Method for improving fluorescent analysis raw material contrast qualified ratio

A technology of fluorescence analysis and pass rate, which is applied in the direction of analyzing materials, using wave/particle radiation for material analysis, measuring devices, etc., can solve problems such as large influence, high failure rate, poor stability, etc., to improve the comparison pass rate, overcome High failure rate and good stability

Inactive Publication Date: 2015-05-13
GUANGXI YUFENG CEMENT
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In 2012, we found that the fluctuation of the raw material was large, and the qualified rate was low. In view of these situations, in order to better do the batching work and cooperate with the production, it is necessary to improve the qualified rate of the raw material
[0013] There are many faults in the mill and tablet press; the raw meal sample is dusty; the grinding aid triethanolamine has a great influence on the chemical composition of the raw meal
[0014] In the process of realizing the present invention, the inventor found that there are at least defects such as high failure rate, poor stability and unreasonable proportioning in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving fluorescent analysis raw material contrast qualified ratio
  • Method for improving fluorescent analysis raw material contrast qualified ratio
  • Method for improving fluorescent analysis raw material contrast qualified ratio

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] Implementation 1. In view of the problem of many failures of mills and tablet presses, we have conducted an analysis:

[0062] It was found that the bottom of the grinding seat was fixed by several screws. Due to the daily vibration, the screws became loose or even broke, causing grinding and dust. We welded the bottom of the disc grinding seat, so there will be no more loose screws; at the same time, we found that the tablet press made the sample crack because the pressure of the tablet press was not enough. Therefore, we found out the appropriate pressure through experiments and comparisons for specific mills. ; When the mold is damaged and cannot be used, contact the manufacturer to repair and replace the mold.

[0063] Grinding machine, tabletting machine due to verification effect table

[0064]

[0065] Depend on Figure 7 It can be seen that from January to July 2012, the operation rate of the mill and tablet press before the activity was low, with an aver...

Embodiment 2

[0066] Implementation 2. We analyzed the problem of low fluorescence operation rate:

[0067]The raw material sample is dusty because the vacuum cleaner failed to clean it in time, resulting in insufficient suction of the vacuum cleaner. When the raw material was detected, the spectrometer could not accurately analyze the actual strength of each element in the material, which directly caused the fluctuation of the ingredients. Therefore, We arrange specific post personnel to clean the vacuum cleaner every day. When the vacuum cleaner is normal, if powder samples are found around the steel ring of the raw sample and on the surface of the sample, the post personnel will be subject to financial penalties.

[0068] Verification effect table of reasons for low operating rate of spectrometer

[0069]

[0070] Depend on Figure 8 It can be seen that from January to July 2012, the operating rate of the spectrometer before the event was low, with an average of 82.50%, and the flu...

Embodiment 3

[0071] Implementation 3. Aiming at the problem that the grinding aid triethanolamine has a great influence on the chemical composition of the raw meal, we analyzed:

[0072] Research has found that grinding aids have an impact on the strength of elements in raw meal samples. Therefore, we must control the amount of triethanolamine added within a certain range, and the biggest factor that affects the constant amount of triethanolamine added is the breakage of the burette and the post personnel. In this regard, we require that once the burette is damaged, the post must be replaced immediately, and the correct method of adding triethanolamine must also be practiced during the post assessment.

[0073] Grinding aid factor verification effect table

[0074]

[0075] The pass rate of raw meal comparison has reached an average of 92.3%, which is higher than the predetermined target value of 90%, indicating that the pass rate of raw meal element comparison has increased, and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for improving fluorescent analysis raw material contrast qualified ratio. The method comprises: a, adjusting a grinding machine; b, adjusting a spectrometer; and c, performing recular screening on burettes, adjusting the formula of a grinding aid, and enabling the grinding aid to be prepared according to the following compositions in parts by weight: 0.06 part of triethanolamine, 0.08 part of Aitewei AD-E8223, and 1.12 parts of Honghai HGA620. The method capable of improving fluorescent analysis raw material contrast qualified ratio is capable of overcoming defects such as high failure rate, bad stability, unreasonable ratio and the like in the prior art, and realizes the advantages of low failure rate, good stability and reasonable ratio.

Description

technical field [0001] The invention relates to the technical field of cement processing, in particular to a method capable of improving the pass rate of raw meal comparison in fluorescence analysis. Background technique [0002] X-ray fluorescence analysis is a method for quickly determining the chemical components of various materials. This method has been widely used in the cement industry because of its fast and accurate characteristics. At present, this method is used in the analysis of limestone, sand shale, raw meal, clinker, cement and other samples in our company. Therefore, the accuracy of fluorescence inspection will indirectly affect the quality of the factory cement. Therefore, fluorescence analysis is an important part of the entire cement production control is particularly important in the process. [0003] In 2012, we found that the fluctuation of the raw material was large, and the qualified rate was low. In view of these situations, in order to better prep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G01N23/223
Inventor 钟靖华叶明波刘嘉康张彦君谭永凡韦昭井班富李金福兰琴唐定才黎柳张芳
Owner GUANGXI YUFENG CEMENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com