Novel high density integrated electric inductance manufacturing method

A manufacturing method and high-density technology, applied in the manufacture of inductors/transformers/magnets, circuits, electrical components, etc., can solve the problems of poor electromagnetic performance of inductors, poor heat dissipation, large size, etc. , small size effect

Active Publication Date: 2015-09-09
POCO HLDG CO LTD +2
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] The invention proposes a method for manufacturing an inductor, which solves the problem of poor electromagnetic performance, low density, large volume, and poor heat dissipation effect of the inductor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel high density integrated electric inductance manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0043] Example 1

[0044] A new type of manufacturing method for high-density integrated inductors includes the following steps:

[0045] (1) Through an automatic winding machine, the enameled wire coil is wound in a spiral shape;

[0046] (2) The first ferromagnetic powder is mechanically pressed into a density of 6.5g / cm 3 The magnetic core, the first ferromagnetic powder is iron silicon powder;

[0047] (3) Put the magnetic core into the hollow cavity of the enameled wire coil;

[0048] (4) Put the enameled wire coil equipped with the magnetic core into an injection mold;

[0049] (5) Mix the modified epoxy silicone resin, mercaptopropylmethyldimethoxysilane, and m-xylylenediamine in a weight ratio of 7:1:2 to obtain a high-temperature resin glue;

[0050] (6) The second ferromagnetic powder and the high temperature resin glue are mixed and stirred uniformly at a weight ratio of 94:6 to obtain a magnetic composite material. The second ferromagnetic powder is made of -100 mesh to 200 me...

Example Embodiment

[0054] Example 2

[0055] A new type of manufacturing method for high-density integrated inductors includes the following steps:

[0056] (1) Through an automatic winding machine, the enameled wire coil is wound in a spiral shape;

[0057] (2) The first ferromagnetic powder is mechanically pressed to a density of 6.2g / cm 3 The magnetic core, the first ferromagnetic powder is iron silicon powder;

[0058] (3) Put the magnetic core into the hollow cavity of the enameled wire coil;

[0059] (4) Put the enameled wire coil equipped with the magnetic core into an injection mold;

[0060] (5) Mix the modified epoxy silicone resin, mercaptopropylmethyldimethoxysilane, and m-xylylenediamine in a weight ratio of 75:7:18 to obtain a high-temperature resin glue;

[0061] (6) Mix the second ferromagnetic powder and the high-temperature resin glue at a weight ratio of 9:1 to obtain a magnetic composite material. The second ferromagnetic powder is made of -100 mesh to 200 mesh, -200 mesh to 500 mesh. T...

Example Embodiment

[0065] Example 3

[0066] A new type of manufacturing method for high-density integrated inductors includes the following steps:

[0067] (1) Through an automatic winding machine, the enameled wire coil is wound in a spiral shape;

[0068] (2) The first ferromagnetic powder is mechanically pressed to a density of 6.9g / cm 3 The magnetic core, the first ferromagnetic powder is iron silicon powder;

[0069] (3) Put the magnetic core into the hollow cavity of the enameled wire coil;

[0070] (4) Put the enameled wire coil equipped with the magnetic core into an injection mold;

[0071] (5) Mix and stir epoxy silicone resin, mercaptopropylmethyldimethoxysilane, and m-xylylenediamine in a weight ratio of 80:5:15 to obtain a high temperature resin glue;

[0072] (6) Mix the second ferromagnetic powder and the high temperature resin glue at a weight ratio of 88:12 to obtain a magnetic composite material. The second ferromagnetic powder is made from -100 mesh to 200 mesh and -200 mesh to 500 mesh....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel high density integrated electric inductance manufacturing method, which comprises: (1) winding an varnished wire coil into a spiral shape; (2) making first iron magnetic powers into a magnetic core through mechanical pressing; (3) packing the magnetic core into a hollow cavity of the varnished wire coil; (4) packing the varnished wire coil packed with the magnetic core into an injection mold; (5) uniformly mixing and blending resin adhesive, coupling agent and accelerant to obtain high temperature resin adhesive; (6) uniformly mixing and blending the second iron magnetic powers and the high temperature resin adhesive to obtain magnetism composite material; (7) injecting the magnetism composite material into a mold cavity of the injection mold to mold, and solidifying to obtain external magnetic body; and (8) cooling and stripping to obtain molded electric inductance. According to the invention, the volume of the electric inductance manufactured with the method provided herein is small; the density is high; the relative magnetic conductivity is high; the cooling performance is good; the service life is long; the electric inductance is molded as a whole; and the manufacturing method of the electric inductance is simple, thus reducing the production cost.

Description

technical field [0001] The invention relates to the technical field of inductance components, in particular to a method for manufacturing a novel high-density integrally formed inductance. Background technique [0002] With the development of the electronics industry, filters, choke coils, transformers and reactors are widely used in circuit control systems in various switching power supplies, UPS, photovoltaic inverters, wind energy and other power supplies. Filtering, rectification, and inverter can all be applied to inductive components. [0003] The use of inductors or reactors plays a vital role in the development of the modern electronics industry. The components made by traditional techniques are gradually not fully suitable for the development of miniaturization in the future. To develop a high-performance miniaturized inductor or reactor It is of great significance to adapt to the rapid development of modern electronic technology. [0004] The manufacturing proces...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01F41/00H01F41/02H01F1/147
Inventor 郭雄志肖强阮佳林邱俊刘志达罗涛刘元来
Owner POCO HLDG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap