Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Inorganic-organic composite permeable crystallization type waterproof agent

A technology of permeating crystallization and waterproofing agent, applied in the field of concrete building waterproofing materials, can solve the problems of high production cost of waterproofing materials, limiting the application scope of concrete waterproofing engineering, etc., to improve waterproofness and self-healing properties, enhance waterproofing effect, and increase thickness Effect

Inactive Publication Date: 2015-11-25
GUILIN HEXIN WATERPROOF DECORATION MATERIAL
View PDF7 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, domestic osmotic crystalline waterproof materials are mainly configured by importing osmotic crystalline masterbatches, such as Chinese patent numbers CN102786275B, CN101362867A, CN101654351A, etc. Therefore, the production cost of waterproof materials is relatively high, which limits its application in concrete waterproofing projects. Application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inorganic-organic composite permeable crystallization type waterproof agent
  • Inorganic-organic composite permeable crystallization type waterproof agent
  • Inorganic-organic composite permeable crystallization type waterproof agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] Below in conjunction with embodiment, the present invention will be further described:

[0028] The inorganic-organic composite osmotic crystalline waterproofing agent of the present invention is made of the following components in proportion by weight: 8-15 parts of sodium silicate, 3-6 parts of sodium methyl silicate, sodium alginate 2-6 parts, 6-10 parts of gelatin, 2-6 parts of dodecyl ethoxy sulfobetaine, 2-5 parts of sodium carbonate, 1-4 parts of sodium citrate, 2-4 parts of triethanolamine, sulfuric acid 1-9 parts of aluminum potassium, 1-6 parts of calcium sulfate, 1-3 parts of polyacrylamide, 1-4 parts of calcium lignosulfonate, 2-7 parts of hydroxyethyl methylcellulose, 3-7 parts of calcium hydroxide 1-3 parts of boric acid, 60-85 parts of water. In specific implementation, it can be directly applied to the base surface to be waterproofed by spraying or brushing, and repeated brushing to a certain thickness, and curing for 3 days or more is enough.

[0029]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an inorganic-organic composite permeable crystallization type waterproof agent. The waterproof agent is prepared from, by weight, 8-15 parts of sodium silicate, 3-6 parts of methyl sodium silicate, 2-6 parts of sodium alginate, 6-10 parts of gelatin, 2-6 parts of dodecyl ethoxy sulpho betaine, 2-5 parts of sodium carbonate, 1-4 parts of sodium citrate, 2-4 parts of triethanolamine, 1-9 parts of aluminum potassium sulfate, 1-6 parts of calcium sulfate, 1-3 parts of polyacrylamide, 1-4 parts of calcium lignosulphonate, 2-7 parts of hydroxyethyl methyl cellulose, 3-7 parts of calcium hydroxide, 1-3 parts of boric acid and 60-85 parts of water. The inorganic-organic composite permeable crystallization type waterproof agent has good waterproofness, endurance performance and self-curing performance and is low in cost and capable of being applied to waterproofing of house faces, basements, restrooms and the like.

Description

technical field [0001] The invention relates to an inorganic-organic composite osmotic crystalline waterproofing agent, which belongs to the technical field of concrete building waterproofing materials. Background technique [0002] Concrete is a multi-phase composite brittle material, its tensile strength is relatively low (about 1 / 20-1 / 10 of the compressive strength), and the ultimate tensile strain is relatively small (only 0.02%-0.03%). When it is in the process of hydration and hardening, due to drying shrinkage, chemical shrinkage, carbonation shrinkage and other reasons, the internal tensile stress caused by volume shrinkage and deformation is greater than its own tensile strength, cracking will occur in concrete, which can not only destroy its The impermeability of the structure will also affect its durability, the stability of steel bars and the safety of the building. In addition, concrete is also a heterogeneous material. From the perspective of macrostructure, c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B24/38C04B103/65
Inventor 黄志强王继发刘泓铭
Owner GUILIN HEXIN WATERPROOF DECORATION MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com