Ceramsite concrete structure, preparation method thereof and corresponding ceramsite plate and ceramsite brick

A technology of ceramsite concrete and concrete structure, which is applied in the field of lightweight and high-strength ceramsite slabs and light-weight and high-strength ceramsite bricks, can solve the problems of being easily broken, uneven distribution of ceramsite, unstable structural performance, etc., and achieve complete good effect

Inactive Publication Date: 2015-10-28
FUJIAN ANGU NEW ENVIRONMENTAL BUILDING MATERIALS CO LTD
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] For this reason, it is necessary to provide a ceramsite concrete structure, which is used to solve the problem that the ceramsite is unevenly distributed and easily smashed when pouring ceramsite concrete in the prior art, resulting in unstable structural performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramsite concrete structure, preparation method thereof and corresponding ceramsite plate and ceramsite brick
  • Ceramsite concrete structure, preparation method thereof and corresponding ceramsite plate and ceramsite brick
  • Ceramsite concrete structure, preparation method thereof and corresponding ceramsite plate and ceramsite brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A lightweight high-strength ceramsite board, the concrete structure in the lightweight high-strength ceramsite board is formed by pouring and solidifying the raw materials for preparation, and the raw materials for preparation include the following materials in parts by weight:

[0041] Cement: 30 parts, sand: 35 parts, fly ash: 15 parts, ceramsite 30 parts;

[0042] Such as figure 1 As shown, wherein, the diameter of the ceramsite 1 is 1-5 cm, and the ceramsite 1 is provided with a through hole 11, and the ceramsite 2 is connected in series by the metal wire 2 through the through hole 11. In order to fix the ceramsite on the wire, after the metal wire passes through the through hole of the ceramsite, soak the wire with the ceramsite in the adhesive. In this embodiment, the adhesive uses epoxy resin adhesive , In other embodiments, acrylate reactive adhesives and the like may also be used. Then adjust the ceramsite on the wire to a suitable position, and wait for the ...

Embodiment 2

[0046] A light-weight high-strength ceramsite board. In this embodiment, the structure of the light-weight high-strength ceramsite board is similar to the structure of the light-weight high-strength ceramsite board in Embodiment 1. They are all connected in series by wire ceramsite. The difference is that the ratio of the parts by weight of the concrete preparation raw materials is different. In this embodiment, the raw materials for the preparation include the following parts by weight:

[0047] Cement: 50 parts, sand: 25 parts, fly ash: 25 parts, ceramsite 50 parts;

[0048] Wherein, the diameter of the ceramsite is 3-5 cm.

[0049] The pouring process of the lightweight high-strength ceramsite board is:

[0050]Prepare the following preparation raw materials in parts by weight: cement: 50 parts, sand: 25 parts, fly ash: 25 parts, ceramsite 50 parts, foaming agent 1 part;

[0051] Wherein, the diameter of the ceramsite is 3-5 cm, and the ceramsite has three through holes t...

Embodiment 3

[0059] A lightweight high-strength ceramsite brick, the lightweight high-strength ceramsite brick is cast from ceramsite concrete, and the preparation raw materials of the ceramsite concrete include the following materials in parts by weight:

[0060] Cement: 40 parts, sand: 30 parts, fly ash: 20 parts, ceramsite 40 parts;

[0061] Wherein, the diameter of the ceramsite is 1-3 cm, the concrete structure also includes a metal wire, the ceramsite has a through hole for the metal wire to pass through, and the metal wire passes through the through hole and connects two or more of ceramsite.

[0062] The preparation process of the lightweight high-strength ceramsite brick is:

[0063] Prepare raw materials for preparation, which include the following materials in parts by weight: cement: 40 parts, sand: 30 parts, fly ash: 20 parts, ceramsite 40 parts, foaming agent 0.5 parts;

[0064] Mix the cement, sand, fly ash, foaming agent and 25 parts by weight of water in the raw material...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramsite concrete structure. The ceramsite concrete is formed by adding water into preparation raw materials to conduct pouring and solidification. The preparation raw materials include, by weight, 30-50 parts of cement, 25-35 parts of sand, 15-25 parts of fly ash, and 30-50 parts of ceramsite with a diameter of 1-5cm. The concrete structure also comprises a metal wire, ceramsites have through-holes for the metal wire to pass through, and the metal wire passes throught the through-holes and connects over two ceramites. The invention also discloses a preparation method of the ceramsite concrete structure and a corresponding ceramsite plate and ceramsite brick. The ceramsite concrete structure and the corresponding ceramsite plate and ceramsite brick provided by the invention have evenly distributed ceramsites and high structural strength.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a structure and preparation process of ceramsite concrete, and a lightweight high-strength ceramsite board and a lightweight high-strength ceramsite brick obtained through the structure and process. Background technique [0002] Using ceramsite instead of stone as the aggregate of concrete, such concrete is called "ceramsite concrete". The exterior wall panels of prefabricated steel-concrete structures use "ceramsite concrete". It is formulated from cementitious materials and lightweight aggregates. It can be divided into full light concrete (with light sand) and sand light concrete (with ordinary sand). [0003] Ceramsite concrete has the following characteristics: [0004] 1. Ceramsite concrete is light in weight, and its dry bulk density is 800---1900KG / M 3 , 2 / 3-1 / 5 lighter than ordinary concrete, and the grade can reach CL5---CL60. Due to the light weight, it can reduce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B38/02C04B20/00
Inventor 林宏涛
Owner FUJIAN ANGU NEW ENVIRONMENTAL BUILDING MATERIALS CO LTD