A kind of imitation wood grain decorative board and preparation method thereof

A decorative board and imitation wood grain technology, applied in the field of imitation wood grain decorative board and its preparation, can solve the problem of phosphogypsum accumulation such as mountains, and achieve the effects of low production cost, wide source and enhanced comprehensive performance.

Inactive Publication Date: 2016-10-05
GUIZHOU KAILIN GRP CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In view of this, the object of the present invention is to provide an imitation wood grain decorative board with reasonable formula and simple preparation process and its preparation method, so as to solve the current situation that the existing phosphogypsum is piled up like a mountain, and to find a new way for the resource utilization of phosphogypsum , so as to achieve greater economic and social benefits

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of imitation wood grain decorative board and preparation method thereof
  • A kind of imitation wood grain decorative board and preparation method thereof
  • A kind of imitation wood grain decorative board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] raw material:

[0040] Phosphogypsum 40kg, fly ash 10kg, cement 10kg, yellow phosphorus slag 15kg and quicklime 1kg.

[0041] Preparation:

[0042] Grind yellow phosphorus slag into 100-mesh fine powder at 30°C to obtain slag powder, then stir phosphogypsum, fly ash, cement, slag powder and quicklime in a mixer at 50°C for 4 hours, and mix the obtained mixture After natural aging treatment for 16 days, add 10% water of the weight of the mixed material to the aged mixed material and stir evenly, pour it into a mold, and then send the formed phosphogypsum base material into a mold with a pressure of 0.1MPa, Curing treatment in a curing room with a steam temperature of 168°C for 16 hours, slowly drying the cured phosphogypsum substrate at a temperature of 50°C until the moisture content is 3%, and then sanding it with 240# sandpaper to make it smooth The thickness is 0.5mm, then spray nitro wood grain primer with a thickness of 1mm, dry at 50°C for 19 hours, and then spr...

Embodiment 2

[0045] raw material:

[0046] Phosphogypsum 60kg, fly ash 16kg, cement 14kg, yellow phosphorus slag 24kg and quicklime 4kg.

[0047] Preparation:

[0048] Grind yellow phosphorus slag into 100-mesh fine powder at 40°C to obtain slag powder, then stir and react phosphogypsum, fly ash, cement, slag powder and quicklime at 60°C for 4 hours, and mix the obtained mixture After natural aging treatment for 24 days, add water with a weight of 15% of the mixed material to the aged mixed material, stir evenly, pour it into a mold, and then send the formed phosphogypsum base material into a mold with a pressure of 0.1MPa, Curing treatment in a curing room with a steam temperature of 172°C for 18 hours, slowly drying the cured phosphogypsum substrate at a temperature of 60°C until the moisture content is 5%, and then sanding it with 240# sandpaper to make it smooth The thickness is 2mm, then spray nitro wood grain primer, the thickness is 2mm, dry at 60°C for 16h, and then spray the sty...

Embodiment 3

[0051] raw material:

[0052] Phosphogypsum 45kg, fly ash 12kg, cement 11kg, yellow phosphorus slag 17kg and quicklime 2kg.

[0053] Preparation:

[0054] Grind yellow phosphorus slag into 100-mesh fine powder at 32°C to obtain slag powder, then stir and react phosphogypsum, fly ash, cement, slag powder and quicklime at 52°C for 4 hours, and prepare the obtained mixture After natural aging treatment for 18 days, add water with a weight of 12% of the mixed material to the aged mixed material, stir evenly, pour it into a mold, and then send the formed phosphogypsum base material into a mold with a pressure of 0.1MPa, Curing treatment in a curing room with a steam temperature of 169°C for 17 hours, slowly drying the cured phosphogypsum substrate at a temperature of 52°C until the moisture content is 4%, and then sanding it with 240# sandpaper to make it smooth The thickness is 0.8mm, then spray nitro wood grain primer with a thickness of 1.4mm, dry it at a temperature of 52°C f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an imitation wood grain decorative plate and a preparation method thereof. The imitation wood grain decorative plate is prepared from the following raw materials in parts by weight: 40 to 60 parts of ardealite, 10 to 16 parts of coal ash, 10 to 14 parts of cement, 15 to 24 parts of yellow phosphorus slag, and 1 to 4 parts of calcined lime. The invention has the advantages that the imitation wood grain decorative plate is maintained under the condition that the pressure is 0.3 MPa, and the steam temperature is 128 to 132 DEG C, so that the quality and the finished product yield of the imitation wood grain decorative plate are remarkably improved, and low energy consumption, high productivity and low investment are achieved; meanwhile, through the maintenance method, the shrinkage rate of a base material in a dry environment and the expansion rate of the base material in a water-soaked environment are remarkably reduced, the compressive strength of the base material is enhanced, and the service life of the base material is prolonged.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an imitation wood grain decorative board and a preparation method thereof. Background technique [0002] In the phosphoric acid production process, every ton of P produced 2 o 5 Five tons of phosphogypsum are produced by-product, and the annual by-production of phosphogypsum by medium-sized phosphoric acid production enterprises is about 3.5 million tons. So much phosphogypsum not only requires a large slag dump, but also causes water pollution. At present, the most commonly used phosphogypsum treatment methods are as follows: [0003] The first method: Phosphoric acid paste is used to backfill the pit. According to statistics, when phosphogypsum is not used to backfill the mine shaft, the filling cost of the mine shaft accounts for 1 / 3 of the mining, and the filling material accounts for 80% of the filling cost. If phosphogypsum is used to fill the mine shaft, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/14C04B41/71B28B11/24
Inventor 杨永彬杨步雷向前勇王伟刘小成胡新菊李泽钢
Owner GUIZHOU KAILIN GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com