Heat-preserving fireproof decorating wall material made of FBZ nanometer ceramics

A technology of wall materials and nano-ceramics, which is applied in the field of building materials, can solve problems affecting the appearance and safety of buildings, peeling and delamination of exterior decoration layers, and achieve improved spraying yield, consistent effect, and high migration efficiency Effect

Inactive Publication Date: 2015-11-25
徐杰
View PDF13 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Peeling, peeling, and delamination of the exterior laye

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A FBZ nano-ceramic thermal insulation and fireproof decorative wall material is prepared from the following components in parts by weight:

[0020] 1 part of floating beads, 5 parts of artificial vermiculite, 5 parts of brucite fiber, 10 parts of nano ceramic powder, 5 parts of brucite fiber, 5 parts of phenolic resin powder, 0.2 part of organic silicon water repellent powder, 1 part of inorganic adhesive cement 1 part, loadable dispersible latex powder 1 part, hydroxypropyl cellulose 2 parts, sodium alginate 2 parts, chemical resistance modifier 0.5 parts, flame retardant synergist 2 parts, brominated flame retardant 5 parts.

Embodiment 2

[0022] A FBZ nano-ceramic thermal insulation and fireproof decorative wall material is prepared from the following components in parts by weight:

[0023] 5 parts of floating beads, 10 parts of artificial vermiculite, 10 parts of brucite fiber, 30 parts of nano-ceramic powder, 5 parts of colored sand, 10 parts of brucite fiber, 10 parts of phenolic resin powder, 0.4 part of organic silicon water repellent powder , 5 parts of inorganic adhesive cement, 5 parts of loadable dispersible latex powder, 5 parts of hydroxypropyl cellulose, 5 parts of sodium alginate, 5 parts of chemical resistance modifier, 6 parts of flame retardant synergist, brominated retardant Fuel agent 10 parts.

Embodiment 3

[0025] A FBZ nano-ceramic thermal insulation and fireproof decorative wall material is prepared from the following components in parts by weight:

[0026] 3 parts of floating beads, 7.5 parts of artificial vermiculite, 7.5 parts of brucite fiber, 20 parts of nano-ceramic powder, 2.5 parts of colored sand, 7.5 parts of brucite fiber, 7.5 parts of phenolic resin powder, 0.3 parts of silicone water repellent powder , 3 parts of inorganic adhesive cement, 3 parts of loadable dispersible latex powder, 3.5 parts of hydroxypropyl cellulose, 3.5 parts of sodium alginate, 2.75 parts of chemical resistance modifier, 4 parts of flame retardant synergist, brominated retardant Fuel agent 7.5 parts.

[0027] When this specific implementation is in use, directly add tap water in a volume ratio of 1:4 for stirring, then directly spray on the insulation layer with a thickness of 8-12 mm. After the skin is dry, apply the skin luster curing agent to get final product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a heat-preserving fireproof decorating wall material made of FBZ nanometer ceramics. The material is prepared from, by weight, 1-5 parts of floating beads, 5-10 parts of artificial vermiculite, 5-10 parts of brucite fibers, 10-30 parts of nanometer ceramic powder, 0-5 parts of color sand, 5-10 parts of brucite fibers, 5-10 parts of phenolic resin powder, 0.2-0.4 part of organic silicon water repellent powder, 1-5 parts of inorganic adhesive cement, 1-5 parts of loadable dispersity emulsion powder, 2-5 parts of hydroxy propyl cellulose, 2-5 parts of sodium alginate, 0.5-5 parts of chemical resistant modifiers, 2-6 parts of flame-retardant synergist and 5-10 parts of brominated flame retardant. The material prevents leakage, preserves heat, insulates the heat, saves energy, has weather resistance, fireproof performance and durability, and meets the requirement of a building for overall attractiveness.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a FBZ nano-ceramic thermal insulation and fireproof decorative wall material. Background technique [0002] The promotion and application of building energy-saving wall insulation technology and products in my country started in the late 1980s. At that time, there were mainly inorganic insulation materials such as perlite and composite silicate. In 1996, in order to speed up the development of building energy conservation, the state promulgated the energy conservation standard of 50% energy conservation. Due to the high thermal conductivity of inorganic thermal insulation materials, construction operations cannot be guaranteed. Moreover, it has poor thermal insulation performance, good fire and flame retardant performance, hollowing, cracking and falling off. Therefore, the energy saving requirement of 50% energy saving cannot be met. In this way, organic polystyrene insulati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B111/28
Inventor 徐杰徐欢
Owner 徐杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products