A kind of coarse denier porous polyester fiber and its preparation method

A porous polyester and fiber technology, applied in the direction of fiber type, fiber treatment, single-component polyester rayon, etc., can solve the problems of hairiness, short heating time, easy broken filaments, etc., to reduce damage and reduce the surface The effect of improving tension and smoothness

Active Publication Date: 2017-11-03
JIANGSU HENGKE ADVANCED MATERIALS CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the contact heating space between coarse denier porous polyester fiber and hot roller is small, the heating time is short, it is not easy to heat uniformly, and the surface area of ​​coarse denier fiber is large, the tension of spinning, drafting and winding is large, and it is easy to break the filament and produce hairiness. What kind of oil agent, improved wettability and concentration of the oil agent will play a greater role in ensuring the quality of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of coarse denier porous polyester fiber and its preparation method
  • A kind of coarse denier porous polyester fiber and its preparation method
  • A kind of coarse denier porous polyester fiber and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A method for preparing coarse-denier porous polyester fibers. First, an oil-on oil is prepared. The specific preparation steps are: blending the starter butanol and strong alkali potassium hydroxide, then raising the temperature to 105°C, and then adding and mixing Homogeneous ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl] ethylene oxide and propylene oxide, the amount of butanol is ethylene oxide, [(1,1 , 2,2-tetrafluoroethoxy) methyl] 1‰ of the total mass of ethylene oxide and propylene oxide, the amount of strong base potassium hydroxide is ethylene oxide, [(1,1,2,2 -1‰ of the total mass of -tetrafluoroethoxy)methyl]oxirane and propylene oxide, ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl]epoxide The molar ratio of ethane and propylene oxide is 10:1:20, the polymerization reaction is carried out under the protective atmosphere of nitrogen atmosphere, the reaction pressure is 0.4MPa, and after the relative molecular weight is 1000, the fluorine-containing p...

Embodiment 2

[0067] A method for preparing coarse-denier porous polyester fibers. First, an oil-on oil is prepared. The specific steps are: blending the initiator butanol and strong alkali sodium hydroxide, then raising the temperature to 125° C., and then adding the well-mixed Ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl] ethylene oxide and propylene oxide, the amount of butanol is ethylene oxide, [(1,1,2 , 2-tetrafluoroethoxy) methyl] 5‰ of the total mass of ethylene oxide and propylene oxide, the amount of strong alkali sodium hydroxide is ethylene oxide, [(1,1,2,2-tetra 5‰ of the total mass of fluoroethoxy)methyl]oxirane and propylene oxide, ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl]oxirane The molar ratio of propylene oxide and propylene oxide is 20:3:30, and the polymerization reaction is carried out under the protective atmosphere of an inert gas atmosphere, the reaction pressure is 0.5MPa, and after reaching a relative molecular weight of 4000, neutralization, adsorp...

Embodiment 3

[0080] A method for preparing coarse-denier porous polyester fibers. First, an oil-on oil is prepared. The specific steps are: blending the initiator butanol and strong alkali sodium hydroxide, then raising the temperature to 115°C, and then adding the well-mixed Ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl] ethylene oxide and propylene oxide, the amount of butanol is ethylene oxide, [(1,1,2 , 2-tetrafluoroethoxy) methyl] 2‰ of the total mass of ethylene oxide and propylene oxide, the amount of strong alkali sodium hydroxide is ethylene oxide, [(1,1,2,2-tetra 1.5‰ of the total mass of fluoroethoxy)methyl]oxirane and propylene oxide, ethylene oxide, [(1,1,2,2-tetrafluoroethoxy)methyl]oxirane The molar ratio of propylene oxide and propylene oxide is 12:1:30, and the protective atmosphere is an inert gas atmosphere to carry out polymerization reaction, the reaction pressure is 0.8MPa, and after reaching a relative molecular weight of 3000, neutralization, adsorption, vacuum...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to a coarse-denier porous polyester fiber and a preparation method thereof. The coarse-denier porous polyester fiber is mainly prepared by melt-spinning, oiling, stretching and winding of polyester through a number of spinneret holes; The oil agent of the oiling agent includes at least fluorine-containing polyether, and the quality of the fluorine-containing polyether ≥ 45% of the quality of the oil agent; the fluorine-containing polyether is ethylene oxide, [(1,1, 2,2-tetrafluoroethoxy) methyl] random copolymer of oxirane and propylene oxide, its structural formula is: the preparation method of the present invention is that polyester is measured, extruded, cooled, oiled And high-speed winding, made coarse denier porous polyester fiber. The coarse denier porous polyester fiber of the present invention endows the polyester fiber with a soft and elegant silk light feeling, not only has excellent optical properties, but due to the large number of fibers, the arrangement between the fibers cannot be tight, and the gaps increase accordingly, thereby The fabric feels thicker, with better fluffiness and air permeability.

Description

technical field [0001] The invention relates to a coarse denier porous polyester fiber and a preparation method thereof. Background technique [0002] Since its appearance, polyethylene terephthalate (PET) fiber has developed rapidly because of its excellent performance, and its output has become the crown of synthetic fibers in the world. Polyester fiber has a series of excellent properties such as high breaking strength and elastic modulus, moderate resilience, excellent heat setting, good heat resistance and light resistance, acid resistance, alkali resistance and corrosion resistance, and the fabric has the advantages of wrinkle resistance and good stiffness, so , Polyester fibers are widely used in clothing, home textiles and other fields. [0003] Coarse denier porous yarns such as 150D / 144F, 150D / 288F, 150D / 384F, etc., have a large total fiber fineness, a large number of fiber F, soft hand feeling, good fabric drapability, good heat retention and moisture absorption,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/53D06M13/02D06M13/292D06M13/256D06P1/16D06P1/44D01F6/62C08G65/28D06M101/32
Inventor 柴森光韦开顺苏琦
Owner JIANGSU HENGKE ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com