Wheel hub heat treatment speed-up technology

A heat treatment method and wheel hub technology, applied in heat treatment furnaces, heat treatment equipment, manufacturing tools, etc., can solve the problems of unsuitability for large-scale industrial production, slow heating of heat treatment solid solution furnaces, low heat treatment production efficiency, etc., to achieve good cooling characteristics, Reduced energy consumption and high cooling capacity

Active Publication Date: 2015-06-10
盛旺汽车零部件(昆山)有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional heat treatment has the following disadvantages: low production efficiency of heat treatment, slow temperature rise of heat treatment solid solution furnace, high energy consumption of heat treatment
The heat treatment of this invention patent has low production efficiency, takes a long time, consumes a lot of energy, and is not suitable for large-scale industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wheel hub heat treatment speed-up technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The aluminum wheel hub first passes through the camera system. The camera system takes pictures of the shape of the wheel rim and then transmits it to the X-ray machine control system. The X-ray machine retrieves the corresponding program and uses X-rays to irradiate different parts of the wheel rim to find defects inside the aluminum wheel hub. ; The X-ray machine judges that it is OK to continue to stay, and it is NG to discard it. The aluminum wheel hub passes through the X-ray machine, then the riser machine and then reaches the heat treatment. The heat treatment is divided into solid solution, quenching and aging; the temperature of the solid solution stage is set at 544°C, the heating time is 25 minutes, the holding time is 110 minutes, and then the wheel hub is maintained at 544 The temperature of ℃ enters the quenching, the time is 20S, and soaks in the quenching medium of 85 ℃ for 5 minutes. The quenching medium is 15 parts of potassium nitrate, 20 parts of sod...

Embodiment 2

[0020] The aluminum wheel hub first passes through the camera system. The camera system takes pictures of the shape of the wheel rim and then transmits it to the X-ray machine control system. The X-ray machine retrieves the corresponding program and uses X-rays to irradiate different parts of the wheel rim to find defects inside the aluminum wheel hub. ; The X-ray machine judges that it is OK to continue to stay, and it is NG to discard it. The aluminum wheel hub passes through the X-ray machine, then the riser machine and then reaches the heat treatment. The heat treatment is divided into solid solution, quenching and aging; the temperature of the solid solution stage is set at 540°C, the heating time is 28 minutes, the holding time is 115 minutes, and then the wheel hub is kept at 540°C. The temperature of ℃ enters quenching, the time is 19S, and soaks in the medium of 80 ℃ for 5 minutes. The quenching medium is 18 parts of potassium nitrate, 23 parts of sodium chloride, 25 ...

Embodiment 3

[0025] The aluminum wheel hub first passes through the camera system. The camera system takes pictures of the shape of the wheel rim and then transmits it to the X-ray machine control system. The X-ray machine retrieves the corresponding program and uses X-rays to irradiate different parts of the wheel rim to find defects inside the aluminum wheel hub. ; The X-ray machine judges that it is OK to continue to stay, and it is NG to discard it. The aluminum wheel hub passes through the X-ray machine, then the riser machine and then reaches the heat treatment. The heat treatment is divided into solid solution, quenching and aging; the temperature of the solid solution stage is set at 550°C, the heating time is 26 minutes, the holding time is 113 minutes, and then the wheel hub is kept at 550°C. The temperature of ℃ enters quenching, the time is 18S, and soaks in the medium of 90 ℃ for 5 minutes. The quenching medium is 16 parts of potassium nitrate, 22 parts of sodium chloride, 27 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of wheel hub machining, and particularly relates to a wheel hub heat treatment speed-up technology. The heat treatment method comprises three stages, namely a solid solution stage, a quenching stage and an aging stage. The flow of the wheel hub heat treatment speed-up technology comprises the steps that a casted aluminum wheel hub passes through an X-ray machine and a dead head punching machine, and then the aluminum wheel hub is subjected to heat treatment, wherein the heat treatment comprises the solid solution stage, the quenching stage and the aging stage; the temperature for the solid solution stage is set between 540 DEG C to 550 DEG C, the heating-up time ranges from 25 minutes to 28 minutes, the heat-preserving time ranges from 110 minutes to 115 minutes, the wheel hub enters the quenching stage while maintaining the temperature of the solid solution stage; the quenching time is below 20 seconds, the wheel hub is soaked into a quenching medium for 5 minutes at a temperature ranging from 80 DEG C to 90 DEG C, and the wheel hub enters the aging stage; the temperature of the aging stage ranges from 155 DEG C to 165 DEG C, and the heat-preserving time is 60 minutes.

Description

technical field [0001] The invention belongs to the field of wheel hub processing, and in particular relates to a wheel hub heat treatment speed-increasing process. Background technique [0002] Wheel hub is a high-tech, high value-added auto parts developed in recent years. It is a new economic growth point and development direction in the automotive field, especially the successful development of the third-generation wheel produced by DELPffi, the world's largest auto parts supplier. Localization of the wheel has become a top priority, and heat treatment is a key process in the manufacture of wheel units. ; Because of the complex surface shape of the parts, the heat treatment process is difficult and demanding, and has become a key process in the development of this project. Aluminum wheels are constantly being recognized for their advantages of light weight, energy saving, good heat dissipation, aesthetics, corrosion resistance, and good processability. The use of alumin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C21D9/34C21D1/00C21D1/78C21D1/60
Inventor 许育昌
Owner 盛旺汽车零部件(昆山)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap