Flux-cored welding wire for argon-enriched gas shielded welding and its preparation method and application

A flux-cored wire, argon-rich technology, applied in welding equipment, welding media, welding/cutting media/materials, etc., can solve the problems of poor long-distance wire feeding stability, reduced welding productivity, and increased filler metal content. Effects of incomplete fusion welding defects, improved welding productivity, and reduced filler metal content

Active Publication Date: 2017-10-13
HARBIN WELL WELDING CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Flux-cored wire has the advantages of stable arc, small spatter, and easy adjustment of chemical composition, but it has disadvantages such as complicated manufacturing process and high cost, especially the wire feeding performance is not as good as that of solid core wire, and the stability of long-distance wire feeding is poor.
The wire feeding performance of solid wire is good, but its composition is difficult to adjust, the welding spatter is large, the arc stability is poor, and the penetration depth is shallow, especially the penetration depth of MIG welding is shallower. This increases the amount of filler metal and reduces welding productivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] (1) Select a commercially available SPCC steel strip with a wall thickness of 0.9mm and a width of 16mm. After cleaning with ultrasonic cleaning equipment, use the existing flux-cored welding wire production line to roll it into a cross-section along the length direction (longitudinal direction) of the steel strip. It is U-shaped.

[0039] The chemical composition (mass %) of the SPCC steel strip is 0.06%C, 0.02%Si, 0.43%Mn, 0.012%S, 0.023%P.

[0040] (2) add medicinal powder in above-mentioned U-shaped pit, filling rate is 15% (filling rate is the ratio of medicinal powder quality and medicinal powder, steel strip quality sum), wherein: described medicinal powder is that particle size is-297 micron+74 micron ( That is -50 mesh +200 mesh) powder material.

[0041] The chemical composition of the above powder contains 0.05%C, 0.38%Si, 1.35%Mn, 0.02%S, 0.025%P, 1.0%K by mass percentage 2 CO 3 Powder, 1.3% potassium permanganate powder, the balance is Fe and unavoidable...

Embodiment 2

[0046](1) Select a commercially available SPCC steel strip with a wall thickness of 0.8mm and a width of 12mm. After cleaning with ultrasonic cleaning equipment, use the existing flux-cored wire production line to roll it into a cross-section along the length direction (longitudinal direction) of the steel strip. It is U-shaped.

[0047] The chemical composition (mass%) of the SPCC steel strip is 0.08%C, 0.03%Si, 0.48%Mn, 0.015%S, 0.025%P.

[0048] (2) add medicinal powder in above-mentioned U-shaped pit, filling rate is 10% (filling rate is the ratio of medicinal powder quality and medicinal powder, steel strip quality sum), wherein: described medicinal powder is particle size is-297 micron+74 micron ( That is -50 mesh +200 mesh) powder material.

[0049] The chemical composition of the above powder contains 0.10%C, 0.28%Si, 1.50%Mn, 0.025%S, 0.03%P, 1.5%potassium permanganate powder by mass percentage, the balance is Fe and unavoidable for flux cored wire properties Impuri...

Embodiment 3

[0054] (1) Select a commercially available SPCC steel strip with a wall thickness of 1.0mm and a width of 14mm. After cleaning with ultrasonic cleaning equipment, use the existing flux-cored welding wire production line to roll it into a cross-section along the length direction (longitudinal direction) of the steel strip. It is U-shaped.

[0055] The chemical composition (mass%) of the SPCC steel strip is 0.10%C, 0.05%Si, 0.50%Mn, 0.025%S, 0.029%P.

[0056] (2) add medicated powder in above-mentioned U-shaped pit, filling rate is 13% (filling rate is the ratio of the sum of medicated powder quality and medicated powder, steel band quality), wherein: described medicated powder is that particle size is-297 micron+74 micron ( That is -50 mesh +200 mesh) powder material.

[0057] The chemical composition of the above powder contains 0.12%C, 0.40%Si, 1.25%Mn, 0.028%S, 0.032%P, 2.0%K by mass percentage 2 CO 3 Powder, 0.5% potassium permanganate powder, the balance is Fe and unavo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flux-cored wire for full-argon gas shielded arc welding as well as a preparation method and an application of the flux-cored wire. The flux-cored wire comprises powder and a tube wall for covering the powder, wherein the powder comprises components in percentage by mass as follows: no more than 0.12% of C, no more than 0.4% of Si, no more than 1.5% of Mn, 0.35%-0.6% of Mo, no more than 0.035% of S, no more than 0.035% of P, 0-2.0% of K2CO3 powder, 0.5%-1.5% of potassium permanganate powder and the balance of Fe and inevitable impurities having no influence on the performance of the flux-cored wire. The flux-cored wire has the deeper penetration, so that a base material is not required to be grooved, or only a small groove is required to be formed and a large truncated edge is required to be reserved, the filler metal quantity is reduced, and the welding productivity is greatly improved. Meanwhile, the welding defect of incomplete fusion cannot be produced easily, and the safety of a welded structure is improved.

Description

technical field [0001] The invention relates to a welding material, in particular to a flux-cored welding wire for argon-rich gas shielded welding, a preparation method and application thereof. Background technique [0002] With the rapid development of industrial technology, welded structures are developing in the direction of large-scale, high-parameterization, and high-strength toughness. High-strength toughness plates are more and more used in welded structures. At present, submerged arc welding and argon-enriched gas shielded welding are the main welding processes for medium-thick plates. Welding of medium and thick plates requires beveling, multi-layer and multi-pass welding, the welding production process is complicated, and the welding production efficiency is low. The publication number is CN103831541A invention patent "Laser-MIG arc hybrid welding method for high-strength steel butt joints", which uses laser-MIG arc composite heat source to increase penetration de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/30B23K35/40
CPCB23K35/3073B23K35/406
Inventor 杨长岗杨宝胜韩洪伟孙俊生
Owner HARBIN WELL WELDING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com