent, and 2.2 parts of buffering agent;

[0029] The raw materials of the physical and chemical film include by weight: 27 parts of vinyl ester resin, 15.5 parts of dimethyldiethoxysilane, 37 parts of ceramic powder, 13 parts of phenolic resin, 2.5 parts of silicon carbide fiber, and 3.6 parts of titanium dioxide;

[0030] In the preparation process of the modified phenolic resin, 82 parts of wheatgrass lignin, 25 parts of formaldehyde and 3 parts of sodium hydroxide were sent ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a corrosion-resistant physicochemical plate for laboratories, which comprises the following components in parts by weight: 90-100 parts of physicochemical substrate, 5-10 parts of physicochemical membrane and 0.5-1 part of adhesive. The physicochemical substrate and physicochemical membrane are bonded through an adhesive. The physicochemical substrate is prepared from the following raw materials in parts by weight: 40-50 parts of kraft, 50-70 parts of modified phenol formaldehyde resin, 5-8 parts of curing agent and 1-3 parts of buffering agent. The physicochemical membrane is prepared from the following raw materials in parts by weight: 25-30 parts of vinyl ester resin, 14-17 parts of dimethyldiethoxysilane, 10-15 parts of phenol formaldehyde resin, 1-4 parts of silicon carbide fiber, 35-40 parts of ceramic powder and 2-5 parts of titanium white. The corrosion-resistant physicochemical plate for laboratories has the advantages of low cost, excellent corrosion resistance, excellent heat resistance and long service life.

Description

technical field [0001] The invention relates to the technical field of physical and chemical plates, in particular to a corrosion-resistant physical and chemical plate for laboratories. Background technique [0002] With the gradual increase of laboratory equipment at present, the physical and chemical board used in the laboratory is used more and more widely as an indispensable material. Phenolic resin has high bonding strength, water resistance, heat resistance, wear resistance and good chemical stability. Due to its advantages, it is widely used in the physical and chemical board industry, but it has disadvantages such as high cost, high curing temperature and long curing time. The current physical and chemical boards are increasingly unable to meet market demand in terms of corrosion resistance, heat resistance and service life. Contents of the invention [0003] The invention provides a corrosion-resistant physical and chemical plate for laboratory use, which has long...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B29/06B32B13/08B32B13/02B32B7/12C09J161/14C08G8/28C04B26/02
CPCB32B7/12B32B27/10B32B27/18B32B27/22B32B27/30B32B29/06B32B2260/046C04B26/02C08G8/28C09J161/14
Inventor 徐学武
Owner ANHUI XIMA OUMEIJIA DECORATIVE MATERIAL IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products