Fastener steel with high strength

A fastener and high-strength technology, applied in the field of metallurgy, can solve the problems of not meeting the requirements of steel types, high cost, strength, low-temperature toughness and hardenability.

Active Publication Date: 2018-06-29
曹鸿玉
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In view of the above situation, in order to overcome the defects of the existing steel technology, the purpose of the present invention is to provide a high-strength fastener steel, which can effectively solve the problem that the strength, low-temperature toughness and hardenability of the existing steel cannot meet the requirements when the diameter is large. , poor cost performance, high cost, and cannot meet the requirements for steel types under special circumstances in actual production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fastener steel with high strength
  • Fastener steel with high strength
  • Fastener steel with high strength

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] In the specific implementation of the present invention, a high-strength fastener steel is composed of the following components in weight percentage: C 0.42%, Si 0.37%, Mn 1.08%, P 0.007%, S 0.006%, V 0.10%, B 0.0020%, O 0.0010%, and the balance is Fe.

Embodiment 2

[0020] In the specific implementation of the present invention, a high-strength fastener steel is composed of the following components in weight percentage: C0.38-0.45%, Si 0.22-0.36%, Mn 0.81-1.48%, P≤0.018%, S ≤0.010%, V≥0.10%, B0.0009-0.0024%, O≤0.0015%, and the balance is Fe.

Embodiment 3

[0022] In the specific implementation of the present invention, a high-strength fastener steel is composed of the following components in weight percentage: C0.39-0.45%, Si 0.39-0.48%, Mn 0.81-1.48%, P≤0.018%, S ≤0.010%, V≥0.10%, B0.0009-0.0024%, O≤0.0015%, and the balance is Fe.

[0023] The composition and dosage of the present invention are scientific and reasonable. The test steel developed by the present invention is carried out according to the requirements of grade 10.9, which has the largest application amount and the widest application range. The test effect is very good. It cannot be achieved when the diameter requirements are large and the cost performance requirements are high; new steel types have been developed to meet the needs of special steel in the new era. The relevant information is as follows:

[0024] In the implementation of the present invention, steels with seven components are given, and the specific components are shown in Table 1.

[0025] Table 1 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to fastener steel with the good strength, good low-temperature toughness, good hardenability, the high cost performance and the good fatigue performance. According to the fastener steel, the problem that the requirements for the steel type under special conditions in real production cannot be met due to the fact that when existing the steel is large in diameter, the strength,the low-temperature toughness and the hardenability cannot meet the requirements, the cost performance is poor and the cost is high can be effectively solved. The fastener steel is composed of the following components, by weight, 0.38-0.45% of C, 0.22-0.48% of Si, 0.81-1.48% of Mn, less than or equal to 0.018% of P, less than or equal to 0.010% of S, larger than or equal to 0.10% of V, 0.0009-0.0024% of B, less than or equal to 0.0015% of O, and the balance Fe. The fastener steel has the advantages of being scientific and reasonable in component and easy to produce; low-temperature impact absorption energy Kv of 10.9 grade fastener at the temperature of 20 DEG C below zero is not less than 27J, the low-temperature impact absorption energy Kv at the temperature of 40 DEG C below zero is not less than the requirement of 27J, especially when the diameter is large, the requirements of use of new standards and special users can be met, only highest level experts, professors, even academician post-graduates in the country can be met, and the austenite continuous cooling curve of the steel is tested, so that the unexpected effects of remarkable technology, economic and social benefits are achieved.

Description

technical field [0001] The invention relates to an alloy steel in the field of metallurgy, in particular to a high-strength fastener steel with good strength, low-temperature toughness, hardenability, cost performance and fatigue resistance. Background technique [0002] High-strength fasteners are an important basic component with a large amount of use and a wide range of applications. Not only in industries such as machinery, automobiles, and trains, but also in roads, railways, bridges, and building infrastructure projects. With the development of high-quality products in my country and the world, not only the strength requirements for high-strength fasteners have been increased, but also unprecedented new requirements for low-temperature impact toughness. In line with this requirement, corresponding international and domestic standards have been released one after another. In addition, the diameter requirements for high-strength fasteners continue to expand. The exist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/12
CPCC22C38/002C22C38/02C22C38/04C22C38/12
Inventor 韩建中
Owner 曹鸿玉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products