Anti-static two-sided gold-stamped, printed and embossed PVC (polyvinyl chloride) sheet and preparation method thereof

A polyvinyl chloride, antistatic technology, applied in the field of antistatic double-sided bronzing embossed polyvinyl chloride sheet and its preparation, can solve the problems of poor antistatic effect and poor overall performance of the sheet, and achieve improved pressure Texture effect, strong three-dimensional effect, and the effect of improving low temperature resistance

Inactive Publication Date: 2015-04-29
DONGGUAN IUIU HOUSEHOLD PROD
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the antistatic effect of the sheet is not good, and the overall performance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] An antistatic double-sided bronzing embossed polyvinyl chloride sheet, comprising the following raw materials in parts by weight:

[0060] PVC resin 80 parts

[0061] 32 parts plasticizer

[0062] Lubricant 6 parts

[0063] 1 heat stabilizer

[0064] Slippery agent 0.03 parts

[0065] Pigment powder 0.03 parts

[0066] Calcium powder 0.1 part;

[0067] Wherein, the calcium powder is a mixture of nano-calcium carbonate and heavy calcium carbonate at a weight ratio of 1:1.5, the particle size of the nano-calcium carbonate is 120nm; the particle size of the heavy calcium carbonate is 1 μm.

[0068] The PVC resin has a degree of polymerization of 1000, a particle size of 0.1mm, and a density of 1.35g / cm 3 PVC resin.

[0069] The plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 15:1.

[0070] The lubricant is a mixture of microcrystalline paraffin and monoglyceryl stearate in a weight ratio of 1.2:1.

[0071] The heat sta...

Embodiment 2

[0086] An antistatic double-sided bronzing embossed polyvinyl chloride sheet, comprising the following raw materials in parts by weight:

[0087] PVC resin 90 parts

[0088] 37 parts plasticizer

[0089] Lubricant 7 parts

[0090] 2 parts heat stabilizer

[0091] Slippery agent 0.04 parts

[0092] Pigment powder 0.04 parts

[0093] Calcium powder 0.2 parts;

[0094] Wherein, the calcium powder is a mixture of nano-calcium carbonate and heavy calcium carbonate at a weight ratio of 1:1.7, the particle size of the nano-calcium carbonate is 130nm; the particle size of the heavy calcium carbonate is 3 μm.

[0095] The PVC resin has a degree of polymerization of 1050, a particle size of 0.12 mm, and a density of 1.37 g / cm 3 PVC resin.

[0096] The plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 16:1.

[0097] The lubricant is a mixture of microcrystalline paraffin and monoglyceride stearate in a weight ratio of 1.3:1.

[0098] T...

Embodiment 3

[0113] An antistatic double-sided bronzing embossed polyvinyl chloride sheet, comprising the following raw materials in parts by weight:

[0114] PVC resin 100 parts

[0115] Plasticizer 42 parts

[0116] Lubricant 8 parts

[0117] 3 parts heat stabilizer

[0118] Slippery agent 0.05 parts

[0119] Pigment powder 0.05 parts

[0120] Calcium powder 0.3 parts;

[0121] Wherein, the calcium powder is a mixture of nano-calcium carbonate and heavy calcium carbonate at a weight ratio of 1:2, the particle size of the nano-calcium carbonate is 135nm; the particle size of the heavy calcium carbonate is 5 μm.

[0122] The PVC resin has a degree of polymerization of 1100, a particle size of 0.15 mm, and a density of 1.4 g / cm 3 PVC resin.

[0123] The plasticizer is a mixture of dioctyl phthalate and epoxidized soybean oil in a weight ratio of 17:1.

[0124] The lubricant is a mixture of microcrystalline paraffin and monoglyceride stearate in a weight ratio of 1.5:1.

[0125] The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of sheets, in particular to an anti-static two-sided gold-stamped, printed and embossed PVC (polyvinyl chloride) sheet and a preparation method thereof. The sheet comprises raw materials in parts by weight as follows: 80-120 parts of PVC resin, 32-52 parts of a plasticizer, 6-10 parts of a lubricant, 1-4 parts of a heat stabilizer, 0.03-0.07 parts of a slipping agent, 0.03-0.07 parts of pigment powder and 0.1-0.5 parts of calcium powder, wherein the calcium powder is a mixture of nano calcium carbonate and heavy calcium carbonate in the weight ratio of 1:(1.5-2.5), the particle size of the nano calcium carbonate is in a range of 120-150 nm, and the particle size of the heavy calcium carbonate is in a range of 1-10 [mu]m. The raw materials are adopted, and the weight ratio of the raw materials is strictly controlled, so that the sheet is good in anti-static effect, heat-resistant, cold-resistant, acid-resistant, alkali-resistant, heavy-load-resistant, anti-aging, smooth in surface, free of cracks and bubbles, uniform in color, strong in stereoscopic impression, soft in texture, comfortable, healthy and environment-friendly.

Description

technical field [0001] The invention relates to the technical field of sheets, in particular to an antistatic double-sided bronzing embossed polyvinyl chloride sheet and a preparation method thereof. Background technique [0002] Soft polyvinyl chloride sheet is transparent, beautiful and soft, and has been widely used in the field of daily products, such as tablecloths, table mats and placemats. This type of product is generally attached with a transparent film on the other side of the printed pattern. When it is covered on furniture, especially glass furniture, it can not only display the printed pattern on the transparent film, but also observe the shape of the furniture through the transparent film. Play a very good decorative effect. However, the antistatic effect of the sheet is not good, and the overall performance is poor. Contents of the invention [0003] In order to overcome the shortcomings and deficiencies in the prior art, the object of the present inventio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/06C08K13/02C08K3/26C08K5/12C08K5/1515C08K5/103C08K5/098C08K5/20B29C43/58
CPCB29C69/00C08K2201/003C08K2201/011C08K2201/014C08L27/06C08L2201/04C08L2201/08C08L2205/02C08L2205/035C08L91/00C08L91/06C08K13/02C08K2003/265C08K5/12C08K5/103C08K5/098C08K5/20
Inventor 刘承发
Owner DONGGUAN IUIU HOUSEHOLD PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap