A kind of preparation method of modified molasses waste liquid and cement grinding aid

A technology for modifying molasses waste liquid, which is applied in the field of cement grinding aids added to cement, can solve the problems of functional group concentration, inability to fully play the role of grinding aid and hydration aid, and reduce the fineness and specific surface area , strength improvement, and the effect of increasing the setting time

Active Publication Date: 2016-08-31
华润水泥技术研发(广西)有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the use of molasses waste liquid as a raw material for cement grinding aids still has disadvantages, because the molecular structure of functional groups in molasses waste liquid is too large, and the functional groups are too concentrated to fully exert its grinding and hydration-aiding effects. It is necessary to improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of modified molasses waste liquid and cement grinding aid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1, the preparation method of the modified molasses waste liquid of the present embodiment, it comprises the following steps.

[0023] Step A, take an appropriate amount of molasses waste liquid, adjust the pH value of the molasses waste liquid with sodium hydroxide solution until the pH of the molasses waste liquid is 9, and filter under normal pressure to obtain molasses alcohol filtrate A.

[0024] In step B, the acetic acid solution is added to the molasses alcohol filtrate A prepared in step A, and the pH of the molasses alcohol filtrate A is adjusted to 2 to obtain molasses waste liquid B.

[0025] In step C, the molasses waste liquid B prepared in step B is mixed with 35% hydrogen peroxide in a volume ratio of 1:0.1 and then put into an autoclave. The pressure in the autoclave is 20KPa and the temperature is 90°C. The molasses waste liquid B is fully reacted with 35% industrial hydrogen peroxide to obtain the molasses waste liquid C.

[0026] Step D, a...

Embodiment 2

[0028] Embodiment 2, the preparation method of the modified molasses waste liquid of the present embodiment, it comprises the following steps.

[0029] Step A, take an appropriate amount of molasses waste liquid, adjust the pH value of the molasses waste liquid with sodium hydroxide solution until the pH of the molasses waste liquid is 10, and filter under normal pressure to obtain molasses alcohol filtrate A.

[0030] In step B, the acetic acid solution is added to the molasses alcohol filtrate A prepared in step A, and the pH of the molasses alcohol filtrate A is adjusted to 2 to obtain molasses waste liquid B.

[0031] In step C, the molasses waste liquid B prepared in step B is mixed with 35% hydrogen peroxide in a volume ratio of 1:0.1 and then put into an autoclave. The pressure in the autoclave is 30KPa and the temperature is 100°C. The molasses waste liquid B is fully reacted with 35% industrial hydrogen peroxide to obtain the molasses waste liquid C.

[0032] Step D,...

Embodiment 3

[0034] Embodiment 3, the preparation method of the modified molasses waste liquid of the present embodiment, it comprises the following steps.

[0035] Step A, take an appropriate amount of molasses waste liquid, adjust the pH value of the molasses waste liquid with sodium hydroxide solution until the pH of the molasses waste liquid is 11, and filter under normal pressure to obtain molasses alcohol filtrate A.

[0036] In step B, the acetic acid solution is added to the molasses alcohol filtrate A prepared in step A, and the pH of the molasses alcohol filtrate A is adjusted to 3 to obtain molasses waste liquid B.

[0037] In step C, the molasses waste liquid B obtained in step B is mixed with 35% hydrogen peroxide in a volume ratio of 1:0.2 and then put into an autoclave, where the pressure in the autoclave is 30KPa and the temperature is 100°C. The molasses waste liquid B is fully reacted with 35% industrial hydrogen peroxide to obtain the molasses waste liquid C.

[0038] S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of a modified molasses waste liquid. The preparation method comprises the following steps: A, regulating the PH of the molasses waste liquid to the range of 9-11 by use of a sodium hydroxide solution, and filtering under a normal pressure to obtain a molasses filtrate A; B, adding an acetic acid solution to the molasses filtrate A until the PH is within the range of 2-3, thereby obtaining a molasses waste liquid B; C, thoroughly oxidizing the molasses waste liquid B by using 35% hydrogen peroxide, potassium permanganate or ozone, thereby obtaining a molasses waste liquid C; D, regulating the PH of the molasses waste liquid C to the range of 9-11 by use of the sodium hydroxide solution, thereby obtaining the modified molasses waste liquid. The invention also provides a cement grinding aid which is prepared by mixing the following raw materials in parts by weight with water: 2-5 parts of triethanolamine, 18-25 parts of diethanol monoisopropanolamine, 3-5 parts of industrial salt and 20-30 parts of modified molasses waste liquid. The modified molasses waste liquid has the characteristics of low production cost, and good grinding assisting and hydration assisting effects on the cement.

Description

technical field [0001] The invention relates to the technical field of cement admixtures, in particular to cement grinding aids added to cement. Background technique [0002] Cement grinding aids can increase the hourly output of cement grinding machines, increase the strength of cement mortar, increase the amount of mixed materials, and realize energy saving and efficiency enhancement in the cement industry. The use of cement grinding aids has a history of decades, bringing cement enterprises There are obvious economic benefits. [0003] At present, the formulations of grinding aids used in most industries at home and abroad are mainly composed of one or several physical components of pure chemical products such as alcohol amines, polyols, lignin sulfonic acids, alkyl sulfonates, fatty acid salts, etc. It is mixed and can better meet the needs of cement grinding. However, due to the rising cost of chemical raw materials and transportation in recent years, the number of gri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/38C04B24/12C04B103/52
Inventor 刘伟曾荣梁石文腾灼光纪友红钟克辉彭蓉岳琴吴丹
Owner 华润水泥技术研发(广西)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com