Die aluminum alloy

An aluminum alloy and mold technology, applied in the field of mold aluminum alloy, can solve the problems of short manufacturing cycle, low alloy material cost and high manufacturing cost, and achieve the effects of stable performance, good toughness, and scientific and reasonable components

Inactive Publication Date: 2015-09-16
ZXSY KUNSHAN METAL TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of science and technology, the scope of mold application is becoming more and more extensive. For the manufacture of product molds with multiple varieties, small batches or frequent updates and modifications, such as injection molds, blow molds, and compression molds, it is required to have manufacturing The characteristics of short cycle, low manufacturing difficulty and low cost, while the steel mold usually used in the prior art has high manufacturing cost, long cycle, and relatively low cost of alloy materials, so it is widely used in the field of manufacturing such molds
However, pure metals cannot meet the requirements of plasticity, hardness, strength, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A mold aluminum alloy, comprising the following components in parts by weight:

[0020] Carbon 0.03 parts;

[0021] Tungsten 0.3 parts;

[0022] Cobalt 0.001 part;

[0023] Grape straw 0.007 part;

[0024] Technetium 0.1 part;

[0025] Iron 2 parts;

[0026] Copper 10 parts;

[0027] Aluminum 70 parts.

Embodiment 2

[0029] A mold aluminum alloy, comprising the following components in parts by weight:

[0030] Carbon 0.25 parts;

[0031] Tungsten 0.45 parts;

[0032] Cobalt 0.005 parts;

[0033] Grape straw 0.02 part;

[0034] Technetium 0.25 parts;

[0035] Iron 4 parts;

[0036] 12 parts of copper;

[0037] Tin 0.15 parts;

[0038] Aluminum 72 parts.

Embodiment 3

[0040] A mold aluminum alloy, comprising the following components in parts by weight:

[0041] Carbon 0.58 parts;

[0042] Tungsten 0.65 parts;

[0043] Cobalt 0.008 parts;

[0044] Grape straw 0.04 part;

[0045] Technetium 0.35 parts;

[0046] Iron 6 parts;

[0047] 15 parts of copper;

[0048] 0.25 parts of tin;

[0049] Aluminum 75 parts.

[0050] The invention has the advantages that the mold has scientific and reasonable components, good toughness and stable performance, and meets the needs of enterprises.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a die aluminum alloy, which comprises the following components by weight part: 0.03-0.58 parts of carbon, 0.3-0.65 parts of tungsten, 0.001-0.008 parts of cobalt, 0.007-0.04 parts of grape straw, 0.1-0.35 parts of technetium, 2-6 parts of iron, 10-15 parts of copper and 70-75 parts of aluminum. The die aluminum alloy has the advantages that the composition proportion is scientific and reasonable, toughness is good, performance is stable, and enterprise requirement can be satisfied.

Description

technical field [0001] The invention relates to a mold aluminum alloy. Background technique [0002] With the development of science and technology, the scope of mold application is becoming more and more extensive. For the manufacture of product molds with multiple varieties, small batches or frequent updates and modifications, such as injection molds, blow molds, and compression molds, it is required to have manufacturing The characteristics of short cycle, low manufacturing difficulty and low cost, while the steel molds usually used in the prior art have high manufacturing cost, long cycle, and relatively low cost of alloy materials, so they are widely used in the field of manufacturing such molds. But pure metals cannot meet the requirements such as plasticity, hardness, and strength. [0003] Therefore, in order to solve the above problems, a new technical solution is provided. Contents of the invention [0004] The invention provides a mold aluminum alloy. [0005...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/12
Inventor 不公告发明人
Owner ZXSY KUNSHAN METAL TECH