Die aluminum alloy

An aluminum alloy and mold technology, applied in the field of mold aluminum alloy, can solve the problems of short manufacturing cycle, low cost of alloy materials, high manufacturing cost, etc., and achieve the effects of stable performance, good toughness, and scientific and reasonable components

Inactive Publication Date: 2020-05-15
荆门荆华铝业有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of science and technology, the scope of mold application is becoming more and more extensive. For the manufacture of product molds with multiple varieties, small batches or frequent updates and modifications, such as injection molds, blow molds, and compression molds, it is required to have manufacturing The characteristics of short cycle, low manufacturing difficulty and low cost, while the steel mold usually used in the prior art has high manufacturing cost, long cycle, and relatively low cost of alloy materials, so it is widely used in the field of manufacturing such molds
However, pure metals cannot meet the requirements of plasticity, hardness, strength, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A mold aluminum alloy, comprising the following components by weight: 0.03 parts of carbon; 0.3 parts of tungsten; 0.001 parts of cobalt; 0.007 parts of niobium; 0.1 parts of technetium; 2 parts of lime powder; 10 parts of copper; 70 parts of aluminum.

Embodiment 2

[0012] A mold aluminum alloy, comprising the following components by weight: 0.25 parts of carbon; 0.45 parts of tungsten; 0.005 parts of cobalt; 0.02 parts of niobium; 0.25 parts of technetium; 4 parts of lime powder; 12 parts of copper; 0.15 parts of tin; 72 parts of aluminum.

Embodiment 3

[0014] A mold aluminum alloy, comprising the following components by weight: 0.58 parts of carbon; 0.65 parts of tungsten; 0.008 parts of cobalt; 0.04 parts of niobium; 0.35 parts of technetium; 6 parts of lime powder; 15 parts of copper; 0.25 parts of tin; 75 parts of aluminum.

[0015] The invention has the advantages that the mold has scientific and reasonable components, good toughness and stable performance, and meets the needs of enterprises.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a die aluminum alloy. The die aluminum alloy comprises, by weight, 0.03-0.58 part of carbon, 0.3-0.65 part of tungsten, 0.001-0.008 part of cobalt, 0.007-0.04 part of niobium, 0.1-0.35 part of technetium, 2-6 parts of lime powder, 10-15 parts of copper, and 70-75 parts of aluminum. The die aluminum alloy has the advantages that a die made of the die aluminum alloy is scientific and reasonable in component, good in toughness, stable in performance and capable of meeting the requirements of an enterprise.

Description

technical field [0001] The invention relates to a mold aluminum alloy. Background technique [0002] With the development of science and technology, the scope of mold application is becoming more and more extensive. For the manufacture of product molds with multiple varieties, small batches or frequent updates and modifications, such as injection molds, blow molds, and compression molds, it is required to have manufacturing The characteristics of short cycle, low manufacturing difficulty and low cost, while the steel molds usually used in the prior art have high manufacturing cost, long cycle, and relatively low cost of alloy materials, so they are widely used in the field of manufacturing such molds. But pure metals cannot meet the requirements such as plasticity, hardness, and strength. [0003] Therefore, in order to solve the above problems, a new technical solution is provided. Contents of the invention [0004] The invention provides a mold aluminum alloy. [0005...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/12
CPCC22C21/12
Inventor 田圣乔
Owner 荆门荆华铝业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com