Thermal insulation mortar for building external walls and preparation method thereof

A technology for thermal insulation mortar and building exterior walls, which is applied in the field of building materials, can solve the problems such as the treatment method and utilization status of papermaking sludge ash that are not specified in detail, and achieve good economic and social benefits, resource saving, and good thermal insulation performance.

Active Publication Date: 2015-11-18
东莞市欧瑞建筑有限公司
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention describes the method of producing paper sludge ash, but does not specify the treatment method and utilization status of paper sludge ash

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A building exterior wall thermal insulation mortar, which is composed of the following raw materials in parts by weight: 110 parts of sulphoaluminate cement, 20 parts of papermaking sludge ash, 5 parts of polyphenylene particles, 8 parts of vitrified microbeads, and 0.5 parts of cellulose ether 0.3 parts of air-entraining agent, 0.6 parts of polycarboxylate superplasticizer, 0.3 parts of alkali-resistant glass fiber, and 60 parts of water.

[0027] As described above, the papermaking sludge ash is the powder obtained by incinerating papermaking sludge at 400-850° C., sieved with a 200-mesh sieve, and the residue is less than 10%.

[0028] As mentioned above, the main components of papermaking sludge ash are calcium aluminosilicate and anhydrous calcium sulfate.

[0029] Described, the particle diameter of polyphenylene particle is 2-5mm, and bulk density is 8.9kg / m 3 .

[0030] Described, the air-entraining agent is sodium dodecylbenzenesulfonate.

[0031] Said alkal...

Embodiment 2

[0037] A building exterior wall insulation mortar, which is composed of the following raw materials in parts by weight: 110 parts of sulphoaluminate cement, 23 parts of papermaking sludge ash, 6 parts of polyphenylene particles, 10 parts of vitrified microbeads, and 0.6 parts of cellulose ether 0.5 parts of air-entraining agent, 0.8 parts of polycarboxylate superplasticizer, 0.4 parts of alkali-resistant glass fiber, and 70 parts of water.

[0038] As described above, the papermaking sludge ash is the powder obtained by incinerating papermaking sludge at 400-850° C., sieved with a 200-mesh sieve, and the residue is less than 10%.

[0039] As mentioned above, the main components of papermaking sludge ash are calcium aluminosilicate and anhydrous calcium sulfate.

[0040] Described, the particle diameter of polyphenylene particle is 2-5mm, and bulk density is 8.9kg / m 3 .

[0041] Described, the air-entraining agent is sodium dodecylbenzenesulfonate.

[0042] Said alkali-resis...

Embodiment 3

[0048] A building exterior wall thermal insulation mortar, which is composed of the following raw materials in parts by weight: 110 parts of sulphoaluminate cement, 25 parts of papermaking sludge ash, 8 parts of polyphenylene particles, 12 parts of vitrified microbeads, and 0.8 parts of cellulose ether 0.6 parts of air-entraining agent, 0.9 parts of polycarboxylate superplasticizer, 0.5 parts of alkali-resistant glass fiber, and 80 parts of water.

[0049] As described above, the papermaking sludge ash is the powder obtained by incinerating papermaking sludge at 400-850° C., sieved with a 200-mesh sieve, and the residue is less than 10%.

[0050] As mentioned above, the main components of papermaking sludge ash are calcium aluminosilicate and anhydrous calcium sulfate.

[0051] Described, the particle diameter of polyphenylene particle is 2-5mm, and bulk density is 8.9kg / m 3 .

[0052] Described, the air-entraining agent is sodium dodecylbenzenesulfonate.

[0053]Said alkal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a thermal insulation mortar for building external walls. The thermal insulation mortar consists of sulfate aluminium cement, papermaking sewage sludge ash, polystyrene granules, glazed hollow beads, cellulose ether, an air-entraining agent, a polycarboxylate superplasticizer, alkali-resistant glass fibers and water, and further discloses a preparation method of the thermal insulation mortar. As paper mill sludge ash replaces part of cement, the compactness and the water resistance are very good, the thermal insulation mortar is stable in physical property, free of cracks, ageing-resistant, long in service life and excellent in thermal insulation performance. Not only is harmless utilization of paper mill sludge ash realized to protect the environment, but also resources are saved, waste is changed into valuable, the consumption of cement is reduced, the cost is lowered, and favorable economic and social benefits are achieved. The preparation method is simple, can be completed according to the conventional technology and is low in production cost.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a building exterior wall thermal insulation mortar and a preparation method thereof. Background technique [0002] Insulation mortar mainly uses cement as the cementitious material, lightweight materials as the aggregate, mixed with modified admixtures of specific components, and a certain amount of admixture is introduced, and after being stirred by a mixer, it is used to build external wall insulation Base mortar in the system. In recent years, some new materials are often used to replace traditional cementitious materials and aggregates, mainly including finely ground granular blast furnace slag, fly ash, silica fume, glass, rubber and milled cable waste, etc. [0003] With the development of the economy, the amount of paper used is increasing, and the sludge produced by the paper industry every year has brought serious pollution to the environment. In Europe, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B18/10
CPCY02W30/91
Inventor 刘广利
Owner 东莞市欧瑞建筑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap